SUS316N
1 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for SUS316N →SUS316N · JIS G 4305-2021
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- JIS G 4305-2021
- Table / clause
- Table 3 · Footnotes; 5.1/5.2
- PDF page references
- 7、8
- Unit
- Mass fraction (wt%)
- Analysis type
- Heat analysis, not product analysis
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Mn | ≤ 2 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Ni | 10 ～ 14 |
| Cr | 16 ～ 18 |
| Mo | 2 ～ 3 |
| N | 0.1 ～ 0.22 |
Applicability and limitations
JIS G 4305:2021, Table 3, heat analysis, mass fraction wt%; each actual edition is retained separately. Applicable to cold-rolled stainless steel plate, sheet and strip; this does not establish suitability for delivery as cold-heading wire or guarantee cold-heading performance. 5.2 product analysis permits variations under JIS G0321, Table 5; unlisted items require agreement between the parties. These variations are not added to the heat-analysis limits in this batch. A dash indicates that no general limit is specified; it is not treated as 0. Conventional welding carbon-equivalent formulas for low-alloy steels do not apply to this stainless steel category.