X2CRNIMON17-11-2
13 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for X2CRNIMON17-11-2 →Material demand assessment
Looking for X2CRNIMON17-11-2 material?
Not listed in our catalog? You are welcome to submit your requirements. We assess whether our equipment, production lines and process capabilities suit your grade, product form, dimensions, processing and delivery requirements, then discuss possible processing, trials or supply arrangements.
Feasibility and supply terms are confirmed after technical review. The standard information on this page is not a supply or performance commitment.
Keep your entries and try again later, or contact website@chqwire.net. If you have already received confirmation, do not submit again.
X2CrNiMoN17-11-2 · EN 10088-1-2005
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- EN 10088-1-2005
- Table / clause
- Table 4 and continuation; notes a–e; all 50 austenitic corrosion-resistant steel grades
- PDF page references
- 1、3、11、12
Carbon-equivalent reference
Estimates are presented separately for each applicable composition condition. Match the actual ordering conditions; ranges must not be combined.
Default sulfur requirement; default Ni; the cold-heading Cu exception is not selected, so the original-table Cu requirement applies.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Default sulphur requirement; default Ni; note c: Cu≤1.0% for cold heading/cold extrusion.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Default sulfur requirement; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Default sulfur requirement; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b, S for long products/wire etc.: ≤0.030%Default Ni; cold-heading Cu exception not selected, so the original-table Cu requirement applies.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b, S for long products/wire etc.: ≤0.030%Default Ni; note c allows Cu≤1.0% for cold heading/cold extrusion.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b: S≤.030 applies to long products, wire and the other stated forms; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b: S≤.030 applies to long products, wire and the other stated forms; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b, recommended S for machining: 0.015–0.030%Default Ni; cold-heading Cu exception not selected, so the original-table Cu requirement applies.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b, recommended S for machining: 0.015–0.030%Default Ni; note c allows Cu≤1.0% for cold heading/cold extrusion.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b: S .015–.030 is recommended for machining; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b: S .015–.030 is recommended for machining; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b, recommended S for welding: 0.008–0.030%Default Ni; cold-heading Cu exception not selected, so the original-table Cu requirement applies.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b, recommended S for welding: 0.008–0.030%Default Ni; note c allows Cu≤1.0% for cold heading/cold extrusion.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b: S .008–.030 is recommended for welding; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b: S .008–.030 is recommended for welding; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b, recommended S for polishing: ≤0.015%Default Ni; cold-heading Cu exception not selected, so the original-table Cu requirement applies.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b, recommended S for polishing: ≤0.015%Default Ni; note c allows Cu≤1.0% for cold heading/cold extrusion.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b: S≤.015 is recommended for polishing; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b: S≤.015 is recommended for polishing; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Composition record (conditional branches apply; this is not an unconditional requirement)
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
Applicability and limitations
EN 10088-1:2005 Table 4 and continuation: ladle analysis (wt%); the official SIST adoption preview PDF, pages 11/12, covers all 50 grades and notes. Note a: unlisted elements are not intentionally added without purchaser consent, except as needed to complete steelmaking; a blank is not zero. Note b: for grades marked b only, S is selected separately for long products and by property requirement. Note d: the increased Ni maximum for special reasons applies only to listed grades, not all grades. Note c: Cu up to 1.0% for cold heading/extrusion; this condition path is provided here only for grades with blank Cu in the original table. Existing Cu alloy ranges retain their original values; the exception has not automatically rewritten them. The linked Ti≥5C/Nb≥10C and Ti≥8(C+N) conditions are retained; an unlisted N maximum is not zero. Note e: the source warns of skin-contact regulatory issues for high-sulfur free-machining steel; this is retained as a historical warning only and is not a claim of current compliance based on the 2005 text. Listed chemistry and the cold-heading Cu exception alone do not establish overall cold-heading performance or company supply; mechanical and product standards must be checked separately, and national adoption does not mean automatic equivalence.
Original condition-branch records
Default sulfur requirement; default Ni; the cold-heading Cu exception is not selected, so the original-table Cu requirement applies.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
Default sulphur requirement; default Ni; note c: Cu≤1.0% for cold heading/cold extrusion.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
Default sulfur requirement; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
Default sulfur requirement; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
Note b, S for long products/wire etc.: ≤0.030%Default Ni; cold-heading Cu exception not selected, so the original-table Cu requirement applies.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
Note b, S for long products/wire etc.: ≤0.030%Default Ni; note c allows Cu≤1.0% for cold heading/cold extrusion.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
Note b: S≤.030 applies to long products, wire and the other stated forms; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
Note b: S≤.030 applies to long products, wire and the other stated forms; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
Note b, recommended S for machining: 0.015–0.030%Default Ni; cold-heading Cu exception not selected, so the original-table Cu requirement applies.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | 0.015 ～ 0.03 |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
Note b, recommended S for machining: 0.015–0.030%Default Ni; note c allows Cu≤1.0% for cold heading/cold extrusion.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | 0.015 ～ 0.03 |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
Note b: S .015–.030 is recommended for machining; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | 0.015 ～ 0.03 |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
Note b: S .015–.030 is recommended for machining; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | 0.015 ～ 0.03 |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
Note b, recommended S for welding: 0.008–0.030%Default Ni; cold-heading Cu exception not selected, so the original-table Cu requirement applies.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | 0.008 ～ 0.03 |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
Note b, recommended S for welding: 0.008–0.030%Default Ni; note c allows Cu≤1.0% for cold heading/cold extrusion.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | 0.008 ～ 0.03 |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
Note b: S .008–.030 is recommended for welding; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | 0.008 ～ 0.03 |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
Note b: S .008–.030 is recommended for welding; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | 0.008 ～ 0.03 |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
Note b, recommended S for polishing: ≤0.015%Default Ni; cold-heading Cu exception not selected, so the original-table Cu requirement applies.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
Note b, recommended S for polishing: ≤0.015%Default Ni; note c allows Cu≤1.0% for cold heading/cold extrusion.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
Note b: S≤.015 is recommended for polishing; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
Note b: S≤.015 is recommended for polishing; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
A condition branch must be selected
YesVerification notes
Official source Table 4, all 50 rows and footnotes visually checked; conditional route for Cu cells left blank in the original.X2CrNiMoN17-11-2 · NF EN 10088-1-2005
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Original record status
- Composition basis in the adopted standard verified
- Standard edition
- EN 10088-1-2005
- Table / clause
- Table 4 and continuation; notes a–e; all 50 austenitic corrosion-resistant steel grades
- PDF page references
- 1、3、11、12
Carbon-equivalent reference
Estimates are presented separately for each applicable composition condition. Match the actual ordering conditions; ranges must not be combined.
Default sulfur requirement; default Ni; the cold-heading Cu exception is not selected, so the original-table Cu requirement applies.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Default sulphur requirement; default Ni; note c: Cu≤1.0% for cold heading/cold extrusion.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Default sulfur requirement; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Default sulfur requirement; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b, S for long products/wire etc.: ≤0.030%Default Ni; cold-heading Cu exception not selected, so the original-table Cu requirement applies.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b, S for long products/wire etc.: ≤0.030%Default Ni; note c allows Cu≤1.0% for cold heading/cold extrusion.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b: S≤.030 applies to long products, wire and the other stated forms; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b: S≤.030 applies to long products, wire and the other stated forms; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b, recommended S for machining: 0.015–0.030%Default Ni; cold-heading Cu exception not selected, so the original-table Cu requirement applies.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b, recommended S for machining: 0.015–0.030%Default Ni; note c allows Cu≤1.0% for cold heading/cold extrusion.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b: S .015–.030 is recommended for machining; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b: S .015–.030 is recommended for machining; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b, recommended S for welding: 0.008–0.030%Default Ni; cold-heading Cu exception not selected, so the original-table Cu requirement applies.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b, recommended S for welding: 0.008–0.030%Default Ni; note c allows Cu≤1.0% for cold heading/cold extrusion.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b: S .008–.030 is recommended for welding; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b: S .008–.030 is recommended for welding; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b, recommended S for polishing: ≤0.015%Default Ni; cold-heading Cu exception not selected, so the original-table Cu requirement applies.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b, recommended S for polishing: ≤0.015%Default Ni; note c allows Cu≤1.0% for cold heading/cold extrusion.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b: S≤.015 is recommended for polishing; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b: S≤.015 is recommended for polishing; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Composition record (conditional branches apply; this is not an unconditional requirement)
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
Applicability and limitations
NF EN 10088-1:2005 adopts EN 10088-1:2005 (EN 10088-1-2005); See the data basis for the actual composition source file and table number. EN10088-1:2005 Table 4 and its continuation; heat analysis wt%; all 50 grades and footnotes on PDF pages 11/12 of the official SIST adoption preview.. ; Note a: Elements not listed shall not be intentionally added without the consent of the purchaser (except additions needed to finish steelmaking).; Blanks are not entered as zero. ; Note b: For grades marked b, S shall be selected separately according to long products and properties.; The increased Ni upper limit based on special reasons in Note d applies only to the listed steel grades and cannot be generalized to all grades.. ; Note c: For cold-heading/cold-extrusion applications, Cu max 1.0%.; This conditional path is provided only for grades where Cu was blank in the original table; existing Cu alloying ranges shall retain their original values, and their Cu exceptions have not been automatically rewritten.. ; The linkages Ti≥5C/Nb≥10C and Ti≥8(C+N) are retained.; If no N upper limit is listed, do not fill as zero.. ; Note e retains the original historical caution about skin-contact regulations for high-sulfur free-cutting steel; the 2005 text is not used to claim present-day compliance.. ; The listed compositions and the cold-heading Cu exception do not independently prove the overall cold-heading properties of the material or company supply.; Mechanical properties and product standards require separate verification; national adoption does not automatically establish equivalence..
Original condition-branch records
Default sulfur requirement; default Ni; the cold-heading Cu exception is not selected, so the original-table Cu requirement applies.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
Default sulphur requirement; default Ni; note c: Cu≤1.0% for cold heading/cold extrusion.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
Default sulfur requirement; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
Default sulfur requirement; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
Note b, S for long products/wire etc.: ≤0.030%Default Ni; cold-heading Cu exception not selected, so the original-table Cu requirement applies.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
Note b, S for long products/wire etc.: ≤0.030%Default Ni; note c allows Cu≤1.0% for cold heading/cold extrusion.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
Note b: S≤.030 applies to long products, wire and the other stated forms; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
Note b: S≤.030 applies to long products, wire and the other stated forms; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
Note b, recommended S for machining: 0.015–0.030%Default Ni; cold-heading Cu exception not selected, so the original-table Cu requirement applies.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | 0.015 ～ 0.03 |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
Note b, recommended S for machining: 0.015–0.030%Default Ni; note c allows Cu≤1.0% for cold heading/cold extrusion.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | 0.015 ～ 0.03 |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
Note b: S .015–.030 is recommended for machining; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | 0.015 ～ 0.03 |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
Note b: S .015–.030 is recommended for machining; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | 0.015 ～ 0.03 |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
Note b, recommended S for welding: 0.008–0.030%Default Ni; cold-heading Cu exception not selected, so the original-table Cu requirement applies.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | 0.008 ～ 0.03 |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
Note b, recommended S for welding: 0.008–0.030%Default Ni; note c allows Cu≤1.0% for cold heading/cold extrusion.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | 0.008 ～ 0.03 |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
Note b: S .008–.030 is recommended for welding; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | 0.008 ～ 0.03 |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
Note b: S .008–.030 is recommended for welding; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | 0.008 ～ 0.03 |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
Note b, recommended S for polishing: ≤0.015%Default Ni; cold-heading Cu exception not selected, so the original-table Cu requirement applies.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
Note b, recommended S for polishing: ≤0.015%Default Ni; note c allows Cu≤1.0% for cold heading/cold extrusion.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
Note b: S≤.015 is recommended for polishing; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
Note b: S≤.015 is recommended for polishing; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
A condition branch must be selected
YesVerification notes
The formal adoption relationship and corresponding EN composition original have been checked; the complete national adoption text has not been verified page by page.X2CrNiMoN17-11-2 · ISO 15510-2014
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Stainless steel
- Subcategory
- Stainless steel
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- ISO 15510-2014
- Table / clause
- The current grade row in Table1; Note a and corresponding footnotes (original text on the publishing platform)
- PDF page references
- 9
Carbon-equivalent reference
Estimates are presented separately for each applicable composition condition. Match the actual ordering conditions; ranges must not be combined.
Base range in Table 1
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note c: only where ferrite content must be reduced for a special reason, the Ni maximum may be increased by 1.00 percentage points; This condition must be confirmed
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Composition record (conditional branches apply; this is not an unconditional requirement)
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 3.0 |
| Ni | 10.0 ～ 12.5 |
| N | 0.12 ～ 0.22 |
Applicability and limitations
ISO 15510:2014, Table 1 gives heat analysis, mass fractions wt%; Under note a, values without a stated range or minimum are maxima; a dash is not treated as zero. Composition rows follow an excerpt of the official PDF edition; relevant footnotes follow the original Table 1 in the Sample text section of the standards publishing platform; Verification of the complete standard text or mechanical properties is not claimed. The standard covers material for wrought products, including ingots and semi-finished products; Similar composition does not establish direct substitution; cold-heading suitability and supply condition require separate confirmation. The S 0.015–0.030% machinability recommendations, 0.008–0.020% weldability recommendation and S≤0.015% polishability recommendation in note b concern specific properties and do not directly replace this row’s sulfur limits. Note c applies only where ferrite content must be reduced for special reasons such as hot workability or low magnetic permeability; The increased Ni maximum is not treated as an unconditional range.
Original condition-branch records
Base range in Table 1
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 3.0 |
| Ni | 10.0 ～ 12.5 |
| N | 0.12 ～ 0.22 |
Note c: only where ferrite content must be reduced for a special reason, the Ni maximum may be increased by 1.00 percentage points; This condition must be confirmed
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 3.0 |
| Ni | 10.0 ～ 13.5 |
| N | 0.12 ～ 0.22 |
A condition branch must be selected
YesVerification notes
The row for this grade in Table 1 has been checked against the official PDF; Relevant original footnotes are retained in the supporting verification record; Full standard text and mechanical properties to be verified separatelyX2CrNiMoN17-11-2 · EN 10088-1-2005
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- EN 10088-1-2005
- Table / clause
- Table 4 and continuation; notes a–e; all 50 austenitic corrosion-resistant steel grades
- PDF page references
- 1、3、11、12
Carbon-equivalent reference
Estimates are presented separately for each applicable composition condition. Match the actual ordering conditions; ranges must not be combined.
Default sulfur requirement; default Ni; the cold-heading Cu exception is not selected, so the original-table Cu requirement applies.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Default sulphur requirement; default Ni; note c: Cu≤1.0% for cold heading/cold extrusion.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Default sulfur requirement; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Default sulfur requirement; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b, S for long products/wire etc.: ≤0.030%Default Ni; cold-heading Cu exception not selected, so the original-table Cu requirement applies.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b, S for long products/wire etc.: ≤0.030%Default Ni; note c allows Cu≤1.0% for cold heading/cold extrusion.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b: S≤.030 applies to long products, wire and the other stated forms; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b: S≤.030 applies to long products, wire and the other stated forms; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b, recommended S for machining: 0.015–0.030%Default Ni; cold-heading Cu exception not selected, so the original-table Cu requirement applies.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b, recommended S for machining: 0.015–0.030%Default Ni; note c allows Cu≤1.0% for cold heading/cold extrusion.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b: S .015–.030 is recommended for machining; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b: S .015–.030 is recommended for machining; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b, recommended S for welding: 0.008–0.030%Default Ni; cold-heading Cu exception not selected, so the original-table Cu requirement applies.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b, recommended S for welding: 0.008–0.030%Default Ni; note c allows Cu≤1.0% for cold heading/cold extrusion.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b: S .008–.030 is recommended for welding; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b: S .008–.030 is recommended for welding; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b, recommended S for polishing: ≤0.015%Default Ni; cold-heading Cu exception not selected, so the original-table Cu requirement applies.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b, recommended S for polishing: ≤0.015%Default Ni; note c allows Cu≤1.0% for cold heading/cold extrusion.
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b: S≤.015 is recommended for polishing; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Note b: S≤.015 is recommended for polishing; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Composition record (conditional branches apply; this is not an unconditional requirement)
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
Applicability and limitations
EN 10088-1:2005 Table 4 and continuation: ladle analysis (wt%); the official SIST adoption preview PDF, pages 11/12, covers all 50 grades and notes. Note a: unlisted elements are not intentionally added without purchaser consent, except as needed to complete steelmaking; a blank is not zero. Note b: for grades marked b only, S is selected separately for long products and by property requirement. Note d: the increased Ni maximum for special reasons applies only to listed grades, not all grades. Note c: Cu up to 1.0% for cold heading/extrusion; this condition path is provided here only for grades with blank Cu in the original table. Existing Cu alloy ranges retain their original values; the exception has not automatically rewritten them. The linked Ti≥5C/Nb≥10C and Ti≥8(C+N) conditions are retained; an unlisted N maximum is not zero. Note e: the source warns of skin-contact regulatory issues for high-sulfur free-machining steel; this is retained as a historical warning only and is not a claim of current compliance based on the 2005 text. Listed chemistry and the cold-heading Cu exception alone do not establish overall cold-heading performance or company supply; mechanical and product standards must be checked separately, and national adoption does not mean automatic equivalence.
Original condition-branch records
Default sulfur requirement; default Ni; the cold-heading Cu exception is not selected, so the original-table Cu requirement applies.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
Default sulphur requirement; default Ni; note c: Cu≤1.0% for cold heading/cold extrusion.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
Default sulfur requirement; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
Default sulfur requirement; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
Note b, S for long products/wire etc.: ≤0.030%Default Ni; cold-heading Cu exception not selected, so the original-table Cu requirement applies.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
Note b, S for long products/wire etc.: ≤0.030%Default Ni; note c allows Cu≤1.0% for cold heading/cold extrusion.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
Note b: S≤.030 applies to long products, wire and the other stated forms; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
Note b: S≤.030 applies to long products, wire and the other stated forms; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
Note b, recommended S for machining: 0.015–0.030%Default Ni; cold-heading Cu exception not selected, so the original-table Cu requirement applies.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | 0.015 ～ 0.03 |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
Note b, recommended S for machining: 0.015–0.030%Default Ni; note c allows Cu≤1.0% for cold heading/cold extrusion.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | 0.015 ～ 0.03 |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
Note b: S .015–.030 is recommended for machining; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | 0.015 ～ 0.03 |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
Note b: S .015–.030 is recommended for machining; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | 0.015 ～ 0.03 |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
Note b, recommended S for welding: 0.008–0.030%Default Ni; cold-heading Cu exception not selected, so the original-table Cu requirement applies.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | 0.008 ～ 0.03 |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
Note b, recommended S for welding: 0.008–0.030%Default Ni; note c allows Cu≤1.0% for cold heading/cold extrusion.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | 0.008 ～ 0.03 |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
Note b: S .008–.030 is recommended for welding; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | 0.008 ～ 0.03 |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
Note b: S .008–.030 is recommended for welding; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | 0.008 ～ 0.03 |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
Note b, recommended S for polishing: ≤0.015%Default Ni; cold-heading Cu exception not selected, so the original-table Cu requirement applies.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
Note b, recommended S for polishing: ≤0.015%Default Ni; note c allows Cu≤1.0% for cold heading/cold extrusion.
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 12.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
Note b: S≤.015 is recommended for polishing; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; The cold-heading Cu exception has not been selected; the original table requires Cu
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
Note b: S≤.015 is recommended for polishing; Note d: Ni increases 1% under specified low-permeability, processing or other special conditions; Note c: Cu≤1.0% applies when used for cold heading or cold extrusion
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| N | 0.12 ～ 0.22 |
| Cr | 16.5 ～ 18.5 |
| Mo | 2.0 ～ 2.5 |
| Ni | 10.0 ～ 13.5 |
| Cu | ≤ 1.0 (lower limit not stated) |
A condition branch must be selected
YesVerification notes
Official source Table 4, all 50 rows and footnotes visually checked; conditional route for Cu cells left blank in the original.X2CrNiMoN17-11-2 · EN 10028-7-2016
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 16.5 ～ 18.5 |
| Mn | ≤ 2 (lower limit not stated) |
| Mo | 2 ～ 2.5 |
| N | 0.12 ～ 0.22 |
| Ni | 10 ～ 12.5 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
X2CrNiMoN17-11-2 · EN 10088-2-2005
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 16.5 ～ 18.5 |
| Mn | ≤ 2 (lower limit not stated) |
| Mo | 2 ～ 2.5 |
| N | 0.1 ～ 0.22 |
| Ni | 10 ～ 12.5 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
X2CrNiMoN17-11-2 · EN 10088-2-2024
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 16.5 ～ 18.5 |
| Mn | ≤ 2 (lower limit not stated) |
| Mo | 2 ～ 2.5 |
| N | 0.12 ～ 0.22 |
| Ni | 10 ～ 12.5 |
| P | ≤ 0.045 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
X2CrNiMoN17-11-2 · EN 10272-2016
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 16.5 ～ 18.5 |
| Mn | ≤ 2 (lower limit not stated) |
| Mo | 2 ～ 2.5 |
| N | 0.12 ～ 0.22 |
| Ni | 10 ～ 12.5 |
| P | ≤ 0.045 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
X2CrNiMoN17-11-2 · NF EN 10028-7-2000
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 16.5 ～ 18.5 |
| Mn | ≤ 2 (lower limit not stated) |
| Mo | 2 ～ 2.5 |
| N | 0.12 ～ 0.22 |
| Ni | 10 ～ 12 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
X2CrNiMoN17-11-2 · NF EN 10028-7-2008
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 16.5 ～ 18.5 |
| Mn | ≤ 2 (lower limit not stated) |
| Mo | 2 ～ 2.5 |
| N | 0.12 ～ 0.22 |
| Ni | 10 ～ 12.5 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
X2CrNiMoN17-11-2 · NF EN 10088-2-2005
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 16.5 ～ 18.5 |
| Mn | ≤ 2 (lower limit not stated) |
| Mo | 2 ～ 2.5 |
| N | 0.12 ～ 0.22 |
| Ni | 10 ～ 12.5 |
| P | ≤ 0.045 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
X2CrNiMoN17-11-2 · ISO 9328-7-2018
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 16.5 ～ 18.5 |
| Mn | ≤ 2 (lower limit not stated) |
| Mo | 2 ～ 2.5 |
| N | 0.12 ～ 0.22 |
| Ni | 10 ～ 12.5 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
X2CrNiMoN17-11-2 · ISO TS 15510-2003
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
IIW / CEV: not directly applicable to this material category
Pcm (Ito–Bessyo): not directly applicable to this material category
CET: not directly applicable to this material category
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 16.5 ～ 18.5 |
| Mn | ≤ 2 (lower limit not stated) |
| Mo | 2 ～ 3 |
| N | 0.12 ～ 0.22 |
| P | ≤ 0.045 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.