N08811
22 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for N08811 →N08811 · ASTM A312/A312M-2025
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Original record status
- Original text of the historical edition verified
- Standard edition
- ASTM A312/A312M-2017
- Table / clause
- Table 1, footnotes A–M and clause 7.1
- PDF page references
- 1、2、6
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | 0.06 ～ 0.1 |
| Mn | ≤ 1.5 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Cr | 19.0 ～ 23.0 |
| Ni | 30.0 ～ 35.0 |
| Ti | 0.15 ～ 0.6 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Al | 0.15 ～ 0.6 |
| Fe | ≥ 39.5 (upper limit not stated) |
Applicability and limitations
Table 1, mass percent; A single value is a maximum; ellipses mean unspecified and are not entered as zero. ; Clause 7.1 requires compliance with Table 1; The general A999/A999M requirements in Clause 5.1 still apply; only the chemical-composition table was checked in this batch. ; Austenitic steel pipe standard; This does not directly establish cold-heading wire suitability or compliance with all product acceptance requirements. ; Footnote C: the nitrogen-analysis method is agreed between purchaser and supplier. ; Footnote J: Fe is calculated as 100 minus the sum of other specified elements and must be at least 39.5%. ; Footnote K: Al and Ti are each 0.15–0.60%, with combined 0.85–1.20% also required; The range giving each A240—2014 as 0.25–0.60% must not be applied.
Combined limits
- Combined-element limits
- Requirement
- Sum of other specified elements ≤60.50%
- Element coefficient
- C
- 1
- Mn
- 1
- P
- 1
- S
- 1
- Si
- 1
- Cr
- 1
- Ni
- 1
- Ti
- 1
- Cu
- 1
- Al
- 1
- Upper limit
- 60.5
- Requirement
- Fe=100 minus the sum of other specified elements
- Element coefficient
- C
- 1
- Mn
- 1
- P
- 1
- S
- 1
- Si
- 1
- Cr
- 1
- Ni
- 1
- Ti
- 1
- Cu
- 1
- Al
- 1
- Fe
- 1
- Lower limit
- 100
- Upper limit
- 100
- Requirement
- Al+Ti=0.85–1.20%
- Element coefficient
- Al
- 1
- Ti
- 1
- Lower limit
- 0.85
- Upper limit
- 1.2
Verification notes
Original edition 2017, Table 1 and footnotes are used; Edition 2025 has not been verified; identical composition across the two editions is not claimed.N08811 · ASTM A240/A240M-2014
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Nickel and nickel alloys
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Original record status
- Original-standard record
- Standard edition
- ASTM A240/A240M-2014
- Table / clause
- Table 1 and footnotes A–O
- PDF page references
- 1、2、6
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | 0.06 ～ 0.1 |
| Mn | ≤ 1.5 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Cr | 19.0 ～ 23.0 |
| Ni | 30.0 ～ 35.0 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Fe | ≥ 39.5 (upper limit not stated) |
| Al | 0.25 ～ 0.6 |
| Ti | 0.25 ～ 0.6 |
Applicability and limitations
Table 1 gives heat-analysis mass percentages; A single value without a stated range or minimum is a maximum; unspecified elements are not entered as zero. ; Cb and Nb are the same element; Where both a formula and a fixed limit apply, the stricter limit is used. ; This is a plate, sheet and strip standard; cold-heading wire applications and actual supply require separate verification. ; Clause 4.1 also requires compliance with the applicable provisions of ASTM A480/A480M; This record displays the heat composition in Table 1; it does not establish verification of A480 or all product acceptance requirements. ; Other elements in the original table: FeH 39.5 min TiI 0.25–0.60 AlI 0.25–0.60; See the limits below for the specific coupled requirements. ; Footnote H: Fe is calculated as 100 minus the sum of other specified elements; Fe and the other elements must not be treated as unrelated ranges. ; Footnote I: Al+Ti is 0.85–1.20%.
Combined limits
- Combined-element limits
- Element coefficient
- Al
- 1
- Ti
- 1
- Lower limit
- 0.85
- Upper limit
- 1.2
- Requirement
- Al+Ti 0.85–1.20
- Requirement
- Sum of other specified elements ≤60.50%; Fe is calculated by difference and is ≥39.50%
- Element coefficient
- C
- 1
- Mn
- 1
- P
- 1
- S
- 1
- Si
- 1
- Cr
- 1
- Ni
- 1
- Cu
- 1
- Al
- 1
- Ti
- 1
- Upper limit
- 60.5
- Requirement
- Fe is calculated as 100 minus the sum of other specified elements
- Element coefficient
- C
- 1
- Mn
- 1
- P
- 1
- S
- 1
- Si
- 1
- Cr
- 1
- Ni
- 1
- Cu
- 1
- Fe
- 1
- Al
- 1
- Ti
- 1
- Lower limit
- 100
- Upper limit
- 100
- Elements requiring measured values from the same heat
- Basis for Fe balance
- Footnote H: Fe is calculated as 100 minus the sum of the other specified elements; Do not use directly as an envelope of independent element limits.
N08811 · ASTM A312/A312M-2017
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Nickel and nickel alloys
- Subcategory
- Nickel and nickel alloys
- Material form
- Reference record
- Original record status
- Original-standard record
- Standard edition
- ASTM A312/A312M-2017
- Table / clause
- Table 1, footnotes A–M and clause 7.1
- PDF page references
- 1、2、6
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | 0.06 ～ 0.1 |
| Mn | ≤ 1.5 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Cr | 19.0 ～ 23.0 |
| Ni | 30.0 ～ 35.0 |
| Ti | 0.15 ～ 0.6 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Al | 0.15 ～ 0.6 |
| Fe | ≥ 39.5 (upper limit not stated) |
Applicability and limitations
Table 1, mass percent; A single value is a maximum; ellipses mean unspecified and are not entered as zero. ; Clause 7.1 requires compliance with Table 1; The general A999/A999M requirements in Clause 5.1 still apply; only the chemical-composition table was checked in this batch. ; Austenitic steel pipe standard; This does not directly establish cold-heading wire suitability or compliance with all product acceptance requirements. ; Footnote C: the nitrogen-analysis method is agreed between purchaser and supplier. ; Footnote J: Fe is calculated as 100 minus the sum of other specified elements and must be at least 39.5%. ; Footnote K: Al and Ti are each 0.15–0.60%, with combined 0.85–1.20% also required; The range giving each A240—2014 as 0.25–0.60% must not be applied.
Combined limits
- Combined-element limits
- Requirement
- Sum of other specified elements ≤60.50%
- Element coefficient
- C
- 1
- Mn
- 1
- P
- 1
- S
- 1
- Si
- 1
- Cr
- 1
- Ni
- 1
- Ti
- 1
- Cu
- 1
- Al
- 1
- Upper limit
- 60.5
- Requirement
- Fe=100 minus the sum of other specified elements
- Element coefficient
- C
- 1
- Mn
- 1
- P
- 1
- S
- 1
- Si
- 1
- Cr
- 1
- Ni
- 1
- Ti
- 1
- Cu
- 1
- Al
- 1
- Fe
- 1
- Lower limit
- 100
- Upper limit
- 100
- Requirement
- Al+Ti=0.85–1.20%
- Element coefficient
- Al
- 1
- Ti
- 1
- Lower limit
- 0.85
- Upper limit
- 1.2
N08811 · ASTM A 314-2025
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.25 ～ 0.6 |
| C | 0.06 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Fe | ≥ 39.5 (upper limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.25 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
N08811 · ASTM A182/A182M-2025
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.25 ～ 0.6 |
| C | 0.06 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Fe | ≥ 39.5 (upper limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.25 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
N08811 · ASTM A213/A213M-2019
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.15 ～ 0.6 |
| C | 0.06 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.15 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
N08811 · ASTM A213/A213M-2025
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.15 ～ 0.6 |
| C | 0.06 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.15 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
N08811 · ASTM A240/240M-2018
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.25 ～ 0.6 |
| C | 0.06 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Fe | ≥ 39.5 (upper limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.25 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
N08811 · ASTM A240/A240M-2020
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.25 ～ 0.6 |
| C | 0.06 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Fe | ≥ 39.5 (upper limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.25 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
N08811 · ASTM A249/A249M-2018
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.25 ～ 0.6 |
| C | 0.05 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Fe | ≥ 39.5 (upper limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.25 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
N08811 · ASTM A249/A249M-2024
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.25 ～ 0.6 |
| C | 0.05 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.25 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
N08811 · ASTM A276/A276M-2017
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.25 ～ 0.6 |
| C | 0.06 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Fe | ≥ 39.5 (upper limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.25 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
N08811 · ASTM A276/A276M-2025
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.25 ～ 0.6 |
| C | 0.06 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.25 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
N08811 · ASTM A479/A479M-2018
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.25 ～ 0.6 |
| C | 0.06 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.25 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
N08811 · ASTM A479/A479M-2025
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.25 ～ 0.6 |
| C | 0.06 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.25 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
N08811 · ASTM A511/A511M-2020
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.25 ～ 0.6 |
| C | 0.06 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.25 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
N08811 · ASTM A511/A511M-2025
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.25 ～ 0.6 |
| C | 0.06 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Fe | ≥ 39.5 (upper limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.25 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
N08811 · ASTM A688/A688M-2018
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.25 ～ 0.6 |
| C | 0.06 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.25 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
N08811 · ASTM A688/A688M-2024
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.25 ～ 0.6 |
| C | 0.06 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.25 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
N08811 · ASTM A959-2019
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.25 ～ 0.6 |
| C | 0.06 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Fe | ≥ 39.5 (upper limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.25 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
N08811 · ASTM B 408-2022
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Alloy steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.25 ～ 0.6 |
| C | 0.06 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.25 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
N08811 · ASTM B 564-2025
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Nickel and nickel alloys
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.15 ～ 0.6 |
| C | 0.06 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Fe | ≥ 39.5 (upper limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.15 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.