X46CRS13
1 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for X46CRS13 →Material demand assessment
Looking for X46CRS13 material?
Not listed in our catalog? You are welcome to submit your requirements. We assess whether our equipment, production lines and process capabilities suit your grade, product form, dimensions, processing and delivery requirements, then discuss possible processing, trials or supply arrangements.
Feasibility and supply terms are confirmed after technical review. The standard information on this page is not a supply or performance commitment.
Keep your entries and try again later, or contact website@chqwire.net. If you have already received confirmation, do not submit again.
X46CrS13 · EN 10088-1-2005
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- EN 10088-1-2005
- Table / clause
- Table 3 and continuation, notes a–d; all 30 martensitic and precipitation-hardening corrosion-resistant steel grades
- PDF page references
- 1、3、9、10
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | 0.43 ～ 0.5 |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | 0.15 ～ 0.35 |
| Cr | 12.5 ～ 14.0 |
Applicability and limitations
EN10088-1:2005, Table 3 including its continuation, heat analysis wt%; official English SIST adoption preview PDF9/10. ; Note a: unlisted elements must not be intentionally added without purchaser consent, except additions needed to finish the heat; blanks are not filled with zero or a general residual maximum. ; Note b distinguishes sulfur conditions for long products, machining, welding and polishing only for grades marked b; it is not extended to all grades. ; Note c: a narrower C range may be agreed at enquiry and ordering; Without a contract, the original table range is not replaced. ; Note d: only for X7CrNiAl17-7 to improve cold-deformation performance, the Ni maximum is 8.3%; select separately from default 7.8. ; A designation-list standard does not independently establish cold-heading suitability, mechanical-property delivery requirements or product supply; Adopted editions such as NF/DIN are not automatically verified by this European main text.