XGSWRCH35KB
1 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for XGSWRCH35KB →Material demand assessment
Looking for XGSWRCH35KB material?
Not listed in our catalog? You are welcome to submit your requirements. We assess whether our equipment, production lines and process capabilities suit your grade, product form, dimensions, processing and delivery requirements, then discuss possible processing, trials or supply arrangements.
Feasibility and supply terms are confirmed after technical review. The standard information on this page is not a supply or performance commitment.
Keep your entries and try again later, or contact website@chqwire.net. If you have already received confirmation, do not submit again.
XGSWRCH35KB · Q/XG 231-2023
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Cold-heading steel
- Material form
- Wire rod
- Original record status
- Original standard verified
- Standard edition
- Q/XG 231-2023
- Table / clause
- Table 1, row 55
- PDF page references
- 5
- Unit
- Mass fraction (wt%)
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | 0.32 ～ 0.38 |
| Si | 0.1 ～ 0.35 |
| Mn | 0.6 ～ 0.9 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| B | 0.0008 ～ 0.003 |
| Cr | ≤ 0.2 (lower limit not stated) |
| Ni | ≤ 0.2 (lower limit not stated) |
| Cu | ≤ 0.2 (lower limit not stated) |
Applicability and limitations
Mass fraction wt%; Q/XG 231-2023, Table 1, heat analysis; Local PDF, page 5. Check product-analysis tolerances under GB/T 222; Heat-analysis ranges are not directly treated as guaranteed product-analysis ranges. Clause 5.1.4: residual Cr, Ni and Cu, where no separate range is specified, are each ≤0.20%. Clause 5.1.3: other grades or compositions may be supplied by agreement between the parties and are not automatically included in Table 1. This table is an enterprise standard for Xingtai Steel wire rod; it does not establish Creation Group stock availability or a project-approved substitute. Table 1, note 1: the XGSWRCH series references the grade-designation system of JIS G3507; Composition values follow Table 1 of this Xingtai Steel standard. Table 1: B is 0.0008%–0.0030%, not unspecified. Clause 5.4: under high or relatively high cold-upsetting test requirements, grades with C≥0.30% must first be spheroidize-annealed.