SAE1035
1 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for SAE1035 →SAE1035 · Q/ZNGF 01.7—2023
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Cold-heading steel
- Subcategory
- Cold-heading steel
- Material form
- Wire rod
- Original record status
- Manufacturer source verified
- Document edition
- 2023 Edition; Published 2023-09-21, implemented 2023-10-01; Supersedes Q/SG18—2022
- Document title
- Steel wire rod for cold heading and cold extrusion
- Table / clause
- Table 1
- PDF page references
- 5
- Unit
- Mass fraction (wt%)
- Manufacturer
- Guangdong Zhongnan Iron & Steel Co., Ltd.
Carbon-equivalent reference
Estimate from manufacturer-published ranges, not a standard guarantee or measured heat result; formula applicability requires review against the application and process.
Composition
| Element | Composition requirement |
|---|---|
| C | 0.32 ～ 0.38 |
| Si | 0.1 ～ 0.35 |
| Mn | 0.6 ～ 0.9 |
| P | ≤ 0.025 (lower limit not stated) |
| S | ≤ 0.025 (lower limit not stated) |
| Cr | ≤ 0.2 (lower limit not stated) |
| Ni | ≤ 0.2 (lower limit not stated) |
| Cu | ≤ 0.2 (lower limit not stated) |
Applicability and limitations
Zhongnan Steel Q/ZNGF 01.7—2023, Table 1, row 32 (PDF page 5), cast analysis wt%; footnotes, delivery process and orders must be confirmed against the corresponding edition. This does not constitute a supply commitment by Creation Group.
Composition conditions
- Table 1 heat analysis, mass fractions wt%; A dash means no limit is listed, not zero.
- Clause 6.1.4 residual impurities Cr, Ni and Cu are each ≤0.20%; Where Cr is intentionally added, the corresponding row limits apply instead of residual maxima.
- Wire rod is delivered in the hot-rolled condition; The ordinary cold-upsetting level is 1/2; high and relatively high levels must be specified in the contract.