Name: 20NiCrMo7 冷镦钢丝
Brand: 上海睿雄实业集团有限公司

原文表头对照：Heat-treatment condition at delivery＝交货热处理状态；Symbol＝符号；Wire rod＝盘条；Bar＝棒材；Wire＝钢丝。原标准表格、符号及适用条件保留如下。

Heat-treatment condition at delivery	Symbol	Products form a			Applicable requirements in cases where the steel concerned has been ordered with reference to the steel names indicated in
Heat-treatment condition at delivery	Symbol	Wire rod	Bar	Wire	T a b les B. 2,B.3,B.4 or B.5		Ta bles B. 2,B.3,B.4,B.5,B.6 or B,7			Optional
As hot-rolled or peeled	+AR or +PE	X	X	X	Chemical composition as specified in Table B.2	Mechanical properties as specified in Ta b le s B.3 ,B.4 and B.5	Chemical compositior as specified in Table B.2	Mechanical properties as specified in Tables B,3, B.4 and B.5	Values for hardenability according to Ta ble s B.6 and B.7	Supplementa- ry or special requirements as specified in Annex Eh
Cold drawn	+AR+C	-	X	X
Cold drawn + spheroidized	+AR+C+AC	-	X	X
Cold drawn + spheroidized+skin passed	+AR+C+AC +LC	-	X	X
Spheroidized or spheroidized+peeled	+AC or +AC +PE	X	X	X
Spheroidized+cold drawn	+AC+C		X	X
Treated to ferrite- pearlite structure and hardness range	+FP	-	X	-
Others	Other delivery conditions may be agreed at the time of ordering
a X=applicable,-=not applicable. b If agreed at the time of the enquiry and order.

Steel name b	% mass fraction a
Steel name b	C	Si c	Mn	P	S	Cr	Ni	Mo	B	Cu
20NiCrMo7	0,17 to 0,23	0,30	0,40 to 0,70	0,025	0,025	0,35 to 0,65	1,60 to 2,00	0,20 to 0,30		0,25
Elements not quoted in this table should not be intentionally added to the steel without the agreement of the purchaser,except those intended for finishing the heat.All reasonable precautions shall be taken in order to prevent the addition of such elements from scrap or other materials used in the production process,which can affect the hardenability, mechanical properties and applicability To improve the performance of cold heading,it is possible to add Al:0,020 %to 0,050 % a Maximum values unless otherwise indicated. b In the case of steels with hardenability requirements (see Ta bles B. 6 and B.7),minor deviations from the specified limits are permitted (with the exception of sulfur and phosphorus),provided that they do not exceed 0,01 %for carbon and the values indicated in Table 2 for the other elements. c A lower silicon content or a specific silicon range may be agreed at the time of ordering.

Steel name	Symbol	Austenitizing temperature °℃±5℃	Limits of range	Hardness HRC at a distance from quenched end of test piece(in mm)of
Steel name	Symbol	Austenitizing temperature °℃±5℃	Limits of range	1,5	3	5	7	9	11	13	15	20	25	30	35	40
20NiCrMo7	+H	900	max.	48	47	45	42	39	36	34	32	29	26	25	24	24
20NiCrMo7	+H	900	min	40	38	34	30	27	25	23	22	20		—	—	—
min.	41	40	39	36	33	30	28	26	23	21	—	—	—

20NiCrMo7 冷镦钢丝

材料技术参数