2 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for SUSXM15J1 →SUSXM15J1 · JIS G 4308-2013
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Subcategory
- Austenitic stainless steel
- Material form
- Hot-rolled stainless-steel wire rod
- Original record status
- Original standard verified
- Standard edition
- JIS G 4308:2013
- Table / clause
- Table 1 · Grade designations; Table 2 · Chemical composition / Footnotes
- PDF page references
- 4、5
- Unit
- Mass fraction (%)
- Analysis type
- Heat analysis
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Si | 3.0 ～ 5.0 |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Ni | 11.5 ～ 15.0 |
| Cr | 15.0 ～ 20.0 |
Applicability and limitations
The original Japanese edition JIS G 4308:2013, Table 2, row 23, heat-analysis mass percentages. ; The standard covers hot-rolled stainless steel wire rod; Product-analysis tolerances must be checked under JIS G 0321 and purchaser requirements; tolerances are not included in the default heat-analysis range. ; Material designation and chemical composition do not establish cold-heading suitability or a supply commitment from Creation Group; Dimensions, delivery and processing condition require separate verification. ; Table 2, footnote: where these unlisted elements are added as needed, their contents must be reported; No general limits are specified, and no values are inserted.
Verification notes
The grades in original Table 1–6, the heat-analysis table and footnotes were visually checked row by row; Cu/Mo/Nb/Ti/N if added reportSUSXM15J1 · JIS G 4305-2021
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- JIS G 4305-2021
- Table / clause
- Table 3 · Footnotes; 5.1/5.2
- PDF page references
- 7、9
- Unit
- Mass fraction (wt%)
- Analysis type
- Heat analysis, not product analysis
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Si | 3 ～ 5 |
| Mn | ≤ 2 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Ni | 11.5 ～ 15 |
| Cr | 15 ～ 20 |
Applicability and limitations
JIS G 4305:2021, Table 3, heat analysis, mass fractions wt%; Each actual edition is retained separately. Applicable to cold-rolled stainless steel plate, sheet and strip; this does not establish suitability for delivery as cold-heading wire or guarantee cold-heading process performance. 5.2 product analysis permits variations under JIS G0321, Table 5; unlisted items require agreement between the parties; Heat-analysis limits are not directly widened in this batch. A dash indicates that no general limit is specified and is not treated as 0; Conventional welding carbon-equivalent formulas for low-alloy steels do not apply to this stainless steel category. Original table note: where unspecified Cu/Mo/Nb/Ti/N is added as needed, its content must be reported; No general limit is specified; a guaranteed range is not invented.