X6CRNI 18-10
3 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for X6CRNI 18-10 →Material demand assessment
Looking for X6CRNI 18-10 material?
Not listed in our catalog? You are welcome to submit your requirements. We assess whether our equipment, production lines and process capabilities suit your grade, product form, dimensions, processing and delivery requirements, then discuss possible processing, trials or supply arrangements.
Feasibility and supply terms are confirmed after technical review. The standard information on this page is not a supply or performance commitment.
Keep your entries and try again later, or contact website@chqwire.net. If you have already received confirmation, do not submit again.
X6CrNi 18-10 · DIN EN 10269-2014
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Original record status
- Composition basis in the adopted standard verified
- Standard edition
- EN 10269-2013
- Table / clause
- Table1 high-temperature steels and note a/b
- PDF page references
- 18、19
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | 0.04 ～ 0.08 |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Cr | 17.0 ～ 19.0 |
| Ni | 8.0 ～ 11.0 |
| N | ≤ 0.1 (lower limit not stated) |
Applicability and limitations
DIN EN 10269:2014-02 is the German-language edition of EN 10269:2013; Current composition is taken from the original EN table and must be verified according to application and delivery condition. Table 1 and Note a/b in the official BS English adoption of EN10269:2013; heat analysis, wt%. ; The Al column is total aluminum; Elements not listed shall not be filled as zero and shall not be intentionally added without the consent of the purchaser (except those required to complete the smelting process). ; Note b: Sulfur levels by agreement are available only for marked grades; ordinary, machining and welding conditions are retained separately.. ; Titanium-stabilized grade X6CrNiTiB18-10 shall simultaneously satisfy Ti≥5C and Ti≤.80; a single-item upper limit shall not replace a linked lower limit. ; Product-analysis deviations, mechanical properties, delivery heat treatment and suitability for cold heading require separate verification; this record is not automatically included in the supply offering..
Verification notes
The official adoption relationship for DIN and original same-designation EN 10269:2013, Table 1 have been checked; The complete German text has not been checked page by pageX6CrNi 18-10 · EN 10269-2013
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- EN 10269-2013
- Table / clause
- Table1 high-temperature steels and note a/b
- PDF page references
- 18、19
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | 0.04 ～ 0.08 |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Cr | 17.0 ～ 19.0 |
| Ni | 8.0 ～ 11.0 |
| N | ≤ 0.1 (lower limit not stated) |
Applicability and limitations
Table 1 and Note a/b in the official BS English adoption of EN10269:2013; heat analysis, wt%. ; The Al column is total aluminum; Elements not listed shall not be filled as zero and shall not be intentionally added without the consent of the purchaser (except those required to complete the smelting process). ; Note b: Sulfur levels by agreement are available only for marked grades; ordinary, machining and welding conditions are retained separately.. ; Titanium-stabilized grade X6CrNiTiB18-10 shall simultaneously satisfy Ti≥5C and Ti≤.80; a single-item upper limit shall not replace a linked lower limit. ; Product-analysis deviations, mechanical properties, delivery heat treatment and suitability for cold heading require separate verification; this record is not automatically included in the supply offering..
Verification notes
Official English Table 1 and applicable footnotes were visually checkedX6CrNi 18-10 · EU 95-1979
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.07 (lower limit not stated) |
| Cr | 17 ～ 19 |
| Mn | ≤ 2 (lower limit not stated) |
| Ni | 8 ～ 11 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.