SUS 405-W2
1 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for SUS 405-W2 →SUS 405-W2 · JIS G 4309-2013
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Ferritic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.1 ～ 0.3 |
| C | ≤ 0.08 (lower limit not stated) |
| Cr | 11.5 ～ 14.5 |
| Mn | ≤ 1 (lower limit not stated) |
| Ni | ≤ 0.6 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
Table 1 of the main text of the original Japanese version of JIS G 4309:2013 lists SUS405, W2 temper condition, classified as ferritic stainless steel. ; Main-text Table 2: W2 applies to wire diameters 0.80–14.0 mm; W1/W2/W1/2H shall not be used interchangeably. ; Clause 4 of the main text references the chemical composition in Clause 5 of JIS G 4308 or JIS G 4311; Annex JA is a wire-composition reference only, not an independent mandatory limit for the finished steel wire covered by this standard. ; Mechanical properties by wire diameter in the main text and composition in Appendix JA have not yet been verified condition-by-condition in this clause; Supply or performance guarantees shall not be inferred from this clause. ; Table 1 Note a: the remark in this edition is intended for consideration of deleting SUS405 in the next revision; Still included in the 2013 edition. ; Existing compositions remain as reference transcriptions and have not been upgraded to cell-by-cell verification against the original text.