A814 TP 316L
1 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for A814 TP 316L →A814 TP 316L · ASTM A814/A814M-2015(R2019)
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Stainless steel
- Subcategory
- Austenitic stainless steel
- Material form
- Reference record
- Original record status
- Adopted-standard basis verified
- Standard edition
- ASME SA-814/SA-814M-2023
- Table / clause
- Table 2, notes A–H; clauses 5.1/5.2; identity statement on PDF page 1
- PDF page references
- 1、4、5
Carbon-equivalent reference
Estimates are presented separately for each applicable composition condition. Match the actual ordering conditions; ranges must not be combined.
Table 2, ordinary condition C≤.030%
Note D: where multiple drawing passes are required and tube outside diameter <12.7mm or the wall is thin (average <1.2mm / minimum <1mm), C≤.040% applies; All conditions must be confirmed
Composition record (conditional branches apply; this is not an unconditional requirement)
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Ni | 10.0 ～ 14.0 |
| Cr | 16.0 ～ 18.0 |
| Mo | 2.0 ～ 3.0 |
Applicability and limitations
Composition alloy: S31603. Table 2, mass fraction wt%; values are maxima except where explicit ranges are given. Ellipses are not replaced with zero. The source actually read is ASME BPVC.II.A-2023 SA814; the cover explicitly states that it is identical to ASTM A814/A814M-15(2019). The analytical method for N is subject to agreement between purchaser and supplier. Product-analysis tolerances under A480/A480M require separate verification and are not incorporated into this table. This standard covers cold-worked welded stainless steel pipe and does not automatically approve a cold-heading product.
Original condition-branch records
Table 2, ordinary condition C≤.030%
| Element | Composition requirement |
|---|---|
| C | ≤ 0.03 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Ni | 10.0 ～ 14.0 |
| Cr | 16.0 ～ 18.0 |
| Mo | 2.0 ～ 3.0 |
Note D: where multiple drawing passes are required and tube outside diameter <12.7mm or the wall is thin (average <1.2mm / minimum <1mm), C≤.040% applies; All conditions must be confirmed
| Element | Composition requirement |
|---|---|
| C | ≤ 0.04 (lower limit not stated) |
| Mn | ≤ 2.0 (lower limit not stated) |
| P | ≤ 0.045 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1.0 (lower limit not stated) |
| Ni | 10.0 ～ 14.0 |
| Cr | 16.0 ～ 18.0 |
| Mo | 2.0 ～ 3.0 |