XG10B37
1 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for XG10B37 →Material demand assessment
Looking for XG10B37 material?
Not listed in our catalog? You are welcome to submit your requirements. We assess whether our equipment, production lines and process capabilities suit your grade, product form, dimensions, processing and delivery requirements, then discuss possible processing, trials or supply arrangements.
Feasibility and supply terms are confirmed after technical review. The standard information on this page is not a supply or performance commitment.
Keep your entries and try again later, or contact website@chqwire.net. If you have already received confirmation, do not submit again.
XG10B37 · Q/XG 232-2021
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Boron steels
- Material form
- Wire rod
- Original record status
- Original standard verified
- Standard edition
- Q/XG 232-2021
- Table / clause
- Table 1, row 13
- PDF page references
- 3
- Unit
- Mass fraction (wt%)
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | 0.32 ～ 0.38 |
| Si | ≤ 0.4 (lower limit not stated) |
| Mn | 0.7 ～ 1.0 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| B | 0.0008 ～ 0.003 |
| Ni | ≤ 0.2 (lower limit not stated) |
| Cu | ≤ 0.2 (lower limit not stated) |
| Cr | ≤ 0.3 (lower limit not stated) |
Applicability and limitations
Mass fraction wt%; Q/XG 232-2021, Table 1, heat analysis; Local PDF, page 3. Table 1 merged cell: P≤0.030%, S≤0.030% and B 0.0008%–0.0030% apply to all 17 rows. Clause 4.1.2: residual Ni and Cu are each ≤0.20%, Cr≤0.30%. Check product-analysis tolerances under GB/T 222; Heat-analysis ranges are not directly treated as guaranteed product-analysis ranges. Clause 4.1.3: other compositions may be supplied by agreement between both parties and are not automatically included in Table 1. Xingtai Steel wire-rod enterprise-standard record; this does not establish Creation Group stock availability or a project-approved substitute. Clause 4.4.3: under high or relatively high cold-upsetting test requirements, specimens of C≥0.30% grades must first be spheroidize-annealed.
Combined limits
- Combined-element limits
- Elements requiring measured values from the same heat