SUS 410
7 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for SUS 410 →SUS 410 · JIS G 4305-2021
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Stainless steel
- Subcategory
- Martensitic stainless steel
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- JIS G 4305-2021
- Table / clause
- Table 6 · Footnotes; 5.1/5.2
- PDF page references
- 7、10
- Unit
- Mass fraction (wt%)
- Analysis type
- Heat analysis, not product analysis
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.15 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Mn | ≤ 1 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Ni | ≤ 0.6 (lower limit not stated) |
| Cr | 11.5 ～ 13.5 |
Applicability and limitations
JIS G 4305:2021, Table 6, heat analysis, mass fraction wt%; each actual edition is retained separately. Applicable to cold-rolled stainless steel plate, sheet and strip; this does not establish suitability for delivery as cold-heading wire or guarantee cold-heading performance. 5.2 product analysis permits variations under JIS G0321, Table 5; unlisted items require agreement between the parties. These variations are not added to the heat-analysis limits in this batch. A dash indicates that no general limit is specified; it is not treated as 0. Conventional welding carbon-equivalent formulas for low-alloy steels do not apply to this stainless steel category.
Verification notes
2021 Japanese original Tables 3–7, chemical composition, footnotes and clauses 5.1/5.2 checked; sheet and strip scope retained.SUS 410 · JIS G 4308-2013
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Stainless steel
- Subcategory
- Martensitic stainless steel
- Material form
- Hot-rolled stainless-steel wire rod
- Original record status
- Original standard verified
- Standard edition
- JIS G 4308:2013
- Table / clause
- Table 1 · Grade designations; Table 5 · Chemical composition / Footnotes
- PDF page references
- 4、6
- Unit
- Mass fraction (%)
- Analysis type
- Heat analysis
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.15 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Mn | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Ni | ≤ 0.6 (lower limit not stated) |
| Cr | 11.5 ～ 13.5 |
Applicability and limitations
JIS G 4308:2013, Japanese original, Table 5, row 2, cast-analysis mass fraction %. The standard covers stainless-steel hot-rolled wire rod. Product-analysis deviations must be checked under JIS G 0321 and purchaser requirements; deviations must not be added to the default cast-analysis range. Grade designation and chemistry do not establish cold-heading suitability or a supply commitment by our company; dimensions, delivery and process condition require separate verification.
Verification notes
The grades in original Table 1–6, the heat-analysis table and footnotes were visually checked row by row; The existing same-edition reference record retains ID and is superseded by the original standard table.SUS 410 · JIS G 4303-2005
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Martensitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.15 (lower limit not stated) |
| Cr | 11.5 ～ 13.5 |
| Mn | ≤ 1 (lower limit not stated) |
| Ni | ≤ 0.6 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A material-database match does not establish cold-heading suitability or a finished-product strength commitment; Confirmation requires the actual wire condition, reduction, heat treatment and physical testing. ; The original Japanese 2005, Table 1 confirms this bar-grade designation; Composition and property sources require separate verification under Table 2—6 and the applicable condition.
SUS 410 · JIS G 4304-2005
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Martensitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.15 (lower limit not stated) |
| Cr | 11.5 ～ 13.5 |
| Mn | ≤ 1 (lower limit not stated) |
| Ni | ≤ 0.6 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
SUS 410 · JIS G 4315-2000
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Martensitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.15 (lower limit not stated) |
| Cr | 11.5 ～ 13.5 |
| Mn | ≤ 1 (lower limit not stated) |
| Ni | ≤ 0.6 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
SUS 410 · JIS G 4318-2016
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Martensitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.15 (lower limit not stated) |
| Cr | 11.5 ～ 13.5 |
| Mn | ≤ 1 (lower limit not stated) |
| Ni | ≤ 0.6 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
SUS 410 · Q/BQB 4302-2009
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Martensitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.15 (lower limit not stated) |
| Cr | 11.5 ～ 13.5 |
| Mn | ≤ 1 (lower limit not stated) |
| Ni | ≤ 0.6 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.