HPB61-2-1
1 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for HPB61-2-1 →HPb61-2-1 · GB/T 5231-2012
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Copper and copper alloys
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- GB/T 5231-2012
- Table / clause
- Table 3, row 24, designation T36220
- PDF page references
- 7、9
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Cu | 59.0 ～ 62.0 |
| Pb | 1.0 ～ 2.5 |
| Sn | 0.3 ～ 1.5 |
| As | 0.02 ～ 0.25 |
Applicability and limitations
Mass fraction wt%; GB/T5231—2012, Table 3, row 24, designation T36220. Zn is balance. Total table-listed impurities ≤0.4%; confirm the calculation scope under clause 2.3 and the row footnotes. A partial sum of listed elements does not replace complete analysis. Note a to Table 3: Fe≤0.030% for nonmagnetic brass applies only to that condition, not to this leaded-brass row. Clause 2.2: unlisted elements are not assigned zero. Clause 2.4: balance Zn must not be mechanically converted into a guaranteed range.
Combined limits
- Combined-element limits
- Elements requiring measured values from the same heat