NICR20TI
2 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for NICR20TI →NiCr20Ti · DIN EN 10095-2018
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Nickel and nickel alloys
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- DIN EN 10095:2018-12
- Table / clause
- Table 3,footnotes 1/2;7.2
- PDF page references
- 1、2、3、9、17
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | 0.08 ～ 0.15 |
| Mn | ≤ 1.0 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.02 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Cr | 18.0 ～ 21.0 |
| Co | ≤ 5.0 (lower limit not stated) |
| Fe | ≤ 5.0 (lower limit not stated) |
| Al | ≤ 0.3 (lower limit not stated) |
| Ti | 0.2 ～ 0.6 |
| Cu | ≤ 0.5 (lower limit not stated) |
Applicability and limitations
DIN EN 10095:2018-12 is the German-language edition of EN 10095:1999 and includes the corrigenda listed in the national foreword; The national publication edition and adopted EN year are retained. Table 1–3 gives heat-analysis mass fractions wt%; 7.2.2 product-analysis tolerances are in Table 4/5 separately and must not be added to this heat-analysis range. Footnote 1: unlisted elements must not be intentionally added without purchaser consent, except for deoxidation; Unspecified content does not mean zero. Applicable to technical conditions for heat-resistant steels; this does not establish cold-heading suitability or product supply. Ni is the balance; A guaranteed numerical range is not inferred.
Combined limits
- Combined-element limits
- Elements requiring measured values from the same heat
Verification notes
All 26 chemical-composition rows and applicable footnotes in the official German text dated 2018-12 were checked; the 2018 corrigendum and product-analysis deviations are recorded separately.NiCr20Ti · EN 10095-1999
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Nickel and nickel alloys
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- EN 10095:1999
- Table / clause
- Table 3 and footnotes; complete historical original edition
- PDF page references
- 1、16
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | 0.08 ～ 0.15 |
| Mn | ≤ 1.0 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| P | ≤ 0.02 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Cr | 18.0 ～ 21.0 |
| Co | ≤ 5.0 (lower limit not stated) |
| Fe | ≤ 5.0 (lower limit not stated) |
| Al | ≤ 0.3 (lower limit not stated) |
| Ti | 0.2 ～ 0.6 |
| Cu | ≤ 0.5 (lower limit not stated) |
Applicability and limitations
Original historical EN 10095:1999, Table 1—3 gives heat-analysis mass fractions wt%; This source is a scan of that original edition and must not be identified as DIN EN 10095:2018-12. ; Unlisted elements are not treated as zero and must not be intentionally added without purchaser consent, except additions needed to finish steelmaking. ; Specific supply form, heat treatment, properties and cold-heading suitability require separate verification against the product standard, contract and material certificate. ; Table 3, note 2 permits Co≤1.5% to be included in Ni; The existing coupled Ni+Co constraint is retained and is not split into an independent Ni interval.
Combined limits
- Combined-element limits
- Elements requiring measured values from the same heat