SUS430F
2 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for SUS430F →SUS430F · JIS G 4308-2013
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Subcategory
- Ferritic stainless steel
- Material form
- Hot-rolled stainless-steel wire rod
- Original record status
- Original standard verified
- Standard edition
- JIS G 4308:2013
- Table / clause
- Table 1 · Grade designations; Table 4 · Chemical composition / Footnotes
- PDF page references
- 4、5
- Unit
- Mass fraction (%)
- Analysis type
- Heat analysis
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.12 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 1.25 (lower limit not stated) |
| P | ≤ 0.06 (lower limit not stated) |
| S | ≥ 0.15 (upper limit not stated) |
| Ni | ≤ 0.6 (lower limit not stated) |
| Cr | 16.0 ～ 18.0 |
| Mo | ≤ 0.6 (lower limit not stated) |
Applicability and limitations
The original Japanese edition JIS G 4308:2013, Table 4, row 3, heat-analysis mass percentages. ; The standard covers hot-rolled stainless steel wire rod; Product-analysis tolerances must be checked under JIS G 0321 and purchaser requirements; tolerances are not included in the default heat-analysis range. ; Material designation and chemical composition do not establish cold-heading suitability or a supply commitment from Creation Group; Dimensions, delivery and processing condition require separate verification. ; Original footnote: the Mo maximum has been recorded according to the table footnote.
Verification notes
The grades in original Table 1–6, the heat-analysis table and footnotes were visually checked row by row; Mo footnote aSUS430F · JIS G 4308-1998
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Subcategory
- Ferritic stainless steel
- Material form
- Stainless-steel wire rod
- Original record status
- Original standard verified
- Standard edition
- JIS G 4308:1998
- Table / clause
- Main text: Table 1 / Table 3 · Footnotes
- PDF page references
- 1、2
- Unit
- Mass fraction (%)
- Analysis type
- Heat analysis
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.12 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 1.25 (lower limit not stated) |
| P | ≤ 0.06 (lower limit not stated) |
| S | ≥ 0.15 (upper limit not stated) |
| Cr | 16.0 ～ 18.0 |
Applicability and limitations
The original scanned Japanese edition JIS G 4308:1998 lists SUS430F in main-text Table 1; main-text Table 3 gives heat-analysis mass percentages. ; This edition covers stainless steel wire rod; reference suffix -WR is not a separate default grade; Standard wire diameters are in Table 6; product-analysis tolerances require separate verification under Clause 4.2. ; Table 3, remark: Ni≤0.60% is a permitted-content condition, not a default composition. ; Table 3, footnote: Mo≤0.60% is only a permitted-addition condition. ; This does not establish cold-heading suitability, stock dimensions or a supply guarantee from Creation Group.