S32760
31 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for S32760 →S32760 · SAE J405-1998
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- SAE J405 JUN1998
- Table / clause
- Table 1, page 2 / page 5, notes 1–7
- PDF page references
- 1、4、5
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Mn | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Cr | 24.0 ～ 26.0 |
| Ni | 6.0 ～ 8.0 |
| Mo | 3.0 ～ 4.0 |
| N | 0.2 ～ 0.3 |
| Cu | 0.5 ～ 1.0 |
| W | 0.5 ～ 1 |
Applicability and limitations
Based on original SAE J405 JUN1998, Table 1; Mass fraction wt%, note 1: values without a stated range or minimum are maxima; a dash means unspecified and is not entered as zero. Note 5: Cb and Nb denote the same element; Alloying elements must be checked against the corresponding UNS row and additional conditions. Note 4: ordinary carbon analysis is reported to 0.01%, and low-carbon types to 0.001%; This is reporting precision and does not widen composition limits. Type names in original Table 1 may include a common name or a ASTM designation footnote; Search aliases follow only explicit correspondences on the same row; substitution across standards is not assessed automatically. 1998 is the actual composition basis; The specified newer edition has not been verified; equivalence between editions is not assumed. Cr+3.3Mo+16N≥40; Check jointly using measured composition from the same heat; independent combinations of element maxima do not establish compliance.
Combined limits
- Combined-element limits
- Requirement
- Cr+3.3Mo+16N≥40
- Element coefficient
- Cr
- 1
- Mo
- 3.3
- N
- 16
- Lower limit
- 40
Verification notes
Composition and table notes were checked using the UNS correspondence in the original 1998 text.S32760 · SAE J405-2018
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Original record status
- Historical-edition reference
- Standard edition
- SAE J405 JUN1998
- Table / clause
- Table 1, page 2 / page 5, notes 1–7
- PDF page references
- 1、4、5
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Mn | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Cr | 24.0 ～ 26.0 |
| Ni | 6.0 ～ 8.0 |
| Mo | 3.0 ～ 4.0 |
| N | 0.2 ～ 0.3 |
| Cu | 0.5 ～ 1.0 |
| W | 0.5 ～ 1 |
Applicability and limitations
Based on original SAE J405 JUN1998, Table 1; Mass fraction wt%, note 1: values without a stated range or minimum are maxima; a dash means unspecified and is not entered as zero. Note 5: Cb and Nb denote the same element; Alloying elements must be checked against the corresponding UNS row and additional conditions. Note 4: ordinary carbon analysis is reported to 0.01%, and low-carbon types to 0.001%; This is reporting precision and does not widen composition limits. Type names in original Table 1 may include a common name or a ASTM designation footnote; Search aliases follow only explicit correspondences on the same row; substitution across standards is not assessed automatically. 1998 is the actual composition basis; The specified newer edition has not been verified; equivalence between editions is not assumed. Cr+3.3Mo+16N≥40; Check jointly using measured composition from the same heat; independent combinations of element maxima do not establish compliance.
Combined limits
- Combined-element limits
- Requirement
- Cr+3.3Mo+16N≥40
- Element coefficient
- Cr
- 1
- Mo
- 3.3
- N
- 16
- Lower limit
- 40
Verification notes
The current composition is based on the 1998 original. The specified newer edition has not been checked; equivalence between editions is not assumed.S32760 · SAE J405-1998
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Stainless steel
- Subcategory
- Stainless steel
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- SAE J405 JUN1998
- Table / clause
- Table 1, page 2 / page 5, notes 1–7
- PDF page references
- 1、4、5
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Mn | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Cr | 24.0 ～ 26.0 |
| Ni | 6.0 ～ 8.0 |
| Mo | 3.0 ～ 4.0 |
| N | 0.2 ～ 0.3 |
| Cu | 0.5 ～ 1.0 |
| W | 0.5 ～ 1 |
Applicability and limitations
Based on original SAE J405 JUN1998, Table 1; Mass fraction wt%, note 1: values without a stated range or minimum are maxima; a dash means unspecified and is not entered as zero. Note 5: Cb and Nb denote the same element; Alloying elements must be checked against the corresponding UNS row and additional conditions. Note 4: ordinary carbon analysis is reported to 0.01%, and low-carbon types to 0.001%; This is reporting precision and does not widen composition limits. Type names in original Table 1 may include a common name or a ASTM designation footnote; Search aliases follow only explicit correspondences on the same row; substitution across standards is not assessed automatically. 1998 is the actual composition basis; The specified newer edition has not been verified; equivalence between editions is not assumed. Cr+3.3Mo+16N≥40; Check jointly using measured composition from the same heat; independent combinations of element maxima do not establish compliance.
Combined limits
- Combined-element limits
- Requirement
- Cr+3.3Mo+16N≥40
- Element coefficient
- Cr
- 1
- Mo
- 3.3
- N
- 16
- Lower limit
- 40
Verification notes
Corresponding UNS rows and table notes in the 1998 original have been checked; this does not verify a newer edition.S32760 · ASTM A240/A240M-2014
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Original record status
- Original-standard record
- Standard edition
- ASTM A240/A240M-2014
- Table / clause
- Table 1 and footnotes A–O
- PDF page references
- 1、4、6
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Mn | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Cr | 24.0 ～ 26.0 |
| Ni | 6.0 ～ 8.0 |
| Mo | 3.0 ～ 4.0 |
| N | 0.2 ～ 0.3 |
| Cu | 0.5 ～ 1.0 |
| W | 0.5 ～ 1 |
Applicability and limitations
Table 1: heat-analysis composition, mass fraction %. A single value without a stated range or lower bound is a maximum; unspecified elements are not assigned zero. Cb and Nb refer to the same element. Where a formula and fixed limits both apply, use the stricter limit. This is a plate, sheet and strip standard; cold-heading wire applications and actual supply require separate verification. Clause 4.1 also requires compliance with applicable provisions of ASTM A480/A480M. This record displays heat composition from Table 1; it does not establish complete verification of A480 or all product-acceptance requirements. Other elements as printed: W 0.50–1.00; see the constraints below for the specific coupled requirements.
Combined limits
- Combined-element limits
- Element coefficient
- Cr
- 1
- Mo
- 3.3
- N
- 16
- Lower limit
- 40
- Upper limit
- Not stated
- Requirement
- Cr+3.3Mo+16N≥40 (footnote K)
- Elements requiring measured values from the same heat
S32760 · ASME SA-240
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.5 ～ 1 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 3 ～ 4 |
| N | 0.2 ～ 0.3 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| W | 0.5 ～ 1 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S32760 · ASME SA-789
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.5 ～ 1 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 3 ～ 4 |
| N | 0.2 ～ 0.3 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| W | 0.5 ～ 1 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S32760 · ASTM A 314-2025
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.5 ～ 1 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 3 ～ 4 |
| N | 0.2 ～ 0.3 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| W | 0.5 ～ 1 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S32760 · ASTM A 473-2024
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.5 ～ 1 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 3 ～ 4 |
| N | 0.2 ～ 0.3 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| W | 0.5 ～ 1 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S32760 · ASTM A1082/A1082M-2016
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.5 ～ 1 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 3 ～ 4 |
| N | 0.2 ～ 0.3 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| W | 0.5 ～ 1 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S32760 · ASTM A182/A182M-2018
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.5 ～ 1 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 3 ～ 4 |
| N | 0.2 ～ 0.3 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| W | 0.5 ～ 1 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S32760 · ASTM A182/A182M-2025
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.5 ～ 1 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 3 ～ 4 |
| N | 0.2 ～ 0.3 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| W | 0.5 ～ 1 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S32760 · ASTM A240/240M-2018
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.5 ～ 1 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 3 ～ 4 |
| N | 0.2 ～ 0.3 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 0.8 (lower limit not stated) |
| W | 0.5 ～ 1 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S32760 · ASTM A240/A240M-2020
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.5 ～ 1 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 3 ～ 4 |
| N | 0.2 ～ 0.3 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 0.8 (lower limit not stated) |
| W | 0.5 ～ 1 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S32760 · ASTM A276/A276M-2017
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.5 ～ 1 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 3 ～ 4 |
| N | 0.2 ～ 0.3 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| W | 0.5 ～ 1 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S32760 · ASTM A276/A276M-2025
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.5 ～ 1 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 3 ～ 4 |
| N | 0.2 ～ 0.3 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| W | 0.5 ～ 1 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S32760 · ASTM A473-2018
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.5 ～ 1 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 3 ～ 4 |
| N | 0.2 ～ 0.3 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| W | 0.5 ～ 1 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S32760 · ASTM A473-2026
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.5 ～ 1 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 3 ～ 4 |
| N | 0.2 ～ 0.3 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| W | 0.5 ～ 1 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S32760 · ASTM A479/A479M-2018
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.5 ～ 1 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 3 ～ 4 |
| N | 0.2 ～ 0.3 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| W | 0.5 ～ 1 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S32760 · ASTM A479/A479M-2025
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.5 ～ 1 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 3 ～ 4 |
| N | 0.2 ～ 0.3 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| W | 0.5 ～ 1 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S32760 · ASTM A511/A511M-2020
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.05 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.5 ～ 1 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 3 ～ 4 |
| N | 0.2 ～ 0.3 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| W | 0.5 ～ 1 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S32760 · ASTM A511/A511M-2025
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.05 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.5 ～ 1 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 3 ～ 4 |
| N | 0.2 ～ 0.3 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| W | 0.5 ～ 1 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S32760 · ASTM A554-2016
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.5 ～ 1 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 3 ～ 4 |
| N | 0.2 ～ 0.3 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| W | 0.5 ～ 1 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S32760 · ASTM A554-2026
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.5 ～ 1 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 3 ～ 4 |
| N | 0.2 ～ 0.3 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| W | 0.5 ～ 1 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S32760 · ASTM A789/A789M-2024
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.5 ～ 1 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 3 ～ 4 |
| N | 0.2 ～ 0.3 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| W | 0.5 ～ 1 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S32760 · ASTM A790/A790M-2024
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.5 ～ 1 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 3 ～ 4 |
| N | 0.2 ～ 0.3 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| W | 0.5 ～ 1 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S32760 · ASTM A815/A815M-2024
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cu | 0.5 ～ 1 |
| Mn | ≤ 1 (lower limit not stated) |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| W | 0.5 ～ 1 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S32760 · ASTM A815/A815M-2026
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.5 ～ 1 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 3 ～ 4 |
| N | 0.2 ～ 0.3 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| W | 0.5 ～ 1 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S32760 · ASTM A959-2004
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.5 ～ 1 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 3 ～ 4 |
| N | 0.2 ～ 0.3 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| W | 0.5 ～ 1 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S32760 · ASTM A959-2019
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.5 ～ 1 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 3 ～ 4 |
| N | 0.2 ～ 0.3 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| W | 0.5 ～ 1 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S32760 · ASTM A988/A988M-2023
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.5 ～ 1 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 3 ～ 4 |
| N | 0.2 ～ 0.3 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| W | 0.5 ～ 1 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S32760 · ASTM A988/A988M-2026
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Cr | 24 ～ 26 |
| Cu | 0.5 ～ 1 |
| Mn | ≤ 1 (lower limit not stated) |
| Mo | 3 ～ 4 |
| N | 0.2 ～ 0.3 |
| Ni | 6 ～ 8 |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.01 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| W | 0.5 ～ 1 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.