X6CRNI 25-20
4 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for X6CRNI 25-20 →Material demand assessment
Looking for X6CRNI 25-20 material?
Not listed in our catalog? You are welcome to submit your requirements. We assess whether our equipment, production lines and process capabilities suit your grade, product form, dimensions, processing and delivery requirements, then discuss possible processing, trials or supply arrangements.
Feasibility and supply terms are confirmed after technical review. The standard information on this page is not a supply or performance commitment.
Keep your entries and try again later, or contact website@chqwire.net. If you have already received confirmation, do not submit again.
X6CrNi 25-20 · DIN EN 10269-2014
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Original record status
- Composition basis in the adopted standard verified
- Standard edition
- EN 10269-2013
- Table / clause
- Table 1 and notes a–c
Carbon-equivalent reference
Estimates are presented separately for each applicable composition condition. Match the actual ordering conditions; ranges must not be combined.
Default sulfur content in Table 1
S 0.015–0.030% agreed at enquiry or ordering to improve machinability
Weldability condition S 0.008–0.030% agreed at enquiry or ordering
Composition record (conditional branches apply; this is not an unconditional requirement)
| Element | Composition requirement |
|---|---|
| C | 0.04 ～ 0.08 |
| Si | ≤ 0.7 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Cr | 24.0 ～ 26.0 |
| Ni | 19.0 ～ 22.0 |
| N | ≤ 0.1 (lower limit not stated) |
Applicability and limitations
DIN EN 10269:2014-02 adopts EN 10269:2013; Composition in this record follows EN 10269:2013, Table 1 and footnotes; the actual text read is the official BS adoption. Heat-analysis mass fractions wt%; Product-analysis tolerances require separate verification under Table 2. ; The agreed sulfur condition in Table 1, note b applies only to grades marked b; default, machining and welding ranges are retained separately. ; This standard covers steels and nickel alloys for high- and low-temperature fasteners; cold-heading suitability is not established for every grade or delivery condition. ; Unlisted elements must not be intentionally added without purchaser consent, except additions needed to finish steelmaking; Unspecified values are not treated as zero.
Original condition-branch records
Default sulfur content in Table 1
| Element | Composition requirement |
|---|---|
| C | 0.04 ～ 0.08 |
| Si | ≤ 0.7 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Cr | 24.0 ～ 26.0 |
| Ni | 19.0 ～ 22.0 |
| N | ≤ 0.1 (lower limit not stated) |
S 0.015–0.030% agreed at enquiry or ordering to improve machinability
| Element | Composition requirement |
|---|---|
| C | 0.04 ～ 0.08 |
| Si | ≤ 0.7 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | 0.015 ～ 0.03 |
| Cr | 24.0 ～ 26.0 |
| Ni | 19.0 ～ 22.0 |
| N | ≤ 0.1 (lower limit not stated) |
Weldability condition S 0.008–0.030% agreed at enquiry or ordering
| Element | Composition requirement |
|---|---|
| C | 0.04 ～ 0.08 |
| Si | ≤ 0.7 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | 0.008 ～ 0.03 |
| Cr | 24.0 ～ 26.0 |
| Ni | 19.0 ～ 22.0 |
| N | ≤ 0.1 (lower limit not stated) |
A condition branch must be selected
YesVerification notes
The adoption relationship and original composition in the corresponding EN, Table 1 have been checked; The complete main text of DIN has not been checked page by pageX6CrNi 25-20 · EN 10269-2013
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- EN 10269-2013
- Table / clause
- Table 1 and notes a–c
Carbon-equivalent reference
Estimates are presented separately for each applicable composition condition. Match the actual ordering conditions; ranges must not be combined.
Default sulfur content in Table 1
S 0.015–0.030% agreed at enquiry or ordering to improve machinability
Weldability condition S 0.008–0.030% agreed at enquiry or ordering
Composition record (conditional branches apply; this is not an unconditional requirement)
| Element | Composition requirement |
|---|---|
| C | 0.04 ～ 0.08 |
| Si | ≤ 0.7 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Cr | 24.0 ～ 26.0 |
| Ni | 19.0 ～ 22.0 |
| N | ≤ 0.1 (lower limit not stated) |
Applicability and limitations
Heat-analysis mass fractions wt%; Product-analysis tolerances require separate verification under Table 2. ; The agreed sulfur condition in Table 1, note b applies only to grades marked b; default, machining and welding ranges are retained separately. ; This standard covers steels and nickel alloys for high- and low-temperature fasteners; cold-heading suitability is not established for every grade or delivery condition. ; Unlisted elements must not be intentionally added without purchaser consent, except additions needed to finish steelmaking; Unspecified values are not treated as zero.
Original condition-branch records
Default sulfur content in Table 1
| Element | Composition requirement |
|---|---|
| C | 0.04 ～ 0.08 |
| Si | ≤ 0.7 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Cr | 24.0 ～ 26.0 |
| Ni | 19.0 ～ 22.0 |
| N | ≤ 0.1 (lower limit not stated) |
S 0.015–0.030% agreed at enquiry or ordering to improve machinability
| Element | Composition requirement |
|---|---|
| C | 0.04 ～ 0.08 |
| Si | ≤ 0.7 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | 0.015 ～ 0.03 |
| Cr | 24.0 ～ 26.0 |
| Ni | 19.0 ～ 22.0 |
| N | ≤ 0.1 (lower limit not stated) |
Weldability condition S 0.008–0.030% agreed at enquiry or ordering
| Element | Composition requirement |
|---|---|
| C | 0.04 ～ 0.08 |
| Si | ≤ 0.7 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | 0.008 ～ 0.03 |
| Cr | 24.0 ～ 26.0 |
| Ni | 19.0 ～ 22.0 |
| N | ≤ 0.1 (lower limit not stated) |
A condition branch must be selected
YesVerification notes
The original English Table 1 and footnotes were checkedX6CrNi 25-20 · EN 10302-2008
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | 0.04 ～ 0.08 |
| Cr | 24 ～ 26 |
| Mn | ≤ 2 (lower limit not stated) |
| N | ≤ 0.1 (lower limit not stated) |
| Ni | 19 ～ 22 |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 0.7 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
X6CrNi 25-20 · EU 95-1979
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Mn | ≤ 2 (lower limit not stated) |
| Ni | 19 ～ 22 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.5 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.