S39274
14 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for S39274 →S39274 · ASTM A240/A240M-2014
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Original record status
- Original-standard record
- Standard edition
- ASTM A240/A240M-2014
- Table / clause
- Table 1 and footnotes A–O
- PDF page references
- 1、4、6
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Mn | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.02 (lower limit not stated) |
| Si | ≤ 0.8 (lower limit not stated) |
| Cr | 24.0 ～ 26.0 |
| Ni | 6.0 ～ 8.0 |
| Mo | 2.5 ～ 3.5 |
| N | 0.24 ～ 0.32 |
| Cu | 0.2 ～ 0.8 |
| W | 1.5 ～ 2.5 |
Applicability and limitations
Table 1: heat-analysis composition, mass fraction %. A single value without a stated range or lower bound is a maximum; unspecified elements are not assigned zero. Cb and Nb refer to the same element. Where a formula and fixed limits both apply, use the stricter limit. This is a plate, sheet and strip standard; cold-heading wire applications and actual supply require separate verification. Clause 4.1 also requires compliance with applicable provisions of ASTM A480/A480M. This record displays heat composition from Table 1; it does not establish complete verification of A480 or all product-acceptance requirements. Other elements as printed: W 1.50–2.50; see the constraints below for the specific coupled requirements.
Combined limits
- Combined-element limits
- Elements requiring measured values from the same heat
S39274 · ASTM A182/A182M-2018
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.2 ～ 0.8 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 2.5 ～ 3.5 |
| N | 0.24 ～ 0.32 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.02 (lower limit not stated) |
| Si | ≤ 0.8 (lower limit not stated) |
| W | 1.5 ～ 2.5 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S39274 · ASTM A182/A182M-2025
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.2 ～ 0.8 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 2.5 ～ 3.5 |
| N | 0.24 ～ 0.32 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.02 (lower limit not stated) |
| Si | ≤ 0.8 (lower limit not stated) |
| W | 1.5 ～ 2.5 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S39274 · ASTM A240/240M-2018
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.2 ～ 0.8 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 2.5 ～ 3.5 |
| N | 0.24 ～ 0.32 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.02 (lower limit not stated) |
| Si | ≤ 0.8 (lower limit not stated) |
| W | 1.5 ～ 2.5 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S39274 · ASTM A240/A240M-2020
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.2 ～ 0.8 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 2.5 ～ 3.5 |
| N | 0.24 ～ 0.32 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.02 (lower limit not stated) |
| Si | ≤ 0.8 (lower limit not stated) |
| W | 1.5 ～ 2.5 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S39274 · ASTM A511/A511M-2020
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.2 ～ 0.8 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 2.5 ～ 3.5 |
| N | 0.24 ～ 0.32 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.02 (lower limit not stated) |
| Si | ≤ 0.8 (lower limit not stated) |
| W | 1.5 ～ 2.5 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S39274 · ASTM A511/A511M-2025
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.2 ～ 0.8 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 2.5 ～ 3.5 |
| N | 0.24 ～ 0.32 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.02 (lower limit not stated) |
| Si | ≤ 0.8 (lower limit not stated) |
| W | 1.5 ～ 2.5 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S39274 · ASTM A789/A789M-2024
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.2 ～ 0.8 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 2.5 ～ 3.5 |
| N | 0.24 ～ 0.32 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.02 (lower limit not stated) |
| Si | ≤ 0.8 (lower limit not stated) |
| W | 1.5 ～ 2.5 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S39274 · ASTM A790/A790M-2024
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.2 ～ 0.8 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 2.5 ～ 3.5 |
| N | 0.24 ～ 0.32 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.02 (lower limit not stated) |
| Si | ≤ 0.8 (lower limit not stated) |
| W | 1.5 ～ 2.5 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S39274 · ASTM A815/A815M-2024
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.2 ～ 0.8 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 2.5 ～ 3.5 |
| N | 0.24 ～ 0.32 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.02 (lower limit not stated) |
| Si | ≤ 0.8 (lower limit not stated) |
| W | 1.5 ～ 2.5 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S39274 · ASTM A815/A815M-2026
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.2 ～ 0.8 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 2.5 ～ 3.5 |
| N | 0.24 ～ 0.32 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.02 (lower limit not stated) |
| Si | ≤ 0.8 (lower limit not stated) |
| W | 1.5 ～ 2.5 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S39274 · ASTM A959-2019
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.2 ～ 0.8 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 2.5 ～ 3.5 |
| N | 0.24 ～ 0.32 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.02 (lower limit not stated) |
| Si | ≤ 0.8 (lower limit not stated) |
| W | 1.5 ～ 2.5 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S39274 · ASTM A988/A988M-2023
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.2 ～ 0.8 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 2.5 ～ 3.5 |
| N | 0.24 ～ 0.32 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.02 (lower limit not stated) |
| Si | ≤ 0.8 (lower limit not stated) |
| W | 1.5 ～ 2.5 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S39274 · ASTM A988/A988M-2026
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.2 ～ 0.8 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 2.5 ～ 3.5 |
| N | 0.24 ～ 0.32 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.02 (lower limit not stated) |
| Si | ≤ 0.8 (lower limit not stated) |
| W | 1.5 ～ 2.5 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.