X3CRNICU18-9-4

BS EN 10263-5:2017; Heat analysis, mass percent; Values without a stated range are maxima; Notes below the table are retained. Cr has been restored from the original page after omission during table extraction: 17.0–19.0%. No edition is stated on the website; Displayed under this source edition; contract applicability is not established

ISO 4954:2018; heat analysis, mass fraction %; values without a stated range are upper limits; see the source page for complete table footnotes. The website does not specify the edition; the source edition is shown here and does not establish contractual applicability.

ISO 4954:2018 Table D.2 gives cast analysis; single values are maxima and dashes are not zero.

Product-analysis deviations are listed separately under Tables 2/3, not used directly to relax cast-composition limits.

Elements not listed must not be intentionally added without the purchaser's consent, except for finishing the heat.

Heat-analysis mass fractions wt%; Product-analysis tolerances follow Table 4 separately. ; The sulfur conditions for machining, welding and polishing in Table 3, note b are retained separately; different requirements are not imposed simultaneously. ; Ti-stabilized grades require 5×C≤Ti≤0.70%, checked jointly with measured C/Ti. ; This standard covers stainless steel for cold heading and cold extrusion; delivery condition, dimensions, surface and mechanical properties still require independent confirmation. ; Unlisted elements must not be intentionally added without purchaser consent, except additions needed to finish steelmaking; unspecified contents are not treated as zero. ; Tabulated Ni 8.5–10.5%; note e permits a Ni minimum of 8.0% unless otherwise agreed at enquiry or ordering; Displayed separately by condition.

Actual source: DIN EN 10263-5:2002-02; German adoption of EN 10263-5:2001, PDF p. 8 Table 2 and Notes a–e.

Default is ladle analysis, mass fraction wt%; product-analysis deviations are separately governed by Table 3 and are not added to default ladle ranges.

Unlisted elements must not be intentionally added without purchaser approval (except as necessary during steelmaking); residual elements must not impair performance or use.

This older edition does not use the 2017 edition’s conditional sulfur provisions; do not copy newer machining/welding/polishing options.

For Ti-stabilized grades, verify 5×C≤Ti≤0.70% using measured C; do not apply this condition to grades without Ti.

The standard covers cold heading/cold extrusion; actual supply, dimensions, delivery condition and properties still require confirmation.

EN 10088-1:2005 Table 4 and continuation: ladle analysis (wt%); the official SIST adoption preview PDF, pages 11/12, covers all 50 grades and notes. Note a: unlisted elements are not intentionally added without purchaser consent, except as needed to complete steelmaking; a blank is not zero. Note b: for grades marked b only, S is selected separately for long products and by property requirement. Note d: the increased Ni maximum for special reasons applies only to listed grades, not all grades. Note c: Cu up to 1.0% for cold heading/extrusion; this condition path is provided here only for grades with blank Cu in the original table. Existing Cu alloy ranges retain their original values; the exception has not automatically rewritten them. The linked Ti≥5C/Nb≥10C and Ti≥8(C+N) conditions are retained; an unlisted N maximum is not zero. Note e: the source warns of skin-contact regulatory issues for high-sulfur free-machining steel; this is retained as a historical warning only and is not a claim of current compliance based on the 2005 text. Listed chemistry and the cold-heading Cu exception alone do not establish overall cold-heading performance or company supply; mechanical and product standards must be checked separately, and national adoption does not mean automatic equivalence.

Table 1 and Note a/b in the official BS English adoption of EN10269:2013; heat analysis, wt%. ; The Al column is total aluminum; Elements not listed shall not be filled as zero and shall not be intentionally added without the consent of the purchaser (except those required to complete the smelting process). ; Note b: Sulfur levels by agreement are available only for marked grades; ordinary, machining and welding conditions are retained separately.. ; Titanium-stabilized grade X6CrNiTiB18-10 shall simultaneously satisfy Ti≥5C and Ti≤.80; a single-item upper limit shall not replace a linked lower limit. ; Product-analysis deviations, mechanical properties, delivery heat treatment and suitability for cold heading require separate verification; this record is not automatically included in the supply offering..

The cover of NF EN 10269:1999 explicitly adopts EN 10269:1999; Preserve the correspondence between the French adoption version and the European version; do not label as other countries or new editions. ; Table 1 gives heat-analysis mass percentages; Single values in P and S columns are upper limits; other single values are parsed according to the inequality signs in the original table; Unspecified elements shall not be filled as zero. ; Applies to billets, bars and wire rod of steels and nickel alloys for fasteners with specified high- or low-temperature properties.; Cold heading and actual supply must be verified in conjunction with delivery condition, dimensions, and process. ; Table 1 Footnote 1: Elements not listed in the table shall not be intentionally added without the buyer's consent (except additions needed to finish steelmaking); Elements that affect properties must be prevented from being introduced via scrap steel, etc.. ; This record only verifies the heat analysis composition in Table 1; product analysis tolerances in Table 2 shall not be automatically added to the heat limits. ; Footnote 2 of Table 1 only suggests controlling S within 0.015–0.030% to improve machinability; The suggested value shall not be treated as a mandatory S lower limit; the default remains S≤0.030%.

DIN EN 10263-5:2018-02 is the German-language edition of EN 10263-5:2017; This record was verified against heat analysis and footnotes in Table 3 of the official German edition. ; Heat-analysis mass fractions wt%; Product-analysis tolerances follow Table 4 separately. ; The sulfur conditions for machining, welding and polishing in Table 3, note b are retained separately; different requirements are not imposed simultaneously. ; Ti-stabilized grades require 5×C≤Ti≤0.70%, checked jointly with measured C/Ti. ; This standard covers stainless steel for cold heading and cold extrusion; delivery condition, dimensions, surface and mechanical properties still require independent confirmation. ; Unlisted elements must not be intentionally added without purchaser consent, except additions needed to finish steelmaking; unspecified contents are not treated as zero. ; Tabulated Ni 8.5–10.5%; note e permits a Ni minimum of 8.0% unless otherwise agreed at enquiry or ordering; Displayed separately by condition.