5 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for S235J0 →S235J0 · EN 10025-2-2019
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Carbon steel
- Subcategory
- Carbon steel
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- EN 10025-2-2019
- Table / clause
- Table 1/5 and footnotes, 7.2, and the Clause 13 option; Only the default and Cu20 combinations
- PDF page references
- 1、12、15、21、22、23、26
Carbon-equivalent reference
Estimates are presented separately for each applicable composition condition. Match the actual ordering conditions; ranges must not be combined.
Flat products; nominal thickness ≤16 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Flat products; nominal thickness ≤16 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Flat products; nominal thickness 16<t≤30 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Flat products; nominal thickness 16<t≤30 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Flat products; nominal thickness 30<t≤40 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Flat products; nominal thickness 30<t≤40 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Flat products; nominal thickness 40<t≤100 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Flat products; nominal thickness 40<t≤100 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Flat products; nominal thickness 100<t≤150 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Flat products; nominal thickness 100<t≤150 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Flat products; nominal thickness 150<t≤250 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Flat products; nominal thickness 150<t≤250 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Flat products; nominal thickness 250<t≤400 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Flat products; nominal thickness 250<t≤400 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness ≤16 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness ≤16 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness 16<t≤30 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness 16<t≤30 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness 30<t≤40 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness 30<t≤40 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness 40<t≤100 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness 40<t≤100 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness 100<t≤150 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness 100<t≤150 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness 150<t≤250 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness 150<t≤250 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness 250<t≤400 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness 250<t≤400 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Sections; nominal thickness ≤16 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Sections; nominal thickness ≤16 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Sections; nominal thickness 16<t≤30 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Sections; nominal thickness 16<t≤30 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Sections; nominal thickness 30<t≤40 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Sections; nominal thickness 30<t≤40 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Sections; nominal thickness 40<t≤100 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Sections; nominal thickness 40<t≤100 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Composition record (conditional branches apply; this is not an unconditional requirement)
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
Applicability and limitations
EN10025-2:2019 European main text, sourced from SFS-EN10025-2:2019 official English adopted standard; Tables 1/5 and 7.2, heat analysis wt%. ; Elements not listed in the table shall refer to Table 1 of EN10020:2000 per Clause 7.2.1 as maximum values, with product table values taking priority; This reference shall not be additionally multiplied by a classification coefficient of 70%. ; Form, thickness, and Cu ordering conditions must be selected; For long products/sections, the P and S limits are .005 above the table values.. C for sections >100mm must be agreed upon by contract; no automatic application range has been generated. ; Table 1 Note e/Option 27: Increased S for long products requires agreement, sulfide shape control, and Ca≥.0020; This special selection has not yet been provided; by default, it is not automatically relaxed. ; Table 1 Note f: The N upper limit may not apply when total Al≥.020, acid-soluble Al≥.015, or other sufficient nitrogen-fixing elements are present; this must be noted in the inspection certificate; The nitrogen-fixing exception requires separate confirmation that the original conditions are met.. ; Option 20 applies only to S235/S275/S355, with heat analysis Cu .25–.40 and Table 5 CEV+.02; Product analysis Cu .20–.45 shall be verified separately and not mixed into the heat analysis range. ; Option 5 for galvanizing composition involves mutual agreement, Si/P linkage, and EN ISO14713-2:2009; it is not a default option for this instance; The CEV increase in 7.2.5 is not superimposed on the default range. ; The IIW carbon equivalent is a coupled constraint. An envelope calculated from independent element extrema may exceed the standard CEV upper limit and must not be treated as a permissible actual composition combination.. ; For hot-rolled structural steels, applicability for cold-drawn/cold-bent orders does not equal applicability for cold-heading; Mechanical properties and supply shall be verified separately. ; Other elements not listed separately in EN10020 (excluding C/P/S/N) and each lanthanide element have a maximum of .10%; the fact that elements are not exhaustively listed does not imply that arbitrary additions are permitted.
Combined limits
- Nitrogen-fixing exception conditions
- Yes
Original condition-branch records
Flat products; nominal thickness ≤16 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.35
- Requirement
- Table 5 IIW CEV≤0.35%, cast analysis; according to the selected thickness and form
Flat products; nominal thickness ≤16 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.37
- Requirement
- Table 5 IIW CEV≤0.37%, cast analysis; according to the selected thickness and form
Flat products; nominal thickness 16<t≤30 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.35
- Requirement
- Table 5 IIW CEV≤0.35%, cast analysis; according to the selected thickness and form
Flat products; nominal thickness 16<t≤30 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.37
- Requirement
- Table 5 IIW CEV≤0.37%, cast analysis; according to the selected thickness and form
Flat products; nominal thickness 30<t≤40 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.35
- Requirement
- Table 5 IIW CEV≤0.35%, cast analysis; according to the selected thickness and form
Flat products; nominal thickness 30<t≤40 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.37
- Requirement
- Table 5 IIW CEV≤0.37%, cast analysis; according to the selected thickness and form
Flat products; nominal thickness 40<t≤100 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.38
- Requirement
- Table 5 IIW CEV≤0.38%, cast analysis; according to the selected thickness and form
Flat products; nominal thickness 40<t≤100 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.4
- Requirement
- Table 5 IIW CEV≤0.40%, cast analysis; according to the selected thickness and form
Flat products; nominal thickness 100<t≤150 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.38
- Requirement
- Table 5 IIW CEV≤0.38%, cast analysis; according to the selected thickness and form
Flat products; nominal thickness 100<t≤150 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.4
- Requirement
- Table 5 IIW CEV≤0.40%, cast analysis; according to the selected thickness and form
Flat products; nominal thickness 150<t≤250 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.4
- Requirement
- Table 5 IIW CEV≤0.40%, cast analysis; according to the selected thickness and form
Flat products; nominal thickness 150<t≤250 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.42
- Requirement
- Table 5 IIW CEV≤0.42%, cast analysis; according to the selected thickness and form
Flat products; nominal thickness 250<t≤400 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.4
- Requirement
- Table 5 IIW CEV≤0.40%, cast analysis; according to the selected thickness and form
Flat products; nominal thickness 250<t≤400 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.42
- Requirement
- Table 5 IIW CEV≤0.42%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness ≤16 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.35
- Requirement
- Table 5 IIW CEV≤0.35%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness ≤16 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.37
- Requirement
- Table 5 IIW CEV≤0.37%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness 16<t≤30 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.35
- Requirement
- Table 5 IIW CEV≤0.35%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness 16<t≤30 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.37
- Requirement
- Table 5 IIW CEV≤0.37%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness 30<t≤40 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.35
- Requirement
- Table 5 IIW CEV≤0.35%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness 30<t≤40 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.37
- Requirement
- Table 5 IIW CEV≤0.37%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness 40<t≤100 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.38
- Requirement
- Table 5 IIW CEV≤0.38%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness 40<t≤100 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.4
- Requirement
- Table 5 IIW CEV≤0.40%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness 100<t≤150 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.38
- Requirement
- Table 5 IIW CEV≤0.38%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness 100<t≤150 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.4
- Requirement
- Table 5 IIW CEV≤0.40%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness 150<t≤250 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.4
- Requirement
- Table 5 IIW CEV≤0.40%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness 150<t≤250 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.42
- Requirement
- Table 5 IIW CEV≤0.42%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness 250<t≤400 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.4
- Requirement
- Table 5 IIW CEV≤0.40%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness 250<t≤400 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.42
- Requirement
- Table 5 IIW CEV≤0.42%, cast analysis; according to the selected thickness and form
Sections; nominal thickness ≤16 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.35
- Requirement
- Table 5 IIW CEV≤0.35%, cast analysis; according to the selected thickness and form
Sections; nominal thickness ≤16 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.37
- Requirement
- Table 5 IIW CEV≤0.37%, cast analysis; according to the selected thickness and form
Sections; nominal thickness 16<t≤30 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.35
- Requirement
- Table 5 IIW CEV≤0.35%, cast analysis; according to the selected thickness and form
Sections; nominal thickness 16<t≤30 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.37
- Requirement
- Table 5 IIW CEV≤0.37%, cast analysis; according to the selected thickness and form
Sections; nominal thickness 30<t≤40 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.35
- Requirement
- Table 5 IIW CEV≤0.35%, cast analysis; according to the selected thickness and form
Sections; nominal thickness 30<t≤40 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.37
- Requirement
- Table 5 IIW CEV≤0.37%, cast analysis; according to the selected thickness and form
Sections; nominal thickness 40<t≤100 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.38
- Requirement
- Table 5 IIW CEV≤0.38%, cast analysis; according to the selected thickness and form
Sections; nominal thickness 40<t≤100 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.4
- Requirement
- Table 5 IIW CEV≤0.40%, cast analysis; according to the selected thickness and form
A condition branch must be selected
YesVerification notes
Official main-text Table 1/5, applicable footnotes and referenced EN10020, Table 1 were visually checked; Special galvanizing or free-cutting conditions require separate verificationS235J0 · EN 10025-2-2019
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- EN 10025-2-2019
- Table / clause
- Table 1/5 and footnotes, 7.2, and the Clause 13 option; Only the default and Cu20 combinations
- PDF page references
- 1、12、15、21、22、23、26
Carbon-equivalent reference
Estimates are presented separately for each applicable composition condition. Match the actual ordering conditions; ranges must not be combined.
Flat products; nominal thickness ≤16 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Flat products; nominal thickness ≤16 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Flat products; nominal thickness 16<t≤30 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Flat products; nominal thickness 16<t≤30 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Flat products; nominal thickness 30<t≤40 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Flat products; nominal thickness 30<t≤40 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Flat products; nominal thickness 40<t≤100 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Flat products; nominal thickness 40<t≤100 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Flat products; nominal thickness 100<t≤150 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Flat products; nominal thickness 100<t≤150 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Flat products; nominal thickness 150<t≤250 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Flat products; nominal thickness 150<t≤250 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Flat products; nominal thickness 250<t≤400 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Flat products; nominal thickness 250<t≤400 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness ≤16 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness ≤16 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness 16<t≤30 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness 16<t≤30 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness 30<t≤40 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness 30<t≤40 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness 40<t≤100 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness 40<t≤100 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness 100<t≤150 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness 100<t≤150 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness 150<t≤250 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness 150<t≤250 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness 250<t≤400 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Long products (excluding sections); nominal thickness 250<t≤400 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Sections; nominal thickness ≤16 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Sections; nominal thickness ≤16 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Sections; nominal thickness 16<t≤30 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Sections; nominal thickness 16<t≤30 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Sections; nominal thickness 30<t≤40 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Sections; nominal thickness 30<t≤40 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Sections; nominal thickness 40<t≤100 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
IIW / CEV：0.0000–0.5680 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0000–0.3303 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0000–0.3735 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Sections; nominal thickness 40<t≤100 mm; Option 20: agreed Cu .25–.40%
IIW / CEV：0.0167–0.5580 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.
Pcm（Ito–Bessyo）：0.0125–0.3228 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.
CET：0.0125–0.3660 Independent-element envelope of standard ranges, not measured heat results; coupled-element constraints require separate checks, and the entire envelope is not guaranteed to be realizable CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.
Composition record (conditional branches apply; this is not an unconditional requirement)
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
Applicability and limitations
EN10025-2:2019 European main text, sourced from SFS-EN10025-2:2019 official English adopted standard; Tables 1/5 and 7.2, heat analysis wt%. ; Elements not listed in the table shall refer to Table 1 of EN10020:2000 per Clause 7.2.1 as maximum values, with product table values taking priority; This reference shall not be additionally multiplied by a classification coefficient of 70%. ; Form, thickness, and Cu ordering conditions must be selected; For long products/sections, the P and S limits are .005 above the table values.. C for sections >100mm must be agreed upon by contract; no automatic application range has been generated. ; Table 1 Note e/Option 27: Increased S for long products requires agreement, sulfide shape control, and Ca≥.0020; This special selection has not yet been provided; by default, it is not automatically relaxed. ; Table 1 Note f: The N upper limit may not apply when total Al≥.020, acid-soluble Al≥.015, or other sufficient nitrogen-fixing elements are present; this must be noted in the inspection certificate; The nitrogen-fixing exception requires separate confirmation that the original conditions are met.. ; Option 20 applies only to S235/S275/S355, with heat analysis Cu .25–.40 and Table 5 CEV+.02; Product analysis Cu .20–.45 shall be verified separately and not mixed into the heat analysis range. ; Option 5 for galvanizing composition involves mutual agreement, Si/P linkage, and EN ISO14713-2:2009; it is not a default option for this instance; The CEV increase in 7.2.5 is not superimposed on the default range. ; The IIW carbon equivalent is a coupled constraint. An envelope calculated from independent element extrema may exceed the standard CEV upper limit and must not be treated as a permissible actual composition combination.. ; For hot-rolled structural steels, applicability for cold-drawn/cold-bent orders does not equal applicability for cold-heading; Mechanical properties and supply shall be verified separately. ; Other elements not listed separately in EN10020 (excluding C/P/S/N) and each lanthanide element have a maximum of .10%; the fact that elements are not exhaustively listed does not imply that arbitrary additions are permitted.
Combined limits
- Nitrogen-fixing exception conditions
- Yes
Original condition-branch records
Flat products; nominal thickness ≤16 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.35
- Requirement
- Table 5 IIW CEV≤0.35%, cast analysis; according to the selected thickness and form
Flat products; nominal thickness ≤16 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.37
- Requirement
- Table 5 IIW CEV≤0.37%, cast analysis; according to the selected thickness and form
Flat products; nominal thickness 16<t≤30 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.35
- Requirement
- Table 5 IIW CEV≤0.35%, cast analysis; according to the selected thickness and form
Flat products; nominal thickness 16<t≤30 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.37
- Requirement
- Table 5 IIW CEV≤0.37%, cast analysis; according to the selected thickness and form
Flat products; nominal thickness 30<t≤40 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.35
- Requirement
- Table 5 IIW CEV≤0.35%, cast analysis; according to the selected thickness and form
Flat products; nominal thickness 30<t≤40 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.37
- Requirement
- Table 5 IIW CEV≤0.37%, cast analysis; according to the selected thickness and form
Flat products; nominal thickness 40<t≤100 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.38
- Requirement
- Table 5 IIW CEV≤0.38%, cast analysis; according to the selected thickness and form
Flat products; nominal thickness 40<t≤100 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.4
- Requirement
- Table 5 IIW CEV≤0.40%, cast analysis; according to the selected thickness and form
Flat products; nominal thickness 100<t≤150 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.38
- Requirement
- Table 5 IIW CEV≤0.38%, cast analysis; according to the selected thickness and form
Flat products; nominal thickness 100<t≤150 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.4
- Requirement
- Table 5 IIW CEV≤0.40%, cast analysis; according to the selected thickness and form
Flat products; nominal thickness 150<t≤250 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.4
- Requirement
- Table 5 IIW CEV≤0.40%, cast analysis; according to the selected thickness and form
Flat products; nominal thickness 150<t≤250 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.42
- Requirement
- Table 5 IIW CEV≤0.42%, cast analysis; according to the selected thickness and form
Flat products; nominal thickness 250<t≤400 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.4
- Requirement
- Table 5 IIW CEV≤0.40%, cast analysis; according to the selected thickness and form
Flat products; nominal thickness 250<t≤400 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.42
- Requirement
- Table 5 IIW CEV≤0.42%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness ≤16 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.35
- Requirement
- Table 5 IIW CEV≤0.35%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness ≤16 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.37
- Requirement
- Table 5 IIW CEV≤0.37%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness 16<t≤30 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.35
- Requirement
- Table 5 IIW CEV≤0.35%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness 16<t≤30 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.37
- Requirement
- Table 5 IIW CEV≤0.37%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness 30<t≤40 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.35
- Requirement
- Table 5 IIW CEV≤0.35%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness 30<t≤40 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.37
- Requirement
- Table 5 IIW CEV≤0.37%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness 40<t≤100 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.38
- Requirement
- Table 5 IIW CEV≤0.38%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness 40<t≤100 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.4
- Requirement
- Table 5 IIW CEV≤0.40%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness 100<t≤150 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.38
- Requirement
- Table 5 IIW CEV≤0.38%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness 100<t≤150 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.4
- Requirement
- Table 5 IIW CEV≤0.40%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness 150<t≤250 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.4
- Requirement
- Table 5 IIW CEV≤0.40%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness 150<t≤250 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.42
- Requirement
- Table 5 IIW CEV≤0.42%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness 250<t≤400 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.4
- Requirement
- Table 5 IIW CEV≤0.40%, cast analysis; according to the selected thickness and form
Long products (excluding sections); nominal thickness 250<t≤400 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.42
- Requirement
- Table 5 IIW CEV≤0.42%, cast analysis; according to the selected thickness and form
Sections; nominal thickness ≤16 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.35
- Requirement
- Table 5 IIW CEV≤0.35%, cast analysis; according to the selected thickness and form
Sections; nominal thickness ≤16 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.37
- Requirement
- Table 5 IIW CEV≤0.37%, cast analysis; according to the selected thickness and form
Sections; nominal thickness 16<t≤30 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.35
- Requirement
- Table 5 IIW CEV≤0.35%, cast analysis; according to the selected thickness and form
Sections; nominal thickness 16<t≤30 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.37
- Requirement
- Table 5 IIW CEV≤0.37%, cast analysis; according to the selected thickness and form
Sections; nominal thickness 30<t≤40 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.35
- Requirement
- Table 5 IIW CEV≤0.35%, cast analysis; according to the selected thickness and form
Sections; nominal thickness 30<t≤40 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.37
- Requirement
- Table 5 IIW CEV≤0.37%, cast analysis; according to the selected thickness and form
Sections; nominal thickness 40<t≤100 mm; Ordinary Cu requirement; no special galvanizing or free-cutting option selected
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.38
- Requirement
- Table 5 IIW CEV≤0.38%, cast analysis; according to the selected thickness and form
Sections; nominal thickness 40<t≤100 mm; Option 20: agreed Cu .25–.40%
| Element | Composition requirement |
|---|---|
| Al | ≤ 0.3 (lower limit not stated) |
| B | ≤ 0.0008 (lower limit not stated) |
| Bi | ≤ 0.1 (lower limit not stated) |
| Co | ≤ 0.3 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | 0.25 ～ 0.4 |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| Nb | ≤ 0.06 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| Pb | ≤ 0.4 (lower limit not stated) |
| Se | ≤ 0.1 (lower limit not stated) |
| Si | ≤ 0.6 (lower limit not stated) |
| Te | ≤ 0.1 (lower limit not stated) |
| Ti | ≤ 0.05 (lower limit not stated) |
| V | ≤ 0.1 (lower limit not stated) |
| W | ≤ 0.3 (lower limit not stated) |
| Zr | ≤ 0.05 (lower limit not stated) |
| O | ≤ 0.1 (lower limit not stated) |
| Sn | ≤ 0.1 (lower limit not stated) |
| As | ≤ 0.1 (lower limit not stated) |
| Sb | ≤ 0.1 (lower limit not stated) |
| Mg | ≤ 0.1 (lower limit not stated) |
| Zn | ≤ 0.1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| C | ≤ 0.17 (lower limit not stated) |
- Combined limits
- Combined-element limits
- Element coefficient
- C
- 1
- Mn
- 0.16666666666666666
- Cr
- 0.2
- Mo
- 0.2
- V
- 0.2
- Ni
- 0.06666666666666667
- Cu
- 0.06666666666666667
- Upper limit
- 0.4
- Requirement
- Table 5 IIW CEV≤0.40%, cast analysis; according to the selected thickness and form
A condition branch must be selected
YesVerification notes
Official main-text Table 1/5, applicable footnotes and referenced EN10020, Table 1 were visually checked; Special galvanizing or free-cutting conditions require separate verificationS235J0 · DIN EN 10025-2-2019
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Carbon steel
- Subcategory
- Carbon steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
IIW / CEV: composition source not verified; standard-range carbon equivalent is not calculated
Pcm (Ito–Bessyo): composition source not verified; standard-range carbon equivalent is not calculated
CET: composition source not verified; standard-range carbon equivalent is not calculated
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.17 (lower limit not stated) |
| Cr | ≤ 0.29 (lower limit not stated) |
| Cu | ≤ 0.55 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| Mo | ≤ 0.11 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| Ni | ≤ 0.42 (lower limit not stated) |
| P | ≤ 0.03 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S235J0 · NF EN 10025-2-2005
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Carbon steel
- Subcategory
- Carbon steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
IIW / CEV: composition source not verified; standard-range carbon equivalent is not calculated
Pcm (Ito–Bessyo): composition source not verified; standard-range carbon equivalent is not calculated
CET: composition source not verified; standard-range carbon equivalent is not calculated
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.17 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
S235J0 · Q/BQB 303-2018
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Carbon steel
- Subcategory
- Carbon steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
IIW / CEV: composition source not verified; standard-range carbon equivalent is not calculated
Pcm (Ito–Bessyo): composition source not verified; standard-range carbon equivalent is not calculated
CET: composition source not verified; standard-range carbon equivalent is not calculated
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.17 (lower limit not stated) |
| Mn | ≤ 1.4 (lower limit not stated) |
| N | ≤ 0.012 (lower limit not stated) |
| P | ≤ 0.025 (lower limit not stated) |
| S | ≤ 0.02 (lower limit not stated) |
| Si | ≤ 0.35 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.