1.7220

Based on the original Table 1 and footnotes of EN10250-3:1999 as recorded in BS EN10250-3:2000, heat analysis mass fraction is in wt%.. ; This standard covers alloy special-steel open-die forgings, forged bars and ring-rolled products after pre-forging, supplied in the quenched-and-tempered condition.; This does not automatically establish a supply standard for cold-heading wire.. ; Table 1 Note 1 allows the manufacturer to add Al, Ti, V, Nb individually or in combination to control grain size.; No new numerical ranges are provided; values cannot be filled as zero or have upper limits arbitrarily determined.. Elements not listed in Table 1/2 shall not be intentionally added without the consent of the purchaser (except additions needed to finish steelmaking).. ; 3.1 requires the heat analysis composition to be in accordance with Table 1 and references A.7/A.8 of EN10250-1.; Clause 3.2: Apply product-analysis tolerances separately under Table 2 and Clause 9.2 of EN10250-1; do not directly expand the default heat-analysis range.. ; Currently, only chemical compositions, grade/steel number correspondences, and related range footnotes are confirmed.; It is not declared that all mechanical properties and the referenced Part 1 have been verified..

A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.