X6CR13
11 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for X6CR13 →Material demand assessment
Looking for X6CR13 material?
Not listed in our catalog? You are welcome to submit your requirements. We assess whether our equipment, production lines and process capabilities suit your grade, product form, dimensions, processing and delivery requirements, then discuss possible processing, trials or supply arrangements.
Feasibility and supply terms are confirmed after technical review. The standard information on this page is not a supply or performance commitment.
Keep your entries and try again later, or contact website@chqwire.net. If you have already received confirmation, do not submit again.
X6Cr13 · EN 10088-1-2005
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Stainless steel
- Subcategory
- Ferritic stainless steel
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- EN 10088-1-2005
- Table / clause
- Table 2 and notes a–c; all 21 ferritic stainless steel grades
- PDF page references
- 1、3、7、8
Carbon-equivalent reference
Estimates are presented separately for each applicable composition condition. Match the actual ordering conditions; ranges must not be combined.
Ordinary sulfur maximum in Table 2; the long-product condition in note b has not been selected
Note b: S≤.030 applies to bars, wire rod, wire, sections, bright products and the corresponding semi-finished products
Note b recommends and permits S .015–.030 to improve machinability
Note b recommends and permits S .008–.030 to improve weldability
Note b recommends S≤.015 for polishability
Composition record (conditional branches apply; this is not an unconditional requirement)
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Cr | 12.0 ～ 14.0 |
Applicability and limitations
EN10088-1:2005, Table 2, cast/heat-analysis mass fractions wt%; complete Table 2 in the official SIST adoption preview PDF8; The preview is not the complete standard. ; Note a: unlisted elements must not be intentionally added without purchaser consent, except additions needed to finish the heat; A blank is not zero; no residual maximum is inserted without a source. ; Note b applies only to grades marked b; S must be checked separately for the selected product and property conditions and is not extended to the entire table. ; The coupled minimum for Ti/Nb/Zr and C/N is retained separately; no N maximum is provided in the table, and this is not entered as zero; The corresponding coupled condition cannot be confirmed without measured N. ; This part is a stainless steel designation list; specific delivery and mechanical-property requirements must follow the corresponding product standard; Cold-heading suitability, supply or equivalence between national editions is not established.
Combined limits
- Elements requiring measured values from the same heat
Original condition-branch records
Ordinary sulfur maximum in Table 2; the long-product condition in note b has not been selected
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Cr | 12.0 ～ 14.0 |
Note b: S≤.030 applies to bars, wire rod, wire, sections, bright products and the corresponding semi-finished products
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Cr | 12.0 ～ 14.0 |
Note b recommends and permits S .015–.030 to improve machinability
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | 0.015 ～ 0.03 |
| Cr | 12.0 ～ 14.0 |
Note b recommends and permits S .008–.030 to improve weldability
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | 0.008 ～ 0.03 |
| Cr | 12.0 ～ 14.0 |
Note b recommends S≤.015 for polishability
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Cr | 12.0 ～ 14.0 |
A condition branch must be selected
YesVerification notes
Visual verification of all 21 rows and footnotes in original Table 2; stabilization is retained only for explicitly specified routes.X6Cr13 · NF EN 10088-1-2005
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Stainless steel
- Subcategory
- Ferritic stainless steel
- Material form
- Reference record
- Original record status
- Composition basis in the adopted standard verified
- Standard edition
- EN 10088-1-2005
- Table / clause
- Table 2 and notes a–c; all 21 ferritic stainless steel grades
- PDF page references
- 1、3、7、8
Carbon-equivalent reference
Estimates are presented separately for each applicable composition condition. Match the actual ordering conditions; ranges must not be combined.
Ordinary sulfur maximum in Table 2; the long-product condition in note b has not been selected
Note b: S≤.030 applies to bars, wire rod, wire, sections, bright products and the corresponding semi-finished products
Note b recommends and permits S .015–.030 to improve machinability
Note b recommends and permits S .008–.030 to improve weldability
Note b recommends S≤.015 for polishability
Composition record (conditional branches apply; this is not an unconditional requirement)
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Cr | 12.0 ～ 14.0 |
Applicability and limitations
NF EN 10088-1:2005 adopts EN 10088-1:2005 (EN 10088-1-2005); See the data basis for the actual composition source file and table number. EN10088-1:2005, Table 2, cast/heat-analysis mass fractions wt%; complete Table 2 in the official SIST adoption preview PDF8; The preview is not the complete standard. ; Note a: unlisted elements must not be intentionally added without purchaser consent, except additions needed to finish the heat; A blank is not zero; no residual maximum is inserted without a source. ; Note b applies only to grades marked b; S must be checked separately for the selected product and property conditions and is not extended to the entire table. ; The coupled minimum for Ti/Nb/Zr and C/N is retained separately; no N maximum is provided in the table, and this is not entered as zero; The corresponding coupled condition cannot be confirmed without measured N. ; This part is a stainless steel designation list; specific delivery and mechanical-property requirements must follow the corresponding product standard; Cold-heading suitability, supply or equivalence between national editions is not established.
Combined limits
- Elements requiring measured values from the same heat
Original condition-branch records
Ordinary sulfur maximum in Table 2; the long-product condition in note b has not been selected
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Cr | 12.0 ～ 14.0 |
Note b: S≤.030 applies to bars, wire rod, wire, sections, bright products and the corresponding semi-finished products
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Cr | 12.0 ～ 14.0 |
Note b recommends and permits S .015–.030 to improve machinability
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | 0.015 ～ 0.03 |
| Cr | 12.0 ～ 14.0 |
Note b recommends and permits S .008–.030 to improve weldability
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | 0.008 ～ 0.03 |
| Cr | 12.0 ～ 14.0 |
Note b recommends S≤.015 for polishability
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Cr | 12.0 ～ 14.0 |
A condition branch must be selected
YesVerification notes
The formal adoption relationship and corresponding EN composition original have been checked; the complete national adoption text has not been verified page by page.X6Cr13 · ISO 15510-2014
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Stainless steel
- Subcategory
- Stainless steel
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- ISO 15510-2014
- Table / clause
- The current grade row in Table1; Note a and corresponding footnotes (original text on the publishing platform)
- PDF page references
- 13
Carbon-equivalent reference
Estimates are presented separately for each applicable composition condition. Match the actual ordering conditions; ranges must not be combined.
Table 1 base range: C≤0.08%
Note i: C≤0.12% may be agreed for specific applications such as weldability or high-strength wire; Not applied without agreement
Composition record (conditional branches apply; this is not an unconditional requirement)
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Cr | 11.5 ～ 14.0 |
| Ni | ≤ 0.75 (lower limit not stated) |
Applicability and limitations
ISO 15510:2014, Table 1 gives heat analysis, mass fractions wt%; Under note a, values without a stated range or minimum are maxima; a dash is not treated as zero. Composition rows follow an excerpt of the official PDF edition; relevant footnotes follow the original Table 1 in the Sample text section of the standards publishing platform; Verification of the complete standard text or mechanical properties is not claimed. The standard covers material for wrought products, including ingots and semi-finished products; Similar composition does not establish direct substitution; cold-heading suitability and supply condition require separate confirmation. The S 0.015–0.030% machinability recommendations, 0.008–0.020% weldability recommendation and S≤0.015% polishability recommendation in note b concern specific properties and do not directly replace this row’s sulfur limits.
Original condition-branch records
Table 1 base range: C≤0.08%
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Cr | 11.5 ～ 14.0 |
| Ni | ≤ 0.75 (lower limit not stated) |
Note i: C≤0.12% may be agreed for specific applications such as weldability or high-strength wire; Not applied without agreement
| Element | Composition requirement |
|---|---|
| C | ≤ 0.12 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Cr | 11.5 ～ 14.0 |
| Ni | ≤ 0.75 (lower limit not stated) |
A condition branch must be selected
YesVerification notes
The row for this grade in Table 1 has been checked against the official PDF; Relevant original footnotes are retained in the supporting verification record; Full standard text and mechanical properties to be verified separatelyX6Cr13 · EN 10088-1-2005
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- EN 10088-1-2005
- Table / clause
- Table 2 and notes a–c; all 21 ferritic stainless steel grades
- PDF page references
- 1、3、7、8
Carbon-equivalent reference
Estimates are presented separately for each applicable composition condition. Match the actual ordering conditions; ranges must not be combined.
Ordinary sulfur maximum in Table 2; the long-product condition in note b has not been selected
Note b: S≤.030 applies to bars, wire rod, wire, sections, bright products and the corresponding semi-finished products
Note b recommends and permits S .015–.030 to improve machinability
Note b recommends and permits S .008–.030 to improve weldability
Note b recommends S≤.015 for polishability
Composition record (conditional branches apply; this is not an unconditional requirement)
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Cr | 12.0 ～ 14.0 |
Applicability and limitations
EN10088-1:2005, Table 2, cast/heat-analysis mass fractions wt%; complete Table 2 in the official SIST adoption preview PDF8; The preview is not the complete standard. ; Note a: unlisted elements must not be intentionally added without purchaser consent, except additions needed to finish the heat; A blank is not zero; no residual maximum is inserted without a source. ; Note b applies only to grades marked b; S must be checked separately for the selected product and property conditions and is not extended to the entire table. ; The coupled minimum for Ti/Nb/Zr and C/N is retained separately; no N maximum is provided in the table, and this is not entered as zero; The corresponding coupled condition cannot be confirmed without measured N. ; This part is a stainless steel designation list; specific delivery and mechanical-property requirements must follow the corresponding product standard; Cold-heading suitability, supply or equivalence between national editions is not established.
Combined limits
- Elements requiring measured values from the same heat
Original condition-branch records
Ordinary sulfur maximum in Table 2; the long-product condition in note b has not been selected
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Cr | 12.0 ～ 14.0 |
Note b: S≤.030 applies to bars, wire rod, wire, sections, bright products and the corresponding semi-finished products
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Cr | 12.0 ～ 14.0 |
Note b recommends and permits S .015–.030 to improve machinability
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | 0.015 ～ 0.03 |
| Cr | 12.0 ～ 14.0 |
Note b recommends and permits S .008–.030 to improve weldability
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | 0.008 ～ 0.03 |
| Cr | 12.0 ～ 14.0 |
Note b recommends S≤.015 for polishability
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Cr | 12.0 ～ 14.0 |
A condition branch must be selected
YesVerification notes
Visual verification of all 21 rows and footnotes in original Table 2; stabilization is retained only for explicitly specified routes.X6Cr13 · DIN EN 10088-3-2014
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Ferritic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Cr | 12 ～ 14 |
| Mn | ≤ 1 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
X6Cr13 · EN 10088-3-2014
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Ferritic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Cr | 12 ～ 14 |
| Mn | ≤ 1 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
X6Cr13 · NF EN 10088-2-2005
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Ferritic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Cr | 12 ～ 14 |
| Mn | ≤ 1 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
X6Cr13 · ISO 4955-1994
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Ferritic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Cr | 12 ～ 14 |
| Mn | ≤ 1 (lower limit not stated) |
| Ni | ≤ 1 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
X6Cr13 · ISO 4955-2005
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Ferritic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Cr | 12 ～ 14 |
| Mn | ≤ 1 (lower limit not stated) |
| Ni | ≤ 1 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
X6Cr13 · ISO 4955-2016
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Ferritic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Cr | 12 ～ 14 |
| Mn | ≤ 1 (lower limit not stated) |
| Ni | ≤ 1 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
X6Cr13 · ISO TS 15510-2003
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Ferritic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Cr | 11.5 ～ 14 |
| Mn | ≤ 1 (lower limit not stated) |
| Ni | ≤ 0.75 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.