H59
7 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for H59 →H59 · GB /T 5231-2001
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Copper and copper alloys
- Subcategory
- Copper and copper alloys
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- GB/T 5231-2001
- Table / clause
- Table 2 and footnotes
- PDF page references
- 1、3、4、5、6、7、8、9、10、11、12、13、14
Carbon-equivalent reference
Estimates are presented separately for each applicable composition condition. Match the actual ordering conditions; ranges must not be combined.
Table 2 standard condition
Table 2, Note 1: Fe ≤0.030% for non-magnetic brass; do not automatically combine with other purchasing conditions
Composition record (conditional branches apply; this is not an unconditional requirement)
| Element | Composition requirement |
|---|---|
| Cu | 57.0 ～ 60.0 |
| Fe | ≤ 0.3 (lower limit not stated) |
| Pb | ≤ 0.5 (lower limit not stated) |
| Ni | ≤ 0.5 (lower limit not stated) |
Applicability and limitations
Mass fraction wt%; Under 2.2, elements with specified lower and upper limits are alloying constituents; a single value is a minimum for copper and a maximum for other elements. A dash means unspecified; it is not entered as zero; Cu+Ag and Ni+Co are subject to combined ranges and are not converted into independent element ranges. The balance remains a balance; subtracting independent maxima does not establish a guaranteed range. Total impurities include all relevant impurities; The sum of listed elements is only a necessary condition and cannot replace complete impurity analysis. Product forms in the original document define the applicable wrought-product scope; they do not establish confirmed supply of cold-heading wire or final properties. Zn is the balance; Total impurities ≤1.0%. Table 2, note 1: Fe≤0.030% applies to nonmagnetic brass only where nonmagnetic performance is expressly required; Ordinary conditions are not automatically tightened.
Combined limits
- Combined-element limits
- Elements requiring measured values from the same heat
- Element-sum limits
- Elements concerned
- Fe
- Pb
- Ni
- Upper limit
- 1.0
Original condition-branch records
Table 2 standard condition
| Element | Composition requirement |
|---|---|
| Cu | 57.0 ～ 60.0 |
| Fe | ≤ 0.3 (lower limit not stated) |
| Pb | ≤ 0.5 (lower limit not stated) |
| Ni | ≤ 0.5 (lower limit not stated) |
Table 2, Note 1: Fe ≤0.030% for non-magnetic brass; do not automatically combine with other purchasing conditions
| Element | Composition requirement |
|---|---|
| Cu | 57.0 ～ 60.0 |
| Fe | ≤ 0.03 (lower limit not stated) |
| Pb | ≤ 0.5 (lower limit not stated) |
| Ni | ≤ 0.5 (lower limit not stated) |
A condition branch must be selected
YesVerification notes
The official GB/T 5231—2001 tables 1–4 and applicable footnotes were checked row by row against the source. The condition conflict for seven grades whose Fe content is incompatible with non-magnetic requirements is retained; it is not applied automatically.H59 · GB/T 5231-2012
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Copper and copper alloys
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- GB/T 5231-2012
- Table / clause
- Table 3, row 11, designation T28200
- PDF page references
- 7、9
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Cu | 57 ～ 60 |
| Fe | ≤ 0.3 (lower limit not stated) |
| Pb | ≤ 0.5 (lower limit not stated) |
Applicability and limitations
Mass fraction wt%; GB/T5231—2012, Table 3, row 11, designation T28200. Zn is balance. Total table-listed impurities ≤1.0%, covering all impurities outside the principal constituents. A partial sum of listed elements does not replace complete impurity analysis. Clause 2.2: single values for other impurity elements are maxima; unlisted limits require purchaser-supplier agreement and are not replaced with zero. This standard covers wrought copper/copper-alloy designations and chemical composition only; it does not establish actual cold-heading wire supply.
Combined limits
- Combined-element limits
- Elements requiring measured values from the same heat
Verification notes
Each cell in row 11 of Table 3 in the scanned original, together with applicable footnotes, was checked manuallyH59 · GB/T 5231-2001
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Copper and copper alloys
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- GB/T 5231-2001
- Table / clause
- Table 2 and footnotes
- PDF page references
- 1、3、4、5、6、7、8、9、10、11、12、13、14
Carbon-equivalent reference
Estimates are presented separately for each applicable composition condition. Match the actual ordering conditions; ranges must not be combined.
Table 2 standard condition
Table 2, Note 1: Fe ≤0.030% for non-magnetic brass; do not automatically combine with other purchasing conditions
Composition record (conditional branches apply; this is not an unconditional requirement)
| Element | Composition requirement |
|---|---|
| Cu | 57.0 ～ 60.0 |
| Fe | ≤ 0.3 (lower limit not stated) |
| Pb | ≤ 0.5 (lower limit not stated) |
| Ni | ≤ 0.5 (lower limit not stated) |
Applicability and limitations
Mass fraction wt%; Under 2.2, elements with specified lower and upper limits are alloying constituents; a single value is a minimum for copper and a maximum for other elements. A dash means unspecified; it is not entered as zero; Cu+Ag and Ni+Co are subject to combined ranges and are not converted into independent element ranges. The balance remains a balance; subtracting independent maxima does not establish a guaranteed range. Total impurities include all relevant impurities; The sum of listed elements is only a necessary condition and cannot replace complete impurity analysis. Product forms in the original document define the applicable wrought-product scope; they do not establish confirmed supply of cold-heading wire or final properties. Zn is the balance; Total impurities ≤1.0%. Table 2, note 1: Fe≤0.030% applies to nonmagnetic brass only where nonmagnetic performance is expressly required; Ordinary conditions are not automatically tightened.
Combined limits
- Combined-element limits
- Elements requiring measured values from the same heat
- Element-sum limits
- Elements concerned
- Fe
- Pb
- Ni
- Upper limit
- 1.0
Original condition-branch records
Table 2 standard condition
| Element | Composition requirement |
|---|---|
| Cu | 57.0 ～ 60.0 |
| Fe | ≤ 0.3 (lower limit not stated) |
| Pb | ≤ 0.5 (lower limit not stated) |
| Ni | ≤ 0.5 (lower limit not stated) |
Table 2, Note 1: Fe ≤0.030% for non-magnetic brass; do not automatically combine with other purchasing conditions
| Element | Composition requirement |
|---|---|
| Cu | 57.0 ～ 60.0 |
| Fe | ≤ 0.03 (lower limit not stated) |
| Pb | ≤ 0.5 (lower limit not stated) |
| Ni | ≤ 0.5 (lower limit not stated) |
A condition branch must be selected
YesVerification notes
The official GB/T 5231—2001 tables 1–4 and applicable footnotes were checked row by row against the source. The condition conflict for seven grades whose Fe content is incompatible with non-magnetic requirements is retained; it is not applied automatically.H59 · GB/T 5231-2012
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Copper and copper alloys
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- GB/T 5231-2012
- Table / clause
- Table 3, row 11, designation T28200
- PDF page references
- 7
- Unit
- Mass fraction (wt%)
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Cu | 57.0 ～ 60.0 |
| Fe | ≤ 0.3 (lower limit not stated) |
| Pb | ≤ 0.5 (lower limit not stated) |
Applicability and limitations
Mass fraction wt%; GB/T 5231-2012, Table 3, row 11, designation T28200; scanned PDF, PDF physical page 7. Zn is balance; dashes mean unspecified and are not replaced with zero. Clause 2.2: single impurity values in the table are maxima. The total of table-listed impurities is ≤1% and must be checked against measured values for the impurity elements specified in the standard. This standard provides the grade-composition basis for wrought copper and copper alloys; actual supply and cold-heading suitability require separate confirmation.
Combined limits
- Combined-element limits
- Elements requiring measured values from the same heat
Verification notes
The original scanned standard, Table 3 was manually checked cell by cell; Coupled elements and application-specific footnotes require separate verificationH59 · GB /T 5231-2022
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Copper and copper alloys
- Subcategory
- Copper and copper alloys
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Cu | 57 ～ 60 |
| Fe | ≤ 0.3 (lower limit not stated) |
| Pb | ≤ 0.5 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
H59 · YS /T 649-2018
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Copper and copper alloys
- Subcategory
- Copper and copper alloys
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Cu | 57 ～ 60 |
| Fe | ≤ 0.3 (lower limit not stated) |
| Pb | ≤ 0.5 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
H59 · YS /T 649-2018
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Copper and copper alloys
- Subcategory
- Copper and copper alloys
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Cu | 57 ～ 60 |
| Fe | ≤ 0.3 (lower limit not stated) |
| Pb | ≤ 0.5 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.