SUS 410-W2
1 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for SUS 410-W2 →SUS 410-W2 · JIS G 4309-2013
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Martensitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.15 (lower limit not stated) |
| Cr | 11.5 ～ 13.5 |
| Mn | ≤ 1 (lower limit not stated) |
| Ni | ≤ 0.6 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
Table 1 of the Japanese original text of JIS G 4309:2013 lists SUS410 and W2 temper condition, classified as martensitic stainless steel. ; Main-text Table 2: W2 applies to wire diameters 0.80–14.0 mm; W1/W2/W1/2H shall not be used interchangeably. ; Clause 4 of the main text references the chemical composition in Clause 5 of JIS G 4308 or JIS G 4311; Annex JA is a wire-composition reference only, not an independent mandatory limit for the finished steel wire covered by this standard. ; Mechanical properties by wire diameter in the main text and composition in Appendix JA have not yet been verified condition-by-condition in this clause; Supply or performance guarantees shall not be inferred from this clause. ; Existing compositions remain as reference transcriptions and have not been upgraded to cell-by-cell verification against the original text.