CW6Mo5Cr4V3 · GB/T 9943-2025

Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results

Subcategory: High-speed tool steel
Material form: Reference record
Original record status: Original standard verified
Standard edition: GB/T 9943-2025
Table / clause: Table 1 · Notes a/b
PDF page references: 7、8

Carbon-equivalent reference

Estimates are presented separately for each applicable composition condition. Match the actual ordering conditions; ranges must not be combined.

Table 1 heat analysis, excluding electroslag-remelted steel

IIW / CEV：3.5050–3.9667Known-element contribution; incomplete value; missing Ni, Cu CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15; an engineering estimate of welding cold-cracking susceptibility for carbon and low-alloy steels.

Pcm（Ito–Bessyo）：2.0283–2.2550Known-element contribution; incomplete value; missing Cu, Ni, B Pcm = C + Si/30 + (Mn + Cu + Cr)/20 + Ni/60 + Mo/15 + V/10 + 5B; mainly used for low-carbon low-alloy steels, particularly modern low-carbon pipeline steels; more relevant when C is approximately no higher than 0.11%.

CET：1.9225–2.1050Known-element contribution; incomplete value; missing Cu, Ni CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40; used in welding preheat assessment for ferritic steels, subject to the applicability conditions of EN 1011-2.

Table 1, note a: no Si minimum is specified for electroslag-remelted steel

Composition record (conditional branches apply; this is not an unconditional requirement)

Element	Composition requirement
C	1.25 ～ 1.32
Si	≤ 0.7 (lower limit not stated)
Mn	0.15 ～ 0.4
Cr	3.75 ～ 4.5
Mo	4.7 ～ 5.2
V	2.7 ～ 3.2
W	5.9 ～ 6.7
P	≤ 0.03 (lower limit not stated)
S	≤ 0.02 (lower limit not stated)

Applicability and limitations

GB/T9943-2025, Table 1, heat analysis, mass percent. ; Note a: No lower limit for Si in ESR steel; ranges of other elements shall not be changed because of this. ; Note b: Special S requirements may be specified in the contract to improve machining performance; since specific values are not provided, the general special S range shall not be filled in arbitrarily. ; Clause 7.1.2: Product-analysis tolerances are specified in Table 2; the heat-analysis limits have not been automatically expanded.. ; High-speed tool steel standards are not proof of suitability for cold-heading wire; Do not automatically add this to the range of cold-heading products available for supply..

Original condition-branch records

Table 1 heat analysis, excluding electroslag-remelted steel

Element	Composition requirement
C	1.25 ～ 1.32
Si	≤ 0.7 (lower limit not stated)
Mn	0.15 ～ 0.4
Cr	3.75 ～ 4.5
Mo	4.7 ～ 5.2
V	2.7 ～ 3.2
W	5.9 ～ 6.7
P	≤ 0.03 (lower limit not stated)
S	≤ 0.02 (lower limit not stated)

Table 1, note a: no Si minimum is specified for electroslag-remelted steel

Element	Composition requirement
C	1.25 ～ 1.32
Si	≤ 0.7 (lower limit not stated)
Mn	0.15 ～ 0.4
Cr	3.75 ～ 4.5
Mo	4.7 ～ 5.2
V	2.7 ～ 3.2
W	5.9 ～ 6.7
P	≤ 0.03 (lower limit not stated)
S	≤ 0.02 (lower limit not stated)