46MNVS6
1 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for 46MNVS6 →46MnVS6 · EN 10267-1998
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Precipitation-hardening ferritic-pearlitic steel
- Material form
- Semi-finished products and bars for hot working; select delivery condition +U, +S or +P and verify against Table 1
- Original record status
- Original standard verified
- Standard edition
- EN 10267:1998
- Table / clause
- Table 3 and footnotes 1–4; Table 1 applicability
- PDF page references
- 1、7、9
- Unit
- Mass fraction (wt%)
- Analysis type
- Heat analysis
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | 0.42 ～ 0.49 |
| Si | 0.15 ～ 0.8 |
| Mn | 1.2 ～ 1.6 |
| P | ≤ 0.025 (lower limit not stated) |
| S | 0.02 ～ 0.06 |
| N | 0.01 ～ 0.02 |
| Cr | ≤ 0.3 (lower limit not stated) |
| Mo | ≤ 0.08 (lower limit not stated) |
| V | 0.08 ～ 0.2 |
Applicability and limitations
Table 3 of EN 10267:1998 is heat analysis mass fraction wt%. ; Table 1: Table 3 and Table 4 are used for untreated +U and cold-sheared +S deliveries; The chemical composition in Table 5 for precipitation hardening +P machined bars is for guidance only; Table 3 shall not be automatically regarded as a +P delivery guarantee. ; Table 3 Footnote 2: Other elements for improving machinability or controlling sulfides/oxides, as well as adjustments to the sulfur range, shall be by agreement. ; Table 3 Footnote 3: Partial or total substitution of V by Nb requires agreement; the lower limit of V must also be separately negotiated; Current composition reverse-checks shall only use the default limits of Table 3 without substitutions. ; Table 3 Footnote 4: Ti addition shall be by agreement; Elements not listed shall not be intentionally added without the buyer's consent (except additions needed to finish steelmaking). ; Product analysis deviations in Table 4 shall be verified separately; The +P mechanical properties in Table 5 correspond only to machined bars and 30–120mm; other sizes shall be by agreement; Cold-heading suitability shall be verified separately.