5A06
8 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for 5A06 →5A06 · GB /T 3190-2008
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Aluminum and aluminum alloys
- Subcategory
- Aluminum and aluminum alloys
- Material form
- Reference record
- Original record status
- Original text of the historical edition verified
- Standard edition
- GB/T 3190—1996
- Table / clause
- Table 1; Clause 4.1～4.5 · Footnotes
- PDF page references
- 3、9、13
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Si | ≤ 0.4 (lower limit not stated) |
| Fe | ≤ 0.4 (lower limit not stated) |
| Cu | ≤ 0.1 (lower limit not stated) |
| Mn | 0.5 ～ 0.8 |
| Mg | 5.8 ～ 6.8 |
| Zn | ≤ 0.2 (lower limit not stated) |
| Ti | 0.02 ～ 0.1 |
| Be | 0.0001 ～ 0.005 |
Applicability and limitations
GB/T 3190—1996, Table 1, mass percent; Unspecified elements are not treated as zero. ; This standard covers chemical composition of wrought aluminum and aluminum alloys; This does not establish cold-heading suitability, actual supply or finished-product properties. ; Al is the balance; The original table specifies no independent numerical range for Al. ; Individual and combined limits for other impurities concern only the other elements defined in Clause 4.3 of the standard, not the sum of all principal alloying elements; Missing impurity test results must not be treated as zero. ; Table 1, footnote 2: beryllium is added in the specified amount and need not be analyzed.
Combined limits
- Other-impurity requirements in the source
- Each other impurity
- 0.05
- Sum of other impurities
- 0.1
- Other impurities require technical review
- Yes
- Conditional requirements in the source
- Footnote
- 2
- Source conditions
- Beryllium is added in the specified amount and need not be analyzed.
- Automatic evaluation implemented
- No
Verification notes
The original GB/T 3190—1996, Table 1 is used as an explicitly historical basis; The 2008/2020 edition cited in the original index has not been verified.5A06 · GB /T 3190-2020
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Aluminum and aluminum alloys
- Subcategory
- Aluminum and aluminum alloys
- Material form
- Reference record
- Original record status
- Original text of the historical edition verified
- Standard edition
- GB/T 3190—1996
- Table / clause
- Table 1; Clause 4.1～4.5 · Footnotes
- PDF page references
- 3、9、13
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Si | ≤ 0.4 (lower limit not stated) |
| Fe | ≤ 0.4 (lower limit not stated) |
| Cu | ≤ 0.1 (lower limit not stated) |
| Mn | 0.5 ～ 0.8 |
| Mg | 5.8 ～ 6.8 |
| Zn | ≤ 0.2 (lower limit not stated) |
| Ti | 0.02 ～ 0.1 |
| Be | 0.0001 ～ 0.005 |
Applicability and limitations
GB/T 3190—1996, Table 1, mass percent; Unspecified elements are not treated as zero. ; This standard covers chemical composition of wrought aluminum and aluminum alloys; This does not establish cold-heading suitability, actual supply or finished-product properties. ; Al is the balance; The original table specifies no independent numerical range for Al. ; Individual and combined limits for other impurities concern only the other elements defined in Clause 4.3 of the standard, not the sum of all principal alloying elements; Missing impurity test results must not be treated as zero. ; Table 1, footnote 2: beryllium is added in the specified amount and need not be analyzed.
Combined limits
- Other-impurity requirements in the source
- Each other impurity
- 0.05
- Sum of other impurities
- 0.1
- Other impurities require technical review
- Yes
- Conditional requirements in the source
- Footnote
- 2
- Source conditions
- Beryllium is added in the specified amount and need not be analyzed.
- Automatic evaluation implemented
- No
Verification notes
The original GB/T 3190—1996, Table 1 is used as an explicitly historical basis; The 2008/2020 edition cited in the original index has not been verified.5A06 · GB/T 3190—1996
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Aluminum and aluminum alloys
- Subcategory
- Aluminum and aluminum alloys
- Material form
- Reference record
- Original record status
- Original-standard record
- Standard edition
- GB/T 3190—1996
- Table / clause
- Table 1; Clause 4.1～4.5 · Footnotes
- PDF page references
- 3、9、13
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Si | ≤ 0.4 (lower limit not stated) |
| Fe | ≤ 0.4 (lower limit not stated) |
| Cu | ≤ 0.1 (lower limit not stated) |
| Mn | 0.5 ～ 0.8 |
| Mg | 5.8 ～ 6.8 |
| Zn | ≤ 0.2 (lower limit not stated) |
| Ti | 0.02 ～ 0.1 |
| Be | 0.0001 ～ 0.005 |
Applicability and limitations
GB/T 3190—1996, Table 1, mass percent; Unspecified elements are not treated as zero. ; This standard covers chemical composition of wrought aluminum and aluminum alloys; This does not establish cold-heading suitability, actual supply or finished-product properties. ; Al is the balance; The original table specifies no independent numerical range for Al. ; Individual and combined limits for other impurities concern only the other elements defined in Clause 4.3 of the standard, not the sum of all principal alloying elements; Missing impurity test results must not be treated as zero. ; Table 1, footnote 2: beryllium is added in the specified amount and need not be analyzed.
Combined limits
- Other-impurity requirements in the source
- Each other impurity
- 0.05
- Sum of other impurities
- 0.1
- Other impurities require technical review
- Yes
- Conditional requirements in the source
- Footnote
- 2
- Source conditions
- Beryllium is added in the specified amount and need not be analyzed.
- Automatic evaluation implemented
- No
5A06 · GB /T 3195-2016
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Aluminum and aluminum alloys
- Subcategory
- Aluminum and aluminum alloys
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Cu | ≤ 0.1 (lower limit not stated) |
| Fe | ≤ 0.4 (lower limit not stated) |
| Mg | 5.8 ～ 6.8 |
| Mn | 0.5 ～ 0.8 |
| Si | ≤ 0.4 (lower limit not stated) |
| Ti | 0.02 ～ 0.1 |
| Zn | ≤ 0.2 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
5A06 · GB /T 3195-2023
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Aluminum and aluminum alloys
- Subcategory
- Aluminum and aluminum alloys
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Cu | ≤ 0.1 (lower limit not stated) |
| Fe | ≤ 0.4 (lower limit not stated) |
| Mg | 5.8 ～ 6.8 |
| Mn | 0.5 ～ 0.8 |
| Si | ≤ 0.4 (lower limit not stated) |
| Ti | 0.02 ～ 0.1 |
| Zn | ≤ 0.2 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
5A06 · GB /T 3880.1-2012
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Aluminum and aluminum alloys
- Subcategory
- Aluminum and aluminum alloys
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Cu | ≤ 0.1 (lower limit not stated) |
| Fe | ≤ 0.4 (lower limit not stated) |
| Mg | 5.8 ～ 6.8 |
| Mn | 0.5 ～ 0.8 |
| Si | ≤ 0.4 (lower limit not stated) |
| Ti | 0.02 ～ 0.1 |
| Zn | ≤ 0.2 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
5A06 · GJB 2053A-2008
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Aluminum and aluminum alloys
- Subcategory
- Aluminum and aluminum alloys
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Cu | ≤ 0.1 (lower limit not stated) |
| Fe | ≤ 0.4 (lower limit not stated) |
| Mg | 5.8 ～ 6.8 |
| Mn | 0.5 ～ 0.8 |
| Si | ≤ 0.4 (lower limit not stated) |
| Ti | 0.02 ～ 0.1 |
| Zn | ≤ 0.2 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
5A06 · GJB 390A-2008
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Aluminum and aluminum alloys
- Subcategory
- Aluminum and aluminum alloys
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Cu | ≤ 0.1 (lower limit not stated) |
| Fe | ≤ 0.4 (lower limit not stated) |
| Mg | 5.8 ～ 6.8 |
| Mn | 0.5 ～ 0.8 |
| Si | ≤ 0.4 (lower limit not stated) |
| Ti | 0.02 ～ 0.1 |
| Zn | ≤ 0.2 (lower limit not stated) |
Applicability and limitations