54SICRV6
2 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for 54SICRV6 →54SiCrV6 · DIN EN 10089-2003
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Spring steels
- Subcategory
- Spring steels
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- DIN EN 10089-2003
- Table / clause
- Table 3 and notes a/b and 7.1; Only the first 17 pages of the original text are available
- PDF page references
- 1、7、9、12、13
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | 0.51 ～ 0.59 |
| Si | 1.2 ～ 1.6 |
| Mn | 0.5 ～ 0.8 |
| Cr | 0.5 ～ 0.8 |
| V | 0.1 ～ 0.2 |
| P | ≤ 0.025 (lower limit not stated) |
| S | ≤ 0.025 (lower limit not stated) |
| Cu | ≤ 0.6 (lower limit not stated) |
| Sn | ≤ 0.06 (lower limit not stated) |
Applicability and limitations
DIN EN10089:2003-04 official English original, adopting standard EN10089:2002; Table 3 heat analysis wt%. ; Cu+10Sn≤.60%; Cu≤.60/Sn≤.06 are only single-item envelopes derived from the linkage formula under the condition that each element is non-negative; they are not independent limits from the original table and the linkage formula must be satisfied simultaneously. ; Table 3 Note a: unspecified elements shall not be intentionally added without the purchaser's consent (except additions needed to finish steelmaking); blanks shall not be filled as zero. ; Note b: when hardenability is specified, C may deviate slightly but not exceed ±.01, others shall comply with Table 4 except for P/S; Default composition has not been automatically relaxed. ; This document contains only the first 17 pages; Table 3 is complete and verifiable; Hardenability Tables 7/8 and other missing pages need to be supplemented separately; the completeness of the entire standard is not claimed. ; Hot-rolled spring steels intended for quenching and tempering; composition or annealed condition alone does not establish cold-heading suitability or actual supply..
Combined limits
- Combined-element limits
- Element coefficient
- Cu
- 1
- Sn
- 10
- Upper limit
- 0.6
- Requirement
- Cu + 10Sn ≤ 0.60 wt%
Verification notes
Official original Table 3: all 19 rows and footnotes visually checked.Jominy end-quench hardenability (conditional requirements)
EN 10089:2002 · BS EN 10089:2002 · Tables 7/8, 7.1.2–7.1.4 and Table 10 · PDF pages 6, 9, 17, 18, 20, 21
- Footnote a of Table 7/Table 8 refers to Figure 1; The scatter bands for +H and +HH shall be maintained separately; lower limits shall not be interchanged.
- Applicable only to conditions where the corresponding +H or +HH hardenability symbols are actually used for ordering; Specific delivery condition and dimension range shall still be confirmed according to the order and Table 1 of the standard.
- When ordering based on core hardness requirements per 7.1.3, the end-quench data in Table 7/Table 8 are for reference only and cannot serve as an acceptance guarantee for the same order item.
- HRC is the hardness at the specified distance of the end-quench test specimen, not the overall hardness of the finished product, nor does it prove cold-heading suitability or part performance.
- A horizontal line in the original table indicates that the lower limit for that distance is not specified and shall remain blank; Shall not be treated as 0; no interpolation, extrapolation, or conformity determination shall be performed for distances not listed.
- The shown quenching temperature is the standard end-quench test condition and cannot be used as a production heat treatment process parameter or recommendation.
- Testing shall be according to EN ISO642 as cited in Table 10 (source standard specifies ISO642:1999); Test units shall be divided by heat, with 1 sample per unit and 1 test per sample; sampling for disputes shall otherwise follow Table 10.
- This record is for DIN EN10089:2003-04 adopting EN10089:2002; Hardenability data is explicitly read from the original table of BS EN10089:2002; it is not claimed that missing pages of the DIN original document have been verified or completed.
+H normal hardenability band (7.1.2)
End-quench test condition temperature 860 ± 5 °C; This is not a production heat-treatment recommendation.
| Distance from quenched end (mm) | Lower limit (HRC) | Upper limit (HRC) |
|---|---|---|
| 1.5 | 57 | 67 |
| 3 | 56 | 66 |
| 5 | 55 | 65 |
| 7 | 50 | 63 |
| 9 | 44 | 62 |
| 11 | 40 | 60 |
| 13 | 37 | 57 |
| 15 | 35 | 55 |
| 20 | 32 | 47 |
| 25 | 30 | 43 |
| 30 | 28 | 40 |
| 35 | 26 | 38 |
| 40 | 25 | 37 |
| 45 | 24 | 36 |
| 50 | 24 | 35 |
+HH restricted hardenability band (7.1.4)
End-quench test condition temperature 860 ± 5 °C; This is not a production heat-treatment recommendation.
| Distance from quenched end (mm) | Lower limit (HRC) | Upper limit (HRC) |
|---|---|---|
| 1.5 | 60 | 67 |
| 3 | 59 | 66 |
| 5 | 58 | 65 |
| 7 | 54 | 63 |
| 9 | 50 | 62 |
| 11 | 47 | 60 |
| 13 | 44 | 57 |
| 15 | 42 | 55 |
| 20 | 37 | 47 |
| 25 | 34 | 43 |
| 30 | 32 | 40 |
| 35 | 30 | 38 |
| 40 | 29 | 37 |
| 45 | 28 | 36 |
| 50 | 28 | 35 |
54SiCrV6 · EN 10089-2002
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Spring steels
- Subcategory
- Spring steels
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- BS EN 10089:2002 (EN 10089:2002)
- Table / clause
- 7.1/Table 3, notes a/b
- PDF page references
- 3、9、13、14
- Unit
- Mass fraction (wt%)
- Analysis type
- Heat analysis
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | 0.51 ～ 0.59 |
| Si | 1.2 ～ 1.6 |
| Mn | 0.5 ～ 0.8 |
| Cr | 0.5 ～ 0.8 |
| V | 0.1 ～ 0.2 |
| P | ≤ 0.025 (lower limit not stated) |
| S | ≤ 0.025 (lower limit not stated) |
| Cu | ≤ 0.6 (lower limit not stated) |
| Sn | ≤ 0.06 (lower limit not stated) |
Applicability and limitations
Complete BS EN 10089:2002 original Table 3 heat analysis mass fraction wt%; Applies to hot-rolled steels for quenched-and-tempered springs; this does not by itself establish suitability for cold heading.. Cu+10Sn≤0.60wt%; Separate listings of Cu ≤0.60 and Sn ≤0.06 are only envelopes derived from a linked formula under the premise of non-negative values; both cannot be used at their upper limits simultaneously. Table 3 Note a: Elements not listed shall not be intentionally added without the purchaser's consent (except additions needed to finish steelmaking); blanks shall not be filled as zero. Table 3 Note b: When hardenability is specified, C may deviate slightly according to restricted conditions; Table 3 compositions are not automatically relaxed by default.
Combined limits
- Combined-element limits
- Element coefficient
- Cu
- 1
- Sn
- 10
- Upper limit
- 0.6
- Requirement
- Cu + 10Sn ≤ 0.60 wt%
Verification notes
All 19 grades and footnotes in original EN10089:2002, Table 3 have been checked; The original record omitted the coupled Cu+10Sn constraint.Jominy end-quench hardenability (conditional requirements)
EN 10089:2002 · BS EN 10089:2002 · Tables 7/8, 7.1.2–7.1.4 and Table 10 · PDF pages 6, 9, 17, 18, 20, 21
- Footnote a of Table 7/Table 8 refers to Figure 1; The scatter bands for +H and +HH shall be maintained separately; lower limits shall not be interchanged.
- Applicable only to conditions where the corresponding +H or +HH hardenability symbols are actually used for ordering; Specific delivery condition and dimension range shall still be confirmed according to the order and Table 1 of the standard.
- When ordering based on core hardness requirements per 7.1.3, the end-quench data in Table 7/Table 8 are for reference only and cannot serve as an acceptance guarantee for the same order item.
- HRC is the hardness at the specified distance of the end-quench test specimen, not the overall hardness of the finished product, nor does it prove cold-heading suitability or part performance.
- A horizontal line in the original table indicates that the lower limit for that distance is not specified and shall remain blank; Shall not be treated as 0; no interpolation, extrapolation, or conformity determination shall be performed for distances not listed.
- The shown quenching temperature is the standard end-quench test condition and cannot be used as a production heat treatment process parameter or recommendation.
- Testing shall be according to EN ISO642 as cited in Table 10 (source standard specifies ISO642:1999); Test units shall be divided by heat, with 1 sample per unit and 1 test per sample; sampling for disputes shall otherwise follow Table 10.
+H normal hardenability band (7.1.2)
End-quench test condition temperature 860 ± 5 °C; This is not a production heat-treatment recommendation.
| Distance from quenched end (mm) | Lower limit (HRC) | Upper limit (HRC) |
|---|---|---|
| 1.5 | 57 | 67 |
| 3 | 56 | 66 |
| 5 | 55 | 65 |
| 7 | 50 | 63 |
| 9 | 44 | 62 |
| 11 | 40 | 60 |
| 13 | 37 | 57 |
| 15 | 35 | 55 |
| 20 | 32 | 47 |
| 25 | 30 | 43 |
| 30 | 28 | 40 |
| 35 | 26 | 38 |
| 40 | 25 | 37 |
| 45 | 24 | 36 |
| 50 | 24 | 35 |
+HH restricted hardenability band (7.1.4)
End-quench test condition temperature 860 ± 5 °C; This is not a production heat-treatment recommendation.
| Distance from quenched end (mm) | Lower limit (HRC) | Upper limit (HRC) |
|---|---|---|
| 1.5 | 60 | 67 |
| 3 | 59 | 66 |
| 5 | 58 | 65 |
| 7 | 54 | 63 |
| 9 | 50 | 62 |
| 11 | 47 | 60 |
| 13 | 44 | 57 |
| 15 | 42 | 55 |
| 20 | 37 | 47 |
| 25 | 34 | 43 |
| 30 | 32 | 40 |
| 35 | 30 | 38 |
| 40 | 29 | 37 |
| 45 | 28 | 36 |
| 50 | 28 | 35 |