40CRMOV13-9
1 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for 40CRMOV13-9 →40CrMoV13-9 · EN 10250-3-1999
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Alloy steel
- Subcategory
- Alloy steel
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- EN 10250-3-1999
- Table / clause
- Table1 and note 1/2; Clauses 1, 3.1 and 3.2
- PDF page references
- 6、8、9
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | 0.35 ～ 0.45 |
| Si | 0.15 ～ 0.4 |
| Mn | 0.4 ～ 0.7 |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.035 (lower limit not stated) |
| Cr | 3.0 ～ 3.5 |
| Mo | 0.8 ～ 1.1 |
| V | 0.15 ～ 0.25 |
Applicability and limitations
Based on the original Table 1 and footnotes of EN10250-3:1999 as recorded in BS EN10250-3:2000, heat analysis mass fraction is in wt%.. ; This standard covers alloy special-steel open-die forgings, forged bars and ring-rolled products after pre-forging, supplied in the quenched-and-tempered condition.; This does not automatically establish a supply standard for cold-heading wire.. ; Table 1 Note 1 allows the manufacturer to add Al, Ti, V, Nb individually or in combination to control grain size.; No new numerical ranges are provided; values cannot be filled as zero or have upper limits arbitrarily determined.. Elements not listed in Table 1/2 shall not be intentionally added without the consent of the purchaser (except additions needed to finish steelmaking).. ; 3.1 requires the heat analysis composition to be in accordance with Table 1 and references A.7/A.8 of EN10250-1.; Clause 3.2: Apply product-analysis tolerances separately under Table 2 and Clause 9.2 of EN10250-1; do not directly expand the default heat-analysis range.. ; Currently, only chemical compositions, grade/steel number correspondences, and related range footnotes are confirmed.; It is not declared that all mechanical properties and the referenced Part 1 have been verified..