A322 1340
1 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for A322 1340 →A322 1340 · ASTM A322-1991(R2001)e1
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- ASTM A322-1991(R2001)e1
- Table / clause
- Table 1 · Notes A–G
- PDF page references
- 1、2、3
Carbon-equivalent reference
Estimates are presented separately for each applicable composition condition. Match the actual ordering conditions; ranges must not be combined.
Table 1 default Si .15–.35%
Purchaser specifies Si≤.10%
Composition record (conditional branches apply; this is not an unconditional requirement)
| Element | Composition requirement |
|---|---|
| C | 0.38 ～ 0.43 |
| Mn | 1.6 ～ 1.9 |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.04 (lower limit not stated) |
| Si | 0.15 ～ 0.35 |
| Ni | ≤ 0.25 (lower limit not stated) |
| Cr | ≤ 0.2 (lower limit not stated) |
| Mo | ≤ 0.06 (lower limit not stated) |
| Cu | ≤ 0.35 (lower limit not stated) |
Applicability and limitations
Original header A322–91(Reapproved2001)e1; note e1 records correction of Table 1 in year 2004, month 5. The full edition is retained, not represented as 2013/2024. Cast analysis wt%. Note A gives maximum incidental contents for elements not otherwise specified or required: Cu≤.35/Ni≤.25/Cr≤.20/Mo≤.06; explicitly specified alloy ranges take priority. Note F: the purchaser may specify Si≤.10%, usually for severely cold-formed parts; default Si .15–.35%. Select the two conditions separately; this does not establish cold-heading supply availability. Note B: adding Pb .15–.35% requires L identification; not included in ordinary grades. This standard covers hot-worked alloy steel bars; coiled dimensions and applicability require supplier confirmation. Product deviations and other composition agreements referring to A29 require separate verification. Original-table UNS G13400; grade column 1340.
Original condition-branch records
Table 1 default Si .15–.35%
| Element | Composition requirement |
|---|---|
| C | 0.38 ～ 0.43 |
| Mn | 1.6 ～ 1.9 |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.04 (lower limit not stated) |
| Si | 0.15 ～ 0.35 |
| Ni | ≤ 0.25 (lower limit not stated) |
| Cr | ≤ 0.2 (lower limit not stated) |
| Mo | ≤ 0.06 (lower limit not stated) |
| Cu | ≤ 0.35 (lower limit not stated) |
Purchaser specifies Si≤.10%
| Element | Composition requirement |
|---|---|
| C | 0.38 ～ 0.43 |
| Mn | 1.6 ～ 1.9 |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.04 (lower limit not stated) |
| Si | ≤ 0.1 (lower limit not stated) |
| Ni | ≤ 0.25 (lower limit not stated) |
| Cr | ≤ 0.2 (lower limit not stated) |
| Mo | ≤ 0.06 (lower limit not stated) |
| Cu | ≤ 0.35 (lower limit not stated) |