NICR19FE19NB5MO 3
2 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for NICR19FE19NB5MO 3 →NiCr19Fe19Nb5Mo 3 · DIN EN 10269-2014
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Stainless steel
- Subcategory
- Nickel and nickel alloys
- Material form
- Reference record
- Original record status
- Composition basis in the adopted standard verified
- Standard edition
- EN 10269-2013
- Table / clause
- Table1 final page: nickel alloys and combined niobium-tantalum requirements
- PDF page references
- 19
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | 0.02 ～ 0.08 |
| Si | ≤ 0.035 (lower limit not stated) |
| Mn | ≤ 0.035 (lower limit not stated) |
| P | ≤ 0.015 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Al | 0.3 ～ 0.7 |
| B | 0.002 ～ 0.006 |
| Cr | 17.0 ～ 21.0 |
| Mo | 2.8 ～ 3.3 |
| Ni | 50.0 ～ 55.0 |
| Cu | ≤ 0.3 (lower limit not stated) |
| Co | ≤ 1.0 (lower limit not stated) |
| Nb | 4.7 ～ 5.5 |
| Ti | 0.6 ～ 1.2 |
Applicability and limitations
DIN EN 10269:2014-02 is the German-language edition of EN 10269:2013; Current composition is taken from the original EN table and must be verified according to application and delivery condition. Table 1 (final table page, PDF19) in the official BS English-language adoption of EN10269:2013; heat-analysis mass fractions wt%. ; Nb+Ta is a combined constraint; when individual Nb/Ta ranges are not specified, they shall not be split into independent standard limits; Reverse lookup requires the input of all relevant elements. ; Ni≥65 or Ni≥70 are lower limits only, with no independent standard upper limit; Do not automatically fill in a range. ; For NiCr19Fe19Nb5Mo3, Si/Mn are each ≤.035% in the original table and are retained as per the original text; Fe is the balance; no independent numerical range is provided. ; Unlisted elements are not entered as zero; Properties, heat treatment, product analysis, and cold heading supply suitability shall be verified separately.
Verification notes
The official adoption relationship for DIN and original same-designation EN 10269:2013, Table 1 have been checked; The complete German text has not been checked page by pageNiCr19Fe19Nb5Mo 3 · EN 10269-2013
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Stainless steel
- Subcategory
- Nickel and nickel alloys
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- EN 10269-2013
- Table / clause
- Table1 final page: nickel alloys and combined niobium-tantalum requirements
- PDF page references
- 19
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | 0.02 ～ 0.08 |
| Si | ≤ 0.035 (lower limit not stated) |
| Mn | ≤ 0.035 (lower limit not stated) |
| P | ≤ 0.015 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Al | 0.3 ～ 0.7 |
| B | 0.002 ～ 0.006 |
| Cr | 17.0 ～ 21.0 |
| Mo | 2.8 ～ 3.3 |
| Ni | 50.0 ～ 55.0 |
| Cu | ≤ 0.3 (lower limit not stated) |
| Co | ≤ 1.0 (lower limit not stated) |
| Nb | 4.7 ～ 5.5 |
| Ti | 0.6 ～ 1.2 |
Applicability and limitations
Table 1 (final table page, PDF19) in the official BS English-language adoption of EN10269:2013; heat-analysis mass fractions wt%. ; Nb+Ta is a combined constraint; when individual Nb/Ta ranges are not specified, they shall not be split into independent standard limits; Reverse lookup requires the input of all relevant elements. ; Ni≥65 or Ni≥70 are lower limits only, with no independent standard upper limit; Do not automatically fill in a range. ; For NiCr19Fe19Nb5Mo3, Si/Mn are each ≤.035% in the original table and are retained as per the original text; Fe is the balance; no independent numerical range is provided. ; Unlisted elements are not entered as zero; Properties, heat treatment, product analysis, and cold heading supply suitability shall be verified separately.