SUS 304N1-W1/2H
1 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for SUS 304N1-W1/2H →SUS 304N1-W1/2H · JIS G 4309-2013
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Cr | 18 ～ 20 |
| Mn | ≤ 2.5 (lower limit not stated) |
| N | 0.1 ～ 0.25 |
| Ni | 7 ～ 10.5 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
JIS G 4309:2013: main-text Table 1 of the Japanese original lists tempers SUS304N1 and W1/2H, classified as austenitic stainless steel. Main-text Table 2: W1/2H applies to wire diameters 0.80–6.00 mm; W1/W2/W1/2H must not be mixed. Main-text clause 4 references the chemical-composition requirements in clause 5 of JIS G 4308 or JIS G 4311. Annex JA gives wire-rod composition references only, not independent mandatory limits for the finished wire. Mechanical properties by wire diameter and Annex JA composition have not been entered condition by condition in this record; no supply or performance guarantee is inferred. Existing composition remains a reference transcription and has not been upgraded to cell-by-cell original-source verification.