SUJ2
4 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for SUJ2 →SUJ2 · JIS G4805
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material form
- Wire rod
- Original record status
- Reference transcription of standard
- Standard edition
- JIS G 4805:2008
- Table / clause
- Table 1
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | 0.95 ～ 1.1 |
| Si | 0.15 ～ 0.35 |
| Mn | ≤ 0.5 (lower limit not stated) |
| P | ≤ 0.025 (lower limit not stated) |
| S | ≤ 0.025 (lower limit not stated) |
| Cr | 1.3 ～ 1.6 |
| Mo | ≤ 0.08 (lower limit not stated) |
| Ni | ≤ 0.25 (lower limit not stated) |
| Cu | ≤ 0.2 (lower limit not stated) |
Applicability and limitations
JIS G 4805:2008; Heat analysis, mass percent; See the original page for table notes and applicability conditions. This record concerns wire rod, under note a, Cu≤0.20%; Non-wire-rod maximum 0.25%. No edition is stated on the website; Displayed under this source edition; contract applicability is not established
Verification notes
Standard source: JIS G 4805:2008 · Table 1View associated products →SUJ2 · JIS G 4805:2008
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Alloy steel
- Subcategory
- High-carbon chromium bearing steel
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- JIS G 4805:2008
- Table / clause
- Table 1 and notes a–d; 4c
Carbon-equivalent reference
Estimates are presented separately for each applicable composition condition. Match the actual ordering conditions; ranges must not be combined.
Wire rod, heat analysis, Table 1, note a Cu≤0.20%
Steel products other than wire rod, heat analysis, Table 1, note a Cu≤0.25%
Composition record (conditional branches apply; this is not an unconditional requirement)
| Element | Composition requirement |
|---|---|
| C | 0.95 ～ 1.1 |
| Si | 0.15 ～ 0.35 |
| Mn | ≤ 0.5 (lower limit not stated) |
| P | ≤ 0.025 (lower limit not stated) |
| S | ≤ 0.025 (lower limit not stated) |
| Cr | 1.3 ～ 1.6 |
| Mo | ≤ 0.08 (lower limit not stated) |
| Ni | ≤ 0.25 (lower limit not stated) |
| Cu | ≤ 0.25 (lower limit not stated) |
Applicability and limitations
Table 1 Heat analysis, unit mass fraction %. ; Note a: Ni/Cu each ≤0.25%, with Cu≤0.20% for wire rod.. ; Note b: except for the purpose of deoxidation, elements not specified shall not be intentionally added without agreement between both parties; Agreement may allow addition of elements outside the table up to 0.25%, which cannot be presumed as a general guaranteed upper limit for all residual elements. ; Note c: When product analysis is required by the purchaser, it shall be tested according to 14.1; permissible deviations shall be per JIS G0321 Table 4; Heat analysis limits cannot be directly used as product analysis tolerances. ; Note d: Mo impurity for SUJ2/3 ≤0.08%. ; Under 4c, spheroidizing annealing is normally performed but may be omitted when specified by the purchaser.; This manufacturing condition clause itself is not proof that all parts are suitable for cold heading.
Original condition-branch records
Wire rod, heat analysis, Table 1, note a Cu≤0.20%
| Element | Composition requirement |
|---|---|
| C | 0.95 ～ 1.1 |
| Si | 0.15 ～ 0.35 |
| Mn | ≤ 0.5 (lower limit not stated) |
| P | ≤ 0.025 (lower limit not stated) |
| S | ≤ 0.025 (lower limit not stated) |
| Cr | 1.3 ～ 1.6 |
| Mo | ≤ 0.08 (lower limit not stated) |
| Ni | ≤ 0.25 (lower limit not stated) |
| Cu | ≤ 0.2 (lower limit not stated) |
Steel products other than wire rod, heat analysis, Table 1, note a Cu≤0.25%
| Element | Composition requirement |
|---|---|
| C | 0.95 ～ 1.1 |
| Si | 0.15 ～ 0.35 |
| Mn | ≤ 0.5 (lower limit not stated) |
| P | ≤ 0.025 (lower limit not stated) |
| S | ≤ 0.025 (lower limit not stated) |
| Cr | 1.3 ～ 1.6 |
| Mo | ≤ 0.08 (lower limit not stated) |
| Ni | ≤ 0.25 (lower limit not stated) |
| Cu | ≤ 0.25 (lower limit not stated) |
A condition branch must be selected
YesVerification notes
PDF, page 4, Table 1 and footnotes have been checkedSUJ2 · Nippon Steel Wire Rods EXE203 2008.3 / JIS G4805-1999
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Bearing steel
- Subcategory
- Bearing steel
- Material form
- Wire rod
- Original record status
- Manufacturer source verified
- Document edition
- Cat. No. EXE203 2008.3 PDF; cover copyright 2008
- Document title
- Nippon Steel Wire Rods
- Table / clause
- Printed page 19, table index 1
- PDF page references
- 11
- Unit
- Mass fraction (%)
- Analysis type
- The original catalogue does not explicitly identify the analysis type for this table
- Manufacturer
- NIPPON STEEL CORPORATION
Carbon-equivalent reference
Estimate from manufacturer-published ranges, not a standard guarantee or measured heat result; formula applicability requires review against the application and process.
Composition
| Element | Composition requirement |
|---|---|
| C | 0.95 ～ 1.1 |
| Si | 0.15 ～ 0.35 |
| Mn | ≤ 0.5 (lower limit not stated) |
| P | ≤ 0.025 (lower limit not stated) |
| S | ≤ 0.025 (lower limit not stated) |
| Cr | 1.3 ～ 1.6 |
| Ni | ≤ 0.25 (lower limit not stated) |
| Cu | ≤ 0.2 (lower limit not stated) |
| Mo | ≤ 0.08 (lower limit not stated) |
Applicability and limitations
Historical Nippon Steel wire-rod catalogue EXE203 2008.3, PDF page 11
printed page 19, JIS G4805-1999. The original catalogue does not explicitly identify the analysis type for this table. Manufacturer range data, not guaranteed standard limits or heat-specific measurements; this does not establish supply by Creation Group. Condition: original bearing-steel note, Cu is generally ≤0.25, with a specific wire-rod limit ≤0.20%; Wire-rod condition selected.
Composition conditions
- Original catalogue mass percentages, historical manufacturer data from 2008.3; Referenced standard names and editions follow the original document; this does not establish that the official texts of those standards have been obtained and verified.
- A dash or blank must not be treated as 0; only chemical composition has been checked in this batch. Mechanical properties and actual supply require separate verification under the applicable conditions.
- Original bearing-steel note: Cu is generally ≤0.25, with a specific wire-rod limit ≤0.20%; Wire-rod condition selected.
Verification notes
Grouped tables were expanded in full and checked against original images and notes. Ordinary, residual and conditional elements are kept separate; suffix tables lacking complete base-steel composition are excluded.SUJ2 · CHINA STEEL CORPORATION · Bars and Wire Rods Product Catalogue 2014-C1 / 7.1.13 JIS G4805 (Edition unspecified)
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Bearing steel
- Subcategory
- Bearing steel
- Material form
- Bars and wire rod
- Original record status
- Manufacturer source verified
- Document edition
- CAT.NO.3-BD-01-2014-C1 (stated on the back cover)
- Document title
- Bars and Wire Rods Product Catalogue
- Table / clause
- 7.1.13 JIS G4805 (Edition unspecified)
- PDF page references
- 21
- Unit
- Mass fraction (%)
- Analysis type
- The original catalogue does not explicitly identify the analysis type for this table
- Manufacturer
- CHINA STEEL CORPORATION
Carbon-equivalent reference
Estimate from manufacturer-published ranges, not a standard guarantee or measured heat result; formula applicability requires review against the application and process.
Composition
| Element | Composition requirement |
|---|---|
| C | 0.95 ～ 1.1 |
| Si | 0.15 ～ 0.35 |
| Mn | ≤ 0.5 (lower limit not stated) |
| P | ≤ 0.025 (lower limit not stated) |
| S | ≤ 0.025 (lower limit not stated) |
| Cr | 1.3 ～ 1.6 |
| Mo | ≤ 0.08 (lower limit not stated) |
| Ni | ≤ 0.25 (lower limit not stated) |
| Cu | ≤ 0.2 (lower limit not stated) |
Applicability and limitations
China Steel bar and wire-rod catalogue CAT.NO.3-BD-01-2014-C1, PDF page 21
printed page 19, 7.1.13 JIS G4805 (edition not stated). The original catalogue does not explicitly identify the analysis type for this table. Historical manufacturer range data, not guaranteed standard limits or heat-specific measurements; this does not establish supply by Creation Group. Condition: each alloying element added by agreement is ≤0.25%; this option does not automatically add unknown elements.
Composition conditions
- Historical manufacturer 2014-C1 catalogue, bars/wire rod; Where the referenced standard edition is not identified, a year is not borrowed from another catalogue; a catalogue is not upgraded to the official standard text.
- A dash or blank must not be treated as zero. Composition data do not establish completeness or applicability of a formula; mechanical properties and supply require separate verification.
- Each alloying element added by agreement is ≤0.25%; this option does not automatically add unknown elements.