SCM415H

7 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.

Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.

Open condition selection, comparison and carbon-equivalent tools for SCM415H →

Reference summary and sources

SCM415H material reference: 7 source records. Composition, standard editions, conditions and verification status are shown separately. Matching grade names do not establish interchangeability; missing values are not treated as zero.

This page is a material-selection reference, not a material certificate or supply guarantee. Mass fractions, analysis types and limitations are stated separately for each source. Material whose original source has not been verified is not treated as a standard guarantee.

View all 7 source records

SCM415H · JIS G 4052-2008
SCM415H · Q/BQB 517-2023
SCM415H · Q/320582 SGY503-2024 (1st edition)
SCM415H · BEXG 021-2020
SCM415H · Nippon Steel Wire Rods EXE203 2008.3 / JIS G4052-2003
SCM415H · Nippon Steel Wire Rods EXE203 2008.3 / JASO M106-92
SCM415H · CHINA STEEL CORPORATION · Bars and Wire Rods Product Catalogue 2014-C1 / 7.1.10 JIS G4052 (Edition unspecified)

SCM415H · JIS G 4052-2008

Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results

Material form: Reference record
Original record status: Original standard verified
Standard edition: JIS G 4052-2008
Table / clause: Table 2 and note a/b, Clause 1/5
PDF page references: 3、5

Carbon-equivalent reference

IIW / CEV：0.4117–0.6850Known-element contribution; incomplete value; missing V CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.

Pcm（Ito–Bessyo）：0.2050–0.3408Known-element contribution; incomplete value; missing V, B Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.

CET：0.2325–0.3888 Independent-element envelope of standard ranges; not measured heat-analysis values CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.

Composition

Element	Composition requirement
C	0.12 ～ 0.18
Si	0.15 ～ 0.35
Mn	0.55 ～ 0.95
P	≤ 0.03 (lower limit not stated)
S	≤ 0.03 (lower limit not stated)
Ni	≤ 0.25 (lower limit not stated)
Cr	0.85 ～ 1.25
Mo	0.15 ～ 0.3
Cu	≤ 0.3 (lower limit not stated)

Applicability and limitations

JIS G4052:2008 official Japanese original, Table 2 and Notes a/b; heat analysis, mass fraction wt%.; H in each grade represents a guaranteed hardenability band and shall not be merged with non-H grades. ; Table 2 Note a: residual Cu≤.30% for all grades; Unspecified elements such as Mo shall not have a uniform upper limit added independently, and shall not be calculated as zero. ; Note b: If product analysis is agreed by both parties, test under 8.1 and apply the permissible variations in JIS G0321 Table 4.; Do not add these variations to the default heat-analysis range.. ; Hot-worked structural steels such as hot-rolled/hot-forged, usually subject to further forging, machining, and heat treatment; Composition does not independently prove suitability for cold-heading or supply. ; Hardenability Tables 10–33, austenitic grain size and other technical conditions require separate verification; this update supplements composition information..

Verification notes

All 24 grades and footnotes in original Japanese Table 2 were visually checked

SCM415H · Q/BQB 517-2023

Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results

Material category: Alloy steel
Subcategory: Cold-heading steel
Material form: Hot-rolled steel wire rod for cold heading
Original record status: Original standard verified
Standard edition: Q/BQB 517—2023
Table / clause: 6.1.1/Table 1, row 82, note a
PDF page references: 11
Unit: Mass fraction (wt%)
Analysis type: Heat analysis

Source document

Carbon-equivalent reference

IIW / CEV：0.4400–0.6667Known-element contribution; incomplete value; missing V CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.

Pcm（Ito–Bessyo）：0.2200–0.3333Known-element contribution; incomplete value; missing V, B Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.

CET：0.2500–0.3800 Independent-element envelope of standard ranges; not measured heat-analysis values CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.

Composition

Element	Composition requirement
C	0.13 ～ 0.18
Si	0.15 ～ 0.35
Mn	0.6 ～ 0.9
P	≤ 0.02 (lower limit not stated)
S	≤ 0.02 (lower limit not stated)
Cr	0.9 ～ 1.2
Mo	0.15 ～ 0.35
Ni	≤ 0.2 (lower limit not stated)
Cu	≤ 0.2 (lower limit not stated)

Applicability and limitations

Q/BQB 517—2023, official original on the Baosteel website, Table 1, row 82; cast-analysis mass fraction wt%. Table footnote a: residual Cr≤0.20, Ni≤0.20, Cu≤0.20, Mo≤0.06 wt%; where this row specifies otherwise, its requirement for that element takes precedence. Unlisted elements and special agreement requirements must not be treated as zero or assumed guarantees; permitted product-analysis deviations are governed separately by GB/T 222. Wire rod is delivered hot rolled; stricter P/S under Z1 and special surface or inclusion quality must be confirmed under normative Annex A and the contractual ordering codes. Fixed mechanical properties must not be inferred from the chemistry table.

Verification notes

All 104 rows of Table 1 and 34 rows of Table 2 in the original Q/BQB517:2023 from Baosteel’s official website were checked row by row; not mixed with older editions.View associated products →

SCM415H · Q/320582 SGY503-2024 (1st edition)

Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results

Material category: Cold-heading steel
Subcategory: Cold-heading steel
Material form: Wire rod
Original record status: Manufacturer source verified
Document edition: Edition 1 (2024); issued 2024-04-26; effective 2024-05-01
Document title: Hot-rolled cold-heading steel wire rod for automotive fasteners
Table / clause: Table 1
PDF page references: 6
Unit: Mass fraction (wt%)
Manufacturer: Jiangsu Shagang Group Co., Ltd.

Carbon-equivalent reference

Estimate from manufacturer-published ranges, not a standard guarantee or measured heat result; formula applicability requires review against the application and process.

IIW / CEV：0.4400–0.6467Known-element contribution; incomplete value; missing V CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.

Pcm（Ito–Bessyo）：0.2200–0.3267Known-element contribution; incomplete value; missing V, B Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.

CET：0.2500–0.3700 Envelope of independent element limits from manufacturer data; neither standard guarantee values nor measured heat results CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.

Composition

Element	Composition requirement
C	0.13 ～ 0.18
Si	0.15 ～ 0.35
Mn	0.6 ～ 0.9
P	≤ 0.015 (lower limit not stated)
S	≤ 0.015 (lower limit not stated)
Cr	0.9 ～ 1.2
Mo	0.15 ～ 0.25
Ni	≤ 0.2 (lower limit not stated)
Cu	≤ 0.2 (lower limit not stated)

Applicability and limitations

Shagang Q/320582 SGY503-2024 (edition 1), Table 1, row 45 (PDF page 6), cast analysis wt%; original grades and values of this edition are shown independently. Orders and actual supply require separate confirmation; this is not a supply commitment by Creation Group.

Composition conditions

2024, 1st edition, Table 1: heat analysis, mass fraction wt%; a dash is not zero.
Clause 6.1.3 residual limits: Cr≤0.20%, Ni≤0.20%, Cu≤0.20%, Mo≤0.05%; where Table 1 specifies otherwise, follow the grade entry.
AlT is the lower limit for total aluminium; B has a separate column, and Ti, V, etc. are in notes; preserve grade suffixes exactly as printed in this edition.
Table 2: oxygen≤30×10⁻⁶ and nitrogen≤70×10⁻⁶; these are not alloy-element fields in mass fraction wt%.
Measured hardness and mechanical data in Clauses 6.10/6.11 are not delivery requirements; no generic properties are entered.

Verification notes

Manufacturer catalogue, 2024 edition 1: text extracted directly from the black original table and checked row by row; the blue public watermark was excluded from the extraction layer.

SCM415H · BEXG 021-2020

Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results

Material category: Cold-heading steel
Subcategory: Cold-heading steel
Material form: Wire rod
Original record status: Manufacturer source verified
Document edition: BEXG 021-2020, sixteenth revision stated on the cover; issued and effective on 2020-12-29; The latest original document available on this computer only
Document title: Technical delivery conditions for cold-heading steel wire rod for automotive parts
Table / clause: Table 1
PDF page references: 4
Unit: Mass fraction (wt%)
Manufacturer: Baoshan Iron & Steel Co., Ltd. (Baosteel)

Carbon-equivalent reference

Estimate from manufacturer-published ranges, not a standard guarantee or measured heat result; formula applicability requires review against the application and process.

CET：0.2500–0.3800 Envelope of independent element limits from manufacturer data; neither standard guarantee values nor measured heat results CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.

Composition

Element	Composition requirement
C	0.13 ～ 0.18
Si	0.15 ～ 0.35
Mn	0.6 ～ 0.9
P	≤ 0.025 (lower limit not stated)
S	≤ 0.025 (lower limit not stated)
Cr	0.9 ～ 1.2
Mo	0.15 ～ 0.35
Ni	≤ 0.2 (lower limit not stated)
Cu	≤ 0.2 (lower limit not stated)

Applicability and limitations

Baosteel BEXG 021-2020, Table 1, row 16, PDF page 4; heat-analysis composition in wt%, hot-rolled wire rod. 2020 is the original edition available locally, with no claim that it is the company’s current latest edition. Special conditions and actual supply require separate confirmation.

Composition conditions

Table 1 and its continuation give heat composition, in mass fractions wt%; The product is hot-rolled wire rod for automotive parts.
Unless expressly stated otherwise, residual Cr≤0.20%, Ni≤0.20%, Cu≤0.20% and Mo≤0.06% apply; Specific requirements in the table and additional notes take precedence.
A dash does not mean zero; Composition outside the table is not inferred from grade names or referenced standards.

Verification notes

Table 1 original images checked page by page, physical pages 3–10; continuation values and other columns kept separate; two disputed rows excluded.

Source footnotes

Mo:0.15-0.35View associated products →

SCM415H · Nippon Steel Wire Rods EXE203 2008.3 / JIS G4052-2003

Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results

Material category: Alloy steel
Subcategory: Alloy steel
Material form: Wire rod
Original record status: Manufacturer source verified
Document edition: Cat. No. EXE203 2008.3 PDF; cover copyright 2008
Document title: Nippon Steel Wire Rods
Table / clause: Printed page 18, table index 0
PDF page references: 11
Unit: Mass fraction (%)
Analysis type: The original catalogue does not explicitly identify the analysis type for this table
Manufacturer: NIPPON STEEL CORPORATION

Carbon-equivalent reference

Estimate from manufacturer-published ranges, not a standard guarantee or measured heat result; formula applicability requires review against the application and process.

CET：0.2325–0.3888 Envelope of independent element limits from manufacturer data; neither standard guarantee values nor measured heat results CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.

Composition

Element	Composition requirement
C	0.12 ～ 0.18
Si	0.15 ～ 0.35
Mn	0.55 ～ 0.95
P	≤ 0.03 (lower limit not stated)
S	≤ 0.03 (lower limit not stated)
Ni	≤ 0.25 (lower limit not stated)
Cr	0.85 ～ 1.25
Mo	0.15 ～ 0.3
Cu	≤ 0.3 (lower limit not stated)

Applicability and limitations

Nippon Steel wire-rod catalogue EXE203 2008.3, historical material; PDF p. 11

printed p. 18; JIS G4052-2003. The original catalogue does not specify the analysis type for this table. Manufacturer range data; not a standard guarantee or a heat-lot test, and does not represent our supply.

Composition conditions

Original catalogue mass percentages, historical manufacturer data from 2008.3; Referenced standard names and editions follow the original document; this does not establish that the official texts of those standards have been obtained and verified.
A dash or blank must not be treated as 0; only chemical composition has been checked in this batch. Mechanical properties and actual supply require separate verification under the applicable conditions.

Verification notes

Grouped tables were expanded in full and checked against original images and notes. Ordinary, residual and conditional elements are kept separate; suffix tables lacking complete base-steel composition are excluded.

SCM415H · Nippon Steel Wire Rods EXE203 2008.3 / JASO M106-92

Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results

Material category: Alloy steel
Subcategory: Alloy steel
Material form: Wire rod
Original record status: Manufacturer source verified
Document title: Nippon Steel Wire Rods
Table / clause: Printed page 22, table index 0
PDF page references: 13
Unit: Mass fraction (%)
Analysis type: The original catalogue does not explicitly identify the analysis type for this table
Manufacturer: NIPPON STEEL CORPORATION

Carbon-equivalent reference

Estimate from manufacturer-published ranges, not a standard guarantee or measured heat result; formula applicability requires review against the application and process.

IIW / CEV：0.4117–0.6867Known-element contribution; incomplete value; missing V CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.

Pcm（Ito–Bessyo）：0.2050–0.3417Known-element contribution; incomplete value; missing V, B Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.

CET：0.2325–0.3887 Envelope of independent element limits from manufacturer data; neither standard guarantee values nor measured heat results CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.

Composition

Element	Composition requirement
C	0.12 ～ 0.18
Si	0.15 ～ 0.35
Mn	0.55 ～ 0.9
P	≤ 0.03 (lower limit not stated)
S	≤ 0.03 (lower limit not stated)
Cr	0.85 ～ 1.25
Mo	0.15 ～ 0.35
Cu	≤ 0.3 (lower limit not stated)
Ni	≤ 0.25 (lower limit not stated)

Applicability and limitations

Nippon Steel wire-rod catalogue EXE203 2008.3, historical material; PDF p. 13

printed p. 22; JASO M106-92. The original catalogue does not specify the analysis type for this table. Manufacturer range data; not a standard guarantee or a heat-lot test, and does not represent our supply.

Composition conditions

Original catalogue mass percentages, historical manufacturer data from 2008.3; Referenced standard names and editions follow the original document; this does not establish that the official texts of those standards have been obtained and verified.
A dash or blank must not be treated as 0; only chemical composition has been checked in this batch. Mechanical properties and actual supply require separate verification under the applicable conditions.

Verification notes

SCM415H · CHINA STEEL CORPORATION · Bars and Wire Rods Product Catalogue 2014-C1 / 7.1.10 JIS G4052 (Edition unspecified)

Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results

Material category: Alloy steel
Subcategory: Alloy steel
Material form: Bars and wire rod
Original record status: Manufacturer source verified
Document edition: CAT.NO.3-BD-01-2014-C1 (stated on the back cover)
Document title: Bars and Wire Rods Product Catalogue
Table / clause: 7.1.10 JIS G4052 (Edition unspecified)
PDF page references: 19
Unit: Mass fraction (%)
Analysis type: The original catalogue does not explicitly identify the analysis type for this table
Manufacturer: CHINA STEEL CORPORATION

Carbon-equivalent reference

Estimate from manufacturer-published ranges, not a standard guarantee or measured heat result; formula applicability requires review against the application and process.

Composition

Element	Composition requirement
C	0.12 ～ 0.18
Si	0.15 ～ 0.35
Mn	0.55 ～ 0.95
P	≤ 0.03 (lower limit not stated)
S	≤ 0.03 (lower limit not stated)
Ni	≤ 0.25 (lower limit not stated)
Cr	0.85 ～ 1.25
Mo	0.15 ～ 0.3
Cu	≤ 0.3 (lower limit not stated)

Applicability and limitations

CSC bars and wire rods catalogue CAT.NO.3-BD-01-2014-C1, PDF page 19

printed page 17; clause 7.1.10 cites JIS G4052 (edition not stated). The original catalogue does not specify the analysis type for this table. Historical manufacturer scope data; neither standard guaranteed values nor measured heat analysis, and not evidence of supply by our company.

Composition conditions

Historical manufacturer 2014-C1 catalogue, bars/wire rod; Where the referenced standard edition is not identified, a year is not borrowed from another catalogue; a catalogue is not upgraded to the official standard text.
A dash or blank must not be treated as zero. Composition data do not establish completeness or applicability of a formula; mechanical properties and supply require separate verification.

Verification notes

Merged cells in all 28 catalogue tables were reconstructed geometrically, with no missing cells. Original images, continuation pages and notes are recorded; disputed conditions are withheld.