06CR13AL
13 source records. Standards, editions and conditions are presented separately; matching grade names do not establish interchangeability.
Refer to each source for mass fractions and analysis type. Missing values are not treated as 0. Manufacturer typical values, standard guarantees and measured heat results must remain separate. Use the material selector for calculations and condition selection.
Open condition selection, comparison and carbon-equivalent tools for 06CR13AL →06Cr13Al · GB/T 1221-2007
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Heat-resistant steels
- Subcategory
- Ferritic heat-resistant steel
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- GB/T 1221-2007
- Table / clause
- Table 5 · Notes; 7.1
- PDF page references
- 6、8
- Unit
- Mass fraction (wt%)
- Analysis type
- Heat analysis, not product analysis
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Mn | ≤ 1 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Cr | 11.5 ～ 14.5 |
| Al | 0.1 ～ 0.3 |
Applicability and limitations
GB/T1221—2007, Table 5, heat-analysis mass fractions wt%; The actual 2007 edition is retained separately. Standard for heat-resistant steel bars; A chemistry match does not guarantee supply of cold-heading wire, heat-treatment condition, mechanical properties or heat resistance. Under the table note, values other than explicit ranges and minima are maxima; A dash indicates unspecified content and is not entered as 0. 7.1.2 product chemical-analysis tolerances require separate verification under GB/T222 and do not directly widen heat-analysis limits. This record retains the heat-resistant-steel category in the original table; applicability of conventional welding carbon-equivalent formulas has not been independently verified, so no automatic calculation is provided.
Verification notes
The 2007 original images of Tables 4–7, footnotes and Clause 7.1 were checked; the melting analysis and scope for heat-resistant steel bars are retained.06Cr13Al · GB /T 20878-2007
Chemical composition source verified; this does not verify every standard clause, actual supply or measured heat results
- Material category
- Stainless steel
- Subcategory
- Ferritic stainless and heat-resistant steels
- Material form
- Reference record
- Original record status
- Original standard verified
- Standard edition
- GB/T 20878—2007
- Table / clause
- Table 3, No. 78
- PDF page references
- 11
- Unit
- Mass fraction (wt%)
- Analysis type
- Standard composition requirements
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| C | ≤ 0.08 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
| Mn | ≤ 1 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Ni | ≤ 0.6 (lower limit not stated) |
| Cr | 11.5 ～ 14.5 |
| Al | 0.1 ～ 0.3 |
Applicability and limitations
GB/T 20878—2007 tabulated chemical-composition mass fractions wt%; Values in parentheses are maximum permitted additions; conditional expressions require manual interpretation against the original text. Ni ≤0.60 is a maximum permitted addition shown in parentheses. A material-database match does not guarantee cold-heading suitability, actual supply or finished-product strength. GB/T 20878—2007 is a historical edition; This record does not replace verification of the current standard, contract or material applicability.
Verification notes
GB/T 20878—2007 historical original, Table 3, entry 78. The complete 45-page scan was checked. The standard is withdrawn; the historical edition’s application limits are retained.06Cr13Al · GB /T 1220-2007
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Ferritic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.1 ～ 0.3 |
| C | ≤ 0.08 (lower limit not stated) |
| Cr | 11.5 ～ 14.5 |
| Mn | ≤ 1 (lower limit not stated) |
| Ni | ≤ 0.6 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
06Cr13Al · GB /T 12770-2012
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Ferritic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.1 ～ 0.3 |
| C | ≤ 0.08 (lower limit not stated) |
| Cr | 11.5 ～ 14.5 |
| Mn | ≤ 1 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 0.75 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
06Cr13Al · GB /T 12771-2019
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Ferritic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.1 ～ 0.3 |
| C | ≤ 0.08 (lower limit not stated) |
| Cr | 11.5 ～ 14.5 |
| Mn | ≤ 1 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
06Cr13Al · GB /T 14975-2012
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Ferritic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.1 ～ 0.3 |
| C | ≤ 0.08 (lower limit not stated) |
| Cr | 11.5 ～ 14.5 |
| Mn | ≤ 1 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
06Cr13Al · GB /T 14976-2012
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Ferritic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.1 ～ 0.3 |
| C | ≤ 0.08 (lower limit not stated) |
| Cr | 11.5 ～ 14.5 |
| Mn | ≤ 1 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
06Cr13Al · GB /T 20878-2024
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Ferritic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.1 ～ 0.3 |
| C | ≤ 0.08 (lower limit not stated) |
| Cr | 11.5 ～ 14.5 |
| Mn | ≤ 1 (lower limit not stated) |
| Ni | ≤ 0.6 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
06Cr13Al · GB /T 24511-2017
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Duplex stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.1 ～ 0.3 |
| C | ≤ 0.08 (lower limit not stated) |
| Cr | 11.5 ～ 14.5 |
| Mn | ≤ 1 (lower limit not stated) |
| Ni | ≤ 0.6 (lower limit not stated) |
| P | ≤ 0.035 (lower limit not stated) |
| S | ≤ 0.02 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
06Cr13Al · GB /T 3280-2015
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Ferritic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.1 ～ 0.3 |
| C | ≤ 0.08 (lower limit not stated) |
| Cr | 11.5 ～ 14.5 |
| Mn | ≤ 1 (lower limit not stated) |
| Ni | ≤ 0.6 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
06Cr13Al · GB /T 4237-2015
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Ferritic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.1 ～ 0.3 |
| C | ≤ 0.08 (lower limit not stated) |
| Cr | 11.5 ～ 14.5 |
| Mn | ≤ 1 (lower limit not stated) |
| Ni | ≤ 0.6 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
06Cr13Al · GB /T 4238-2015
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Ferritic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.1 ～ 0.3 |
| C | ≤ 0.08 (lower limit not stated) |
| Cr | 11.5 ～ 14.5 |
| Mn | ≤ 1 (lower limit not stated) |
| Ni | ≤ 0.6 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.
06Cr13Al · GB /T 4240-2019
Original-source verification is incomplete; this is not a formal standard reference
- Material category
- Stainless steel
- Subcategory
- Ferritic stainless steel
- Material form
- Reference record
- Verification status
- Reference data; original source not verified
Carbon-equivalent reference
Composition
| Element | Composition requirement |
|---|---|
| Al | 0.1 ～ 0.3 |
| C | ≤ 0.08 (lower limit not stated) |
| Cr | 11.5 ～ 14.5 |
| Mn | ≤ 1 (lower limit not stated) |
| Ni | ≤ 0.6 (lower limit not stated) |
| P | ≤ 0.04 (lower limit not stated) |
| S | ≤ 0.03 (lower limit not stated) |
| Si | ≤ 1 (lower limit not stated) |
Applicability and limitations
A match in the materials database does not establish suitability for cold heading or guarantee finished-product strength. Confirmation must consider wire condition, deformation, heat treatment and tests on actual parts.