SGD3

1 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.

Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.

Open condition selection, comparison and carbon-equivalent tools for SGD3 →

SGD3 · Nippon Steel Wire Rods EXE203 2008.3 / JIS G3108-2004

Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results

Material category: Carbon steel
Subcategory: Carbon steel
Material form: Wire rod
Original record status: Manufacturer source verified
Document edition: Cat. No. EXE203 2008.3 PDF; cover copyright 2008
Document title: Nippon Steel Wire Rods
Table / clause: Printed page 14, table index 2
PDF page references: 9
Unit: Mass fraction (%)
Analysis type: Heat analysis (identified as ladle analysis in the original table)
Manufacturer: NIPPON STEEL CORPORATION

Carbon-equivalent reference

Estimate from manufacturer-published ranges, not a standard guarantee or measured heat result; formula applicability requires review against the application and process.

IIW / CEV：0.2000–0.3000 Known-item contribution, not a complete value; missing Cr, Mo, V, Ni, Cu CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.

Pcm（Ito–Bessyo）：0.1650–0.2300Known-element contribution; incomplete value; missing Si, Cu, Cr, Ni, Mo, V, B Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.

CET：0.1800–0.2600 Known-item contribution, not a complete value; missing Mo, Cr, Cu, Ni CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.

Composition

Element	Composition requirement
C	0.15 ～ 0.2
Mn	0.3 ～ 0.6
P	≤ 0.045 (lower limit not stated)
S	≤ 0.045 (lower limit not stated)

Applicability and limitations

Historical Nippon Steel wire-rod catalogue EXE203 2008.3, PDF page 9

printed page 14, JIS G3108-2004. Heat analysis (labeled Ladle in the original table).. Manufacturer range data, not guaranteed standard limits or heat-specific measurements; this does not establish supply by Creation Group. Condition: C/Mn not specified in the original table for SGDA/SGDB; Other grades Mn 0.60–0.90 require M suffix agreement; Do not borrow or supplement with zero. The mechanical properties table includes diameter and specimen conditions; these are not flattened as guaranteed values for this batch.

Composition conditions

Original catalogue mass percentages, historical manufacturer data from 2008.3; Referenced standard names and editions follow the original document; this does not establish that the official texts of those standards have been obtained and verified.
A dash or blank must not be treated as 0; only chemical composition has been checked in this batch. Mechanical properties and actual supply require separate verification under the applicable conditions.
C/Mn not specified in the original table for SGDA/SGDB; Other grades Mn 0.60–0.90 require M suffix agreement; Do not borrow or supplement with zero. The mechanical properties table includes diameter and specimen conditions; these are not flattened as guaranteed values for this batch.

Verification notes

Grouped tables were expanded in full and checked against original images and notes. Ordinary, residual and conditional elements are kept separate; suffix tables lacking complete base-steel composition are excluded.