N08810
14 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for N08810 →N08810 · SAE J405-2018
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Original record status
- Historical-edition reference
- Standard edition
- SAE J405 JUN1998
- Table / clause
- Table 1, page 2 / page 5, notes 1–7
- PDF page references
- 1、2、5
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | 0.05 ～ 0.1 |
| Mn | ≤ 1.5 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Cr | 19.0 ～ 23.0 |
| Ni | 30.0 ～ 35.0 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Al | 0.15 ～ 0.6 |
| Ti | 0.15 ～ 0.6 |
Applicability and limitations
Based on SAE J405 JUN1998 original Table 1; mass fraction wt%. Note 1: a value without a range or lower limit is a maximum; a dash means unspecified, not zero. Note 5: Cb and Nb denote the same element; verify alloying elements against the corresponding UNS row and additional conditions. Note 4: carbon is generally reported to 0.01%, and low-carbon types to 0.001%; this is reporting precision and does not relax composition limits. Original Table 1 type names may include common names or ASTM-naming footnotes; create search aliases only for explicit same-row correspondences, without implying cross-standard equivalence. 1998 is the actual composition basis; the specified newer edition has not been checked, so consistency between editions is not assumed.
Verification notes
The current composition is based on the 1998 original. The specified newer edition has not been checked; equivalence between editions is not assumed.N08810 · SAE J405-1998
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Stainless steel
- Subcategory
- Stainless steel
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- SAE J405 JUN1998
- Table / clause
- Table 1, page 2 / page 5, notes 1–7
- PDF page references
- 1、2、5
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | 0.05 ～ 0.1 |
| Mn | ≤ 1.5 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Cr | 19.0 ～ 23.0 |
| Ni | 30.0 ～ 35.0 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Al | 0.15 ～ 0.6 |
| Ti | 0.15 ～ 0.6 |
Applicability and limitations
Based on SAE J405 JUN1998 original Table 1; mass fraction wt%. Note 1: a value without a range or lower limit is a maximum; a dash means unspecified, not zero. Note 5: Cb and Nb denote the same element; verify alloying elements against the corresponding UNS row and additional conditions. Note 4: carbon is generally reported to 0.01%, and low-carbon types to 0.001%; this is reporting precision and does not relax composition limits. Original Table 1 type names may include common names or ASTM-naming footnotes; create search aliases only for explicit same-row correspondences, without implying cross-standard equivalence. 1998 is the actual composition basis; the specified newer edition has not been checked, so consistency between editions is not assumed.
Verification notes
Corresponding UNS rows and table notes in the 1998 original have been checked; this does not verify a newer edition.N08810 · ASTM A240/A240M-2014
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Nickel and nickel alloys
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Original record status
- Original-standard record
- Standard edition
- ASTM A240/A240M-2014
- Table / clause
- Table 1 and footnotes A–O
- PDF page references
- 1、2、6
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | 0.05 ～ 0.1 |
| Mn | ≤ 1.5 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Cr | 19.0 ～ 23.0 |
| Ni | 30.0 ～ 35.0 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Fe | ≥ 39.5 (upper limit not stated) |
| Al | 0.15 ～ 0.6 |
| Ti | 0.15 ～ 0.6 |
Applicability and limitations
Table 1 gives heat-analysis mass percentages; A single value without a stated range or minimum is a maximum; unspecified elements are not entered as zero. ; Cb and Nb are the same element; Where both a formula and a fixed limit apply, the stricter limit is used. ; This is a plate, sheet and strip standard; cold-heading wire applications and actual supply require separate verification. ; Clause 4.1 also requires compliance with the applicable provisions of ASTM A480/A480M; This record displays the heat composition in Table 1; it does not establish verification of A480 or all product acceptance requirements. ; Other elements in the original table: FeH 39.5 min Al 0.15–0.60 Ti 0.15–0.60; See the limits below for the specific coupled requirements. ; Footnote H: Fe is calculated as 100 minus the sum of other specified elements; Fe and the other elements must not be treated as unrelated ranges.
Combined limits
- Combined-element limits
- Requirement
- Sum of other specified elements ≤60.50%; Fe is calculated by difference and is ≥39.50%
- Element coefficient
- C
- 1
- Mn
- 1
- P
- 1
- S
- 1
- Si
- 1
- Cr
- 1
- Ni
- 1
- Cu
- 1
- Al
- 1
- Ti
- 1
- Upper limit
- 60.5
- Requirement
- Fe is calculated as 100 minus the sum of other specified elements
- Element coefficient
- C
- 1
- Mn
- 1
- P
- 1
- S
- 1
- Si
- 1
- Cr
- 1
- Ni
- 1
- Cu
- 1
- Fe
- 1
- Al
- 1
- Ti
- 1
- Lower limit
- 100
- Upper limit
- 100
- Elements requiring measured values from the same heat
- Basis for Fe balance
- Footnote H: Fe is calculated as 100 minus the sum of the other specified elements; Do not use directly as an envelope of independent element limits.
N08810 · ASTM A312/A312M-2017
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Nickel and nickel alloys
- Subcategory
- Nickel and nickel alloys
- Material form
- Reference record
- Original record status
- Original-standard record
- Standard edition
- ASTM A312/A312M-2017
- Table / clause
- Table 1, footnotes A–M and clause 7.1
- PDF page references
- 1、2、6
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | 0.05 ～ 0.1 |
| Mn | ≤ 1.5 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Cr | 19.0 ～ 23.0 |
| Ni | 30.0 ～ 35.0 |
| Ti | 0.15 ～ 0.6 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Al | 0.15 ～ 0.6 |
| Fe | ≥ 39.5 (upper limit not stated) |
Applicability and limitations
Table 1, mass percent; A single value is a maximum; ellipses mean unspecified and are not entered as zero. ; Clause 7.1 requires compliance with Table 1; The general A999/A999M requirements in Clause 5.1 still apply; only the chemical-composition table was checked in this batch. ; Austenitic steel pipe standard; This does not directly establish cold-heading wire suitability or compliance with all product acceptance requirements. ; Footnote C: the nitrogen-analysis method is agreed between purchaser and supplier. ; Footnote J: Fe is calculated as 100 minus the sum of other specified elements and must be at least 39.5%.
Combined limits
- Combined-element limits
- Requirement
- Sum of other specified elements ≤60.50%
- Element coefficient
- C
- 1
- Mn
- 1
- P
- 1
- S
- 1
- Si
- 1
- Cr
- 1
- Ni
- 1
- Ti
- 1
- Cu
- 1
- Al
- 1
- Upper limit
- 60.5
- Requirement
- Fe=100 minus the sum of other specified elements
- Element coefficient
- C
- 1
- Mn
- 1
- P
- 1
- S
- 1
- Si
- 1
- Cr
- 1
- Ni
- 1
- Ti
- 1
- Cu
- 1
- Al
- 1
- Fe
- 1
- Lower limit
- 100
- Upper limit
- 100
N08810 · ASTM A182/A182M-2025
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.15 ～ 0.6 |
| C | 0.05 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Fe | ≥ 39.5 (upper limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.15 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
N08810 · ASTM A240/240M-2018
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.15 ～ 0.6 |
| C | 0.05 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Fe | ≥ 39.5 (upper limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.15 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
N08810 · ASTM A276/A276M-2017
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.15 ～ 0.6 |
| C | 0.05 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Fe | ≥ 39.5 (upper limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.15 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
N08810 · ASTM A276/A276M-2025
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.15 ～ 0.6 |
| C | 0.05 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.15 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
N08810 · ASTM A479/A479M-2018
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.15 ～ 0.6 |
| C | 0.05 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.15 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
N08810 · ASTM A479/A479M-2025
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.15 ～ 0.6 |
| C | 0.05 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.15 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
N08810 · ASTM A511/A511M-2020
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.15 ～ 0.6 |
| C | 0.05 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.15 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
N08810 · ASTM A511/A511M-2025
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.15 ～ 0.6 |
| C | 0.05 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Fe | ≥ 39.5 (upper limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.15 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
N08810 · ASTM B 408-2022
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Alloy steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.15 ～ 0.6 |
| C | 0.05 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.15 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
N08810 · ASTM B 564-2025
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Nickel and nickel alloys
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.15 ～ 0.6 |
| C | 0.05 ～ 0.1 |
| Cr | 19 ～ 23 |
| Cu | ≤ 0.75 (lower limit not stated) |
| Fe | ≥ 39.5 (upper limit not stated) |
| Mn | ≤ 1.5 (lower limit not stated) |
| Ni | 30 ～ 35 |
| S | ≤ 0.015 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Ti | 0.15 ～ 0.6 |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.