X6CRAL13

NF EN 10088-1:2005 adopts EN 10088-1:2005 (EN 10088-1-2005); See the data basis for the actual composition source file and table number. EN10088-1:2005, Table 2, cast/heat-analysis mass fractions wt%; complete Table 2 in the official SIST adoption preview PDF8; The preview is not the complete standard. ; Note a: unlisted elements must not be intentionally added without purchaser consent, except additions needed to finish the heat; A blank is not zero; no residual maximum is inserted without a source. ; Note b applies only to grades marked b; S must be checked separately for the selected product and property conditions and is not extended to the entire table. ; The coupled minimum for Ti/Nb/Zr and C/N is retained separately; no N maximum is provided in the table, and this is not entered as zero; The corresponding coupled condition cannot be confirmed without measured N. ; This part is a stainless steel designation list; specific delivery and mechanical-property requirements must follow the corresponding product standard; Cold-heading suitability, supply or equivalence between national editions is not established.

EN10088-1:2005, Table 2, cast/heat-analysis mass fractions wt%; complete Table 2 in the official SIST adoption preview PDF8; The preview is not the complete standard. ; Note a: unlisted elements must not be intentionally added without purchaser consent, except additions needed to finish the heat; A blank is not zero; no residual maximum is inserted without a source. ; Note b applies only to grades marked b; S must be checked separately for the selected product and property conditions and is not extended to the entire table. ; The coupled minimum for Ti/Nb/Zr and C/N is retained separately; no N maximum is provided in the table, and this is not entered as zero; The corresponding coupled condition cannot be confirmed without measured N. ; This part is a stainless steel designation list; specific delivery and mechanical-property requirements must follow the corresponding product standard; Cold-heading suitability, supply or equivalence between national editions is not established.

ISO 15510:2014, Table 1 gives heat analysis, mass fractions wt%; Under note a, values without a stated range or minimum are maxima; a dash is not treated as zero. Composition rows follow an excerpt of the official PDF edition; relevant footnotes follow the original Table 1 in the Sample text section of the standards publishing platform; Verification of the complete standard text or mechanical properties is not claimed. The standard covers material for wrought products, including ingots and semi-finished products; Similar composition does not establish direct substitution; cold-heading suitability and supply condition require separate confirmation. The S 0.015–0.030% machinability recommendations, 0.008–0.020% weldability recommendation and S≤0.015% polishability recommendation in note b concern specific properties and do not directly replace this row’s sulfur limits.

EN10088-1:2005, Table 2, cast/heat-analysis mass fractions wt%; complete Table 2 in the official SIST adoption preview PDF8; The preview is not the complete standard. ; Note a: unlisted elements must not be intentionally added without purchaser consent, except additions needed to finish the heat; A blank is not zero; no residual maximum is inserted without a source. ; Note b applies only to grades marked b; S must be checked separately for the selected product and property conditions and is not extended to the entire table. ; The coupled minimum for Ti/Nb/Zr and C/N is retained separately; no N maximum is provided in the table, and this is not entered as zero; The corresponding coupled condition cannot be confirmed without measured N. ; This part is a stainless steel designation list; specific delivery and mechanical-property requirements must follow the corresponding product standard; Cold-heading suitability, supply or equivalence between national editions is not established.

A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.

A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.